Environment-friendly high-phosphorus chemical nickel plating solution for airtight glass-sealed binding terminal, and applications thereof

A technology of electroless nickel plating solution and terminal, applied in the field of electroless plating, can solve the problems of poor bonding force of steel needle plating, difficult welding and plating of steel needle plating, etc., and achieves excellent welding, good stability of plating solution and prolonged The effect of service life

Inactive Publication Date: 2014-07-23
深圳市迪凯鑫科技有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of electronic technology, metal glass packaging technology has been more and more widely used and put forward higher and higher requirements for quality. In addition to the requirements of high airtightness, high insulation, high Friction, easy welding and other properties also put forward higher requirements. In order to meet the above requirements, in addition to the excellent sintering technology of metallic glass, more and more stringent requirements are put forward for the surface treatment technology of sintered products. Among them, high phosphating nickel plating It is the most widely used; however, there are many deficiencies in the application of high-phosphorus electroless nickel plating in the market, such as the difficulty of plating on stainless steel needles (hereinafter referred to as steel needles) or the serious lag behind the plating of steel needles compared with iron covers, or nickel on glass, Or the bonding strength of the steel needle coating is poor, or the steel needle coating is difficult to weld, or it is not environmentally friendly, etc., it is difficult to have a product that meets the above requirements at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly high-phosphorus chemical nickel plating solution for airtight glass-sealed binding terminal, and applications thereof
  • Environment-friendly high-phosphorus chemical nickel plating solution for airtight glass-sealed binding terminal, and applications thereof
  • Environment-friendly high-phosphorus chemical nickel plating solution for airtight glass-sealed binding terminal, and applications thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The implementation process of the present invention is strictly controlled according to the terminal electroless plating process, including the processes of alkaline oxidation, acid etching, activation, neutralization, electroless nickel plating and air-drying of the sintered airtight glass-sealed terminal, wherein,

[0032] The process conditions of the alkaline oxidation treatment step: KMnO4: 70-80g / L, NaOH: 100-120g / L, the temperature is 88-95°C, and the time is 60-90min.

[0033] Process conditions for acid etching: hydrochloric acid with a concentration of 35-45%, rhodin which accounts for 3% of the mass of hydrochloric acid, the control temperature is 45-55°C, and the time is 7-9min.

[0034] Activation process conditions: concentration of 25-35% hydrochloric acid, control temperature of 45-55°C, time of 1.5-2min.

[0035] Neutralization process conditions: adjust the pH to 12-13 with ammonia water, and control the temperature at 60-80°C.

[0036] Water washing ...

Embodiment 2-3

[0049]Compared with Example 1, the difference is that the main and auxiliary complexing agent and the composite stabilizing brightener are adjusted, and the others remain unchanged. As in Table 3:

[0050] table 3

[0051] Material name

Example 2

Example 3

Lactic acid (g / L)

41.2

43.8

Trisodium citrate (g / L)

1.5

2.63

Malic acid(g / L)

13.2

15

Glycine (g / L)

8.3

11.2

[0052] Stannous chloride (g / L)

0.27

0.3

Maleic anhydride (g / L)

0.26

0.33

DEP (mg / L)

3

5

OP-10(ml / L)

0.23

0.36

[0053] After testing (5L beakers simulated trial production of 30 samples and 5 samples each) and tests, the results are shown in Table 4:

[0054] Table 4

[0055]

[0056] With reference to Table 4, from the test situation, when using the configuration parameters to go offline, the strong activity of the plating solution is conducive to improving t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly high-phosphorus chemical nickel plating solution for an airtight glass-sealed binding terminal. The environment-friendly high-phosphorus chemical nickel plating solution comprises the following active ingredients according to concentration: 25-27g / L nickel sulfate, 19-22g / L sodium hypophosphite, 20-23g / L sodium hydroxide, 41-44g / L lactic acid, 1.5-2.3g / L trisodium citrate, 13-15g / L malic acid, 8-12g / L glycine, 0.2-0.4ml / L OP-10, 0.26-0.3g / L stannous chloride, 0.26-0.34g / L maleic anhydride and 3-5mg / L N,N-diethylaminopropyne. The invention discloses a method for performing chemical plating by adopting the chemical nickel plating solution. A stainless steel needle and an iron cover can be simultaneously subjected to chemical nickel plating and be evenly plated, no nickel nuclear generated on sintered glass can be guaranteed, and the difficulty in keeping the smoothness and cleanness of the surface of glass can be solved.

Description

technical field [0001] The invention relates to an environment-friendly high-phosphorus electroless nickel plating solution for airtight glass-sealed terminals and its application, mainly used in electric connectors (airtight glass-sealed) made of stainless steel (needle) and iron cover through glass powder terminal) and belongs to the technical field of electroless plating. Background technique [0002] With the development of electronic technology, metal glass packaging technology has been more and more widely used and put forward higher and higher requirements for quality. In addition to the requirements of high airtightness, high insulation, high Friction, easy welding and other properties also put forward higher requirements. In order to meet the above requirements, in addition to the excellent sintering technology of metallic glass, more and more stringent requirements are put forward for the surface treatment technology of sintered products. Among them, high phosphati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C18/36C23C18/18
Inventor 黄胜平
Owner 深圳市迪凯鑫科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com