A kind of manufacturing process of lithium-sulfur battery

A lithium-sulfur battery and manufacturing process technology, applied in electrode manufacturing, sustainable manufacturing/processing, secondary batteries, etc., can solve problems such as poor electrical conductivity and limited ability to adsorb active material sulfur

Active Publication Date: 2016-08-31
山东卓海能源科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0018] The purpose of the present invention is to provide an all-solid-state electrolyte obtained by compounding porous carbon and sulfur in the prior art because of its limited ability to adsorb active substance sulfur and poor conductivity, which limits its application in batteries. All-solid-state electrolyte for lithium-sulfur batteries with high rate performance and high cycle performance of sulfur batteries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of manufacturing process of lithium-sulfur battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] In a 1L 316L stainless steel reaction kettle, under the protection of continuously feeding 160ml / min nitrogen, add 5.6mol industrial superior grade NMP, 1.0mol industrial superior grade sodium sulfide and 0.001mol industrial superior grade sodium hydroxide, and stir at 690rpm Slowly raise the temperature of the reaction system to 138°C, then add 1.003mol of industrial grade lithium chloride, continue to raise the temperature of the reaction system to 160°C, and keep the reaction system at this temperature for 9 minutes, When fine white crystals are precipitated in the reaction system, evaporate and remove the water in the reaction system at the same time, and stop heating; filter while hot, filter out the white crystals in the reaction system, add the filtrate to the reaction system again, Stirring intensity is 160rpm, add sublimated sulfur of 4mol / mol lithium sulfide and deionized oxygen-free water, wait until the temperature rises to 138°C, and keep it under reflux for...

Embodiment 2

[0058] In a 1L 316L stainless steel reaction kettle, under the protection of continuously feeding 690ml / min nitrogen, add 6.6mol industrial superior grade NMP, 1.0mol industrial superior grade sodium sulfide and 0.001mol industrial superior grade sodium hydroxide, and stir at 690rpm Slowly raise the temperature of the reaction system to 148°C, then add 1.003mol of industrial grade lithium chloride, continue to raise the temperature of the reaction system to 190°C, and keep the reaction system warm for 6min under this temperature condition, When fine white crystals are precipitated in the reaction system, evaporate and remove the water in the reaction system at the same time, and stop heating; filter while hot, filter out the white crystals in the reaction system, add the filtrate to the reaction system again, The stirring intensity is 690rpm, add 8mol / mol lithium sulfide sublimated sulfur and deionized anaerobic water, wait for the temperature to rise to 148°C, and keep it unde...

Embodiment 3

[0063] In a 1L 316L stainless steel reaction kettle, under the protection of continuously feeding 261ml / min nitrogen, add 5.8mol industrial superior grade NMP, 1.0mol industrial superior grade sodium sulfide and 0.001mol industrial superior grade sodium hydroxide, and stir at 234rpm Slowly raise the temperature of the reaction system to 139°C, then add 1.003mol of industrial superior lithium chloride, continue to raise the temperature of the reaction system to 163°C, and keep the reaction system warm for 7min under this temperature condition, When fine white crystals are precipitated in the reaction system, evaporate and remove the water in the reaction system at the same time, and stop heating; filter while hot, filter out the white crystals in the reaction system, add the filtrate to the reaction system again, The stirring intensity is 234rpm, add 5mol / mol lithium sulfide sublimated sulfur and deionized anaerobic water, wait until the temperature rises to 139°C, and keep it u...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
ionic conductivityaaaaaaaaaa
porosityaaaaaaaaaa
porosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing process of a lithium-sulfur battery. Polyacrylonitrile resin micropowder and diatomite are added into a high-speed mixing agitator at a mass ratio of 36-39:64-61, and then 6-24% wt / silicon The NMP solvent of algae earth is the raw material after pre-treatment in the NMP solution of lithium salt (containing lithium polysulfide, lithium methylaminobutyrate, lithium perchlorate, lithium phosphate 6 ~ 9%wt NMP solution) repeated immersion and The positive electrode material is prepared after high-temperature evaporation; the lithium-sulfur battery all-solid-state electrolyte is prepared from lithium methylaminobutyrate, lithium perchlorate, and lithium phosphate; Under the condition of 660°C, the negative electrode material is prepared by absorbing molten metal lithium through the capillary pores of carbon-containing diatomaceous earth. The all-solid-state electrolyte for lithium-sulfur batteries prepared by the process of the present invention has high sulfur-accommodating capacity, high ion transmission capacity and electrical conductivity. Performance, can improve the high rate performance and high cycle performance of lithium-sulfur batteries.

Description

[0001] Field [0002] The invention relates to a lithium-sulfur battery all-solid electrolyte and a preparation method thereof, belonging to the field of new energy. Background technique [0003] With the development of human society, problems such as energy shortage and environmental pollution have become increasingly prominent, and people's understanding and requirements for chemical power sources have become higher and higher, prompting people to continuously explore new energy storage systems based on chemical power sources. Lithium metal-based batteries have led the development of high-performance chemical power sources in recent decades. With the successful commercialization of lithium-ion batteries, countries around the world are stepping up research on lithium-ion power batteries for vehicles. However, due to factors such as energy density, safety, and price, conventional lithium-ion batteries such as lithium cobalt oxide, lithium manganese oxide, and lithium iron pho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/38H01M4/04
CPCH01M4/0471H01M10/38Y02E60/10Y02P70/50
Inventor 宋大余李波徐晨
Owner 山东卓海能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap