Environment-friendly polyurethane water shutoff material and preparation method thereof

A polyurethane, environment-friendly technology, applied in the field of environment-friendly polyurethane water blocking materials and its preparation, can solve problems such as poor reinforcement and complicated operation, and achieve low steam pressure, good permeability, adjustable foaming speed and curing speed Effect

Active Publication Date: 2014-04-02
SHANDONG INOV NEW MATERIALS CO LTD
View PDF4 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although water-soluble polyurethane has good anti-seepage and water-proof effect, its reinforcement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0036] Example 1

[0037] Preparation of polyurethane prepolymer: 15 kg of polyether polyol a (functionality 3, hydroxyl value 370), polyether polyol b (functionality 2, hydroxyl value 380) 5 kg, polyether polyol c (functionality 2.7, Hydroxyl value 167) 2kg, vacuum dehydration at 120°C for 2.5 hours, cooling to 45°C, adding to the synthesis reactor, nitrogen protection, adding 0.1kg of water remover ALT-201 (Anxiang Elite Chemical), while stirring Slowly add 50kg of polyphenyl polymethylene polyisocyanate PM200 (Yantai Wanhua), heat up to 80°C, react for 2.5 hours, the synthesis reaction is completed, and the NCO content in the system is no longer reduced after sampling, and the polyurethane prepolymer can be obtained. body;

[0038] Preparation of additives: add 3 kg of dibutyl phthalate, 5 kg of tributyl citrate, 3 kg of tris (1-chloro-2-propyl) phosphate, 0.3 kg of dibutyl tin dilaurate, and bismorpholino diethyl 0.5kg of base ether, 1kg of H-3625 (Zhongshan Shandong Jun Chem...

Example Embodiment

[0042] Example 2

[0043] Preparation of polyurethane prepolymer: 25kg of polyether polyol a (functionality 3, hydroxyl value 450), polyether polyol b (functionality 2, hydroxyl value 280) 10kg, polyether polyol c (functionality 2. Hydroxyl value 110) 5kg, vacuum dehydration at 110°C for 3 hours, cooling to 40°C, adding to the synthesis reactor, nitrogen protection, adding water remover ALT-201 (Anxiang Elite Chemical) 0.5kg, While stirring, slowly add 50kg of polyphenyl polymethylene polyisocyanate PM200 (Yantai Wanhua), 25kg of polyphenyl polymethylene polyisocyanate M20S (BASF), heat to 85°C, react for 2.0 hours, and the synthesis reaction is complete After the NCO content in the sampling detection system is qualified, the polyurethane prepolymer can be obtained;

[0044] Additives: add 10kg of dioctyl phthalate, 15kg of triethyl citrate, 5kg of triethyl phosphate, 1kg of bismorpholinyl diethyl ether, 1kg of stannous octoate, 3kg of H-3971 (Zhongshan Shandong Jun Chemical Indus...

Example Embodiment

[0048] Example 3

[0049] Polyurethane prepolymer is made of the following parts by weight of raw materials: 15-25 parts of polyether polyol a, 5-10 parts of polyether polyol, 2-5 parts of polyether polyol, 0.1-0.5 parts of water scavenger, isocyanate 50-75 copies;

[0050] Polyether polyol a has a functionality of 3-4 and a hydroxyl value of 300-500,

[0051] Polyether polyol b has a functionality of 2-3 and a hydroxyl value of 200-400,

[0052] Polyether polyol c has a functionality of 2-3 and a hydroxyl value of 100-200;

[0053] The additives are made of the following raw materials in parts by weight: 3-10 parts of plasticizer, 5-15 parts of diluent, 3-5 parts of flame retardant, 0.3-2 parts of catalyst and 1-3 parts of surfactant.

[0054] Preparation of polyurethane prepolymer: Polyether polyol a (functionality 4, hydroxyl value 500) 20kg, polyether polyol b (functionality 3, hydroxyl value 200) 8kg, polyether polyol c (functionality 3, Hydroxyl value 200) 4kg, vacuum dehydrated ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of high polymer materials and particularly relates to an environment-friendly polyurethane water shutoff material. The environment-friendly polyurethane water shutoff material is prepared from a polyurethane prepolymer and an additive, wherein the polyurethane prepolymer is prepared from the following raw materials: polyethylene-polypropylene glycol a (functionality: 3-4 and hydroxyl value: 300-500), polyethylene-polypropylene glycol b (functionality: 2-3 and hydroxyl value: 200-400), polyethylene-polypropylene glycol c (functionality: 2-3 and hydroxyl value: 100-200), a water remover and isocyanate; the additive is prepared from the following raw materials: a plasticizing agent, a diluent, a flame retardant, a catalyst and a surfactant. When being injected to a hole or crack, the polyurethane water shutoff material is diffused and solidified in the crack to generate foam with certain strength; molecules of a gel contain a great number of polar groups, so that the environment-friendly polyurethane water shutoff material is high in bonding strength and capable of shutting off the crack, thus playing the water shutoff and consolidation effects. The invention also provides a preparation method of the environment-friendly polyurethane water shutoff material. The preparation method is reasonable in process and easy for industrial production.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to an environment-friendly polyurethane water blocking material and a preparation method thereof. Background technique [0002] Various waterproof concretes have been widely used in underground engineering, but they are prone to leakage after long-term use. In newly excavated underground projects, sometimes a large amount of groundwater gushes out, especially in underground projects constructed in rocks. Groundwater can cause serious damage to underground projects through rock cracks. If the water is not stopped first at this time, Work will not be carried out. [0003] The chemical grouting plugging technology is to pump the slurry made of chemicals into the concrete structure joints, and play the role of water plugging after condensation and hardening. The grouting water blocking method has its important significance in underground engineering, and has become an indi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L75/08C08G18/76C08G18/48C08G18/12C08K5/11C08K5/101C08K5/521C08G101/00
Inventor 王艳艳唐国涛张丽郝德开宫健
Owner SHANDONG INOV NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap