Vapor phase antirust blown polyethylene film and making method thereof

A technology of gas phase rust prevention and film blowing, applied in the field of gas phase rust prevention, can solve the problems of low cost, short effective time and high cost of desiccant rust prevention, achieve environmental protection and human health, improve the rust prevention effect, and prolong the antirust effect. The effect of rust time

Inactive Publication Date: 2014-08-20
YANTAI HENGDIKE ENERGY TECH
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The most commonly used anti-corrosion method is to coat the metal surface with anti-rust oil, but this method will lose efficacy due to oxidation of the anti-rust oil itself, and it is time-consuming and labor-intensive to remove the protective layer, which is neither hygienic nor safe
The use of desiccant to prevent rust is low in cost, simple in operation, safe and environmentally friendly, easy to remove protective packaging, but the effective time is short, and it is greatly affected by the ambient temperature
As for the packaging and processing of metal materials with special dehumidification equipment, although the anti-rust effect is good, the cost is high, time-consuming and labor-intensive, and the operation is complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vapor phase antirust blown polyethylene film and making method thereof
  • Vapor phase antirust blown polyethylene film and making method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A polyethylene gas-phase antirust blown film comprises low-density polyethylene resin, diisooctyl phthalate, dibutyl phthalate, light calcium carbonate, sodium benzoate, cyclohexylamine phosphite, Azelaic acid dicyclohexylamine, antioxidant, each component and parts by weight thereof are:

[0015]

[0016] Wherein, the antioxidant is β-(3,5-di-tert-butyl-4-hydroxyphenyl) octadecyl propionate.

[0017] Its preparation method is: after each component is measured in parts by mass, it is divided into materials containing and not containing gas phase antirust agent, stirred in a high-speed mixer for 10-15 minutes, and the stirring temperature is 30-50°C, and then enters the manufacturing process. Granulator, the granulation temperature is 140-152°C, the melt temperature is 147°C, the melt of the mixed material containing the vapor phase rust inhibitor is fed into the inner layer of the die head of the co-extrusion blow molding unit, and the outer layer is made of benzene-...

Embodiment 2

[0021] A polyethylene gas-phase antirust blown film comprises low-density polyethylene resin, dibutyl phthalate, talcum powder, sodium benzoate, cyclohexylamine phosphite, dicyclohexylamine sebacate, antioxidant , each component and its mass parts are:

[0022]

[0023] Wherein, the antioxidant preferably uses 1,1,3-tris(2-methyl-4-hydroxyl-5-tert-butylphenyl)butane.

[0024] The preparation method of the polyethylene gas-phase antirust blown film is the same as that of Example 1.

Embodiment 3

[0026] A polyethylene gas-phase antirust blown film comprises low-density polyethylene resin, didecyl phthalate, white carbon black, sodium benzoate, cyclohexylamine phosphite, dicyclohexylamine dodecanedioic acid, Dicyclohexylamine suberate and tris(2,4-di-tert-butyl)phenyl phosphite, each component and parts by weight thereof are:

[0027]

[0028] The preparation method of the polyethylene gas-phase antirust blown film is the same as that of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a vapor phase antirust blown polyethylene film and a making method thereof. The vapor phase antirust blown polyethylene film comprises low density polyethylene resin, a plasticizer, an auxiliary filler, sodium benzoate, cyclohexylamine phosphate, amine salt of aliphatic dibasic acid, and an antioxidant. Polyethylene materials comprising vapor phase antirust agents are utilized to make the vapor phase antirust blown polyethylene film through a blowing production process in order to realize convenient production and vapor phase antirust effects. The vapor phase antirust agents adopted in the invention are different from traditional nitrite vapor phase antirust agents, are in favor of realizing environmental protection and benefiting the health of human bodies. The film made in the invention has the advantages of composite structure, obstruction of the outward penetration of the vapor phase antirust agents, antirust effect increase and antirust time prolongation.

Description

technical field [0001] The invention relates to the field of gas-phase anti-rust, in particular to a polyethylene gas-phase anti-rust blown film and a preparation method thereof. Background technique [0002] Corrosion is a phenomenon in which metal materials and the surrounding environment are destroyed by chemical or electrochemical reactions. It is a reverse process of smelting. Natural environments and industrial media can cause corrosion of metal materials. In the process of transportation and storage of metals and their products, especially sea transportation and high-heat and humid land transportation, it is inevitable to involve rust prevention issues. The most commonly used anti-corrosion method is to coat the metal surface with anti-rust oil, but this method will lose efficacy due to oxidation of the anti-rust oil itself, and it is time-consuming and labor-intensive to remove the protective layer, which is neither hygienic nor safe. The use of desiccant for anti-r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08K13/02C08K5/12C08K3/26C08K3/34C08K3/36C08K5/098C08K5/5399C08K5/17B29C55/28
CPCC08K13/02B29C55/28C08J5/18C08J2323/06C08K3/26C08K3/34C08K3/36C08K5/098C08K5/12C08K5/13C08K5/1345C08K5/17C08K5/526C08K2003/265C08K2201/014C08L2203/16C08L2207/066
Inventor 修建东刘方旭
Owner YANTAI HENGDIKE ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap