Modified calcium carbonate with wide applicable strength and preparation method thereof

A calcium carbonate and modification technology, applied in chemical instruments and methods, inorganic pigment treatment, dyeing low molecular organic compound treatment, etc., can solve the problems of different interface properties, material mechanical properties decline, poor compatibility, etc., and achieve reasonable formula , Increase dispersion and save raw materials

Inactive Publication Date: 2014-09-10
GUANGDONG YUFENG POWDER MATERIAL
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because its surface is hydrophilic, oleophobic and easy to agglomerate, its interface properties are different from those of organi...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified calcium carbonate with wide applicable strength and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] specific implementation plan

[0013] The present invention will be described in detail below through specific examples.

[0014] A modified calcium carbonate suitable for wide strength is prepared from the following raw materials in parts by weight (kg): calcium carbonate 85, zinc hydroxide 3, styrene-butadiene rubber 5, carbon black 2, montmorillonite powder 2, kaolin 2, silicon Magnesium acid 2, anti-aging agent RD1, glycerol triglyceride 4, polyvinyl acetate 4, redispersible rubber powder 2, modified titanium dioxide 3;

[0015] The modified titanium dioxide is made of the following raw materials in parts by weight (kg): aluminum hydroxide 2, nano titanium dioxide 50, silicon carbide 4, methyl methacrylate 5, antimony trioxide 3, terephthalic acid 3, horse Dioctyl maleate 3, ethylene glycol 5, water 50; the preparation method is to first add methyl methacrylate, nano-titanium dioxide, aluminum hydroxide, ethylene glycol, and water and stir evenly to form a suspensi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses modified calcium carbonate with wide applicable strength. The applicable modified calcium carbonate is characterized by being prepared from the following raw materials in parts by weight: 85-90 parts of calcium carbonate, 3-4 parts of zinc hydroxide, 5-7 parts of butadiene styrene rubber, 2-3 parts of carbon black, 2-4 parts of smectite flour, 2-3 parts of kaolin, 2-4 parts of magnesium silicate, 1-2 parts of antiager RD, 4-6 parts of glycerol triglycerin acid ester, 4-6 parts of polyvinyl acetate, 2-3 parts of dispersible rubber powder and 3-4 parts of modified titanium dioxide. The modified calcium carbonate is reasonable in formula, and simple in production technology, the toughness of a cellulosic fiber is enhanced by reinforcing action on the carbon black, and the modified titanium dioxide is added to coat after the grinding process, so that not only is the dispersibility increased, but also raw materials are saved, and the cost is reduced. The packing disclosed by the invention can be conveniently applied to plastic, rubber, coatings and the like.

Description

technical field [0001] The invention relates to the field of industrial fillers, in particular to a wide-strength modified calcium carbonate and a preparation method thereof. Background technique [0002] Due to its good stability, pure color, low wear, easy processing, non-toxicity, wide range of sources, low price and many other advantages, calcium carbonate is often used to fill plastics, rubber and other materials to increase capacity, increase and reduce production costs. However, because its surface is hydrophilic and oleophobic and is easy to agglomerate, it has different interfacial properties with organic polymers and poor compatibility. Direct or excessive filling will easily lead to a decrease in the mechanical properties of the material. Through modification, its surface properties can be improved, and the comprehensive properties such as dispersibility, compatibility with the polymer interface and mechanical strength of the material can be improved. Contents o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09C1/02C09C3/06C09C3/10C09C3/08C09C1/36
Inventor 王俊华朱传路
Owner GUANGDONG YUFENG POWDER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap