Environmental-friendly glass fiber reinforced plastic coating material and preparation method thereof

A coating material, fiberglass technology, applied in epoxy resin coatings, coatings, polyester coatings, etc., can solve the problem of weakening the physical properties of fibers, and achieve good physical properties, good mechanical properties, and excellent insulation.

Inactive Publication Date: 2014-05-07
WUHU BAOYI AMUSEMENT EQUIP
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the FRP material provided by this method overcomes the defects caused by the glass cloth itself, the unique physical properties of the fiber itself are greatly weakened because the glass fiber is cut into powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The present invention will be described in detail below through specific examples.

[0013] An environmentally friendly FRP coating material, made of the following raw materials in parts by weight (kg): nano-mullite 2, E-12 epoxy resin 28, amino resin 10, 3-pyrroline 2, hexafluoroacetylacetone 2, n-Propyl Methacrylate 5, Zinc Naphthenate 6, Chopped Glass Fiber 26, T31 Epoxy Resin Curing Agent 2, Dioxypropylene Ethyl Ether 4, Nano-Silicon Dioxide 2, Bauxite 1, Auxiliary 1;

[0014] The additive is made of the following raw materials in parts by weight (kg): iron powder 10, zinc acetate 5, light-burned magnesium oxide 4, medical stone 3, talc powder 3, peat 2, tripropylene glycol diacrylate 2 , morpholine 1, ascorbic acid 2, silicon carbide 3, chitosan 1, methyl acrylate 3; the preparation method is to put iron powder, peat, medical stone, light-burned magnesia Calcined at low temperature for 4-5 hours, take it out, mix with talcum powder, ascorbic acid, silicon carbide...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environmental-friendly glass fiber reinforced plastic coating material. The environmental-friendly glass fiber reinforced plastic coating material is characterized by being prepared from the following raw materials in parts by weight: 2-3 parts of nano mullite, 28-32 parts of E-12 epoxy resin, 10-12 parts of amino resin, 2-4 parts of 3-pyrroline, 2-3 parts of hexafluoro acetylacetone, 5-8 parts of n-propyl methacrylate, 6-9 parts of zinc naphthenate, 26-29 parts of chopped glass fibers, 2-3 parts of T31 epoxy resin curing agent, 4-6 parts of diepoxy propane ethyl ether, 2-3 parts of nano silica, 1-2 parts of bauxite and 1-2 parts of auxiliaries. According to the coating material, through adding the auxiliaries, the material has good physical properties and mechanical properties, and a reinforcing effect is exerted; the production process of the coating material is simple and reasonable; a formed product has superior corrosion resistance and relatively strong strength property, is lightweight, ageing-resistant, high-temperature resistant, fireproof, flame-retardant, energy-saving and environmental-friendly, and is excellent in insulating performance.

Description

technical field [0001] The invention relates to a composite material and a preparation method thereof, in particular to an environment-friendly FRP coating material and a preparation method thereof. Background technique [0002] FRP material is a material in which glass fiber reinforced materials are embedded in cured thermosetting resin or wrapped by it to form a composite structure. At present, most of the FRP materials used in the market are formed by resin-impregnated glass cloth materials. The method has a good wetting effect and the prepared glass fiber has a high content. However, due to the limitation of the volume and shape of the glass cloth, it is especially not suitable for products such as pipe joints, tee fittings, and elbow fittings, which are not easy to be uniformly compressed. In addition, the impact resistance of the FRP material prepared by this method is poor, and the laminated surface is prone to delamination. In order to solve the above problems, so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/02C09D4/06C09D7/12C09D163/00C09D167/06
CPCY02P20/10
Inventor 张庆
Owner WUHU BAOYI AMUSEMENT EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com