A wear-resistant ball and high-hardness technology, which is applied in the field of wear-resistant materials, can solve the problems of wear-resistant ball hardness, impact resistance, heat resistance, wear resistance, and poor toughness.

Active Publication Date: 2016-08-24
宁国市宁武新材料科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing wear-resistant balls have poor performance in terms of hardness, impact resistance, heat resistance, wear resistance, and toughness, and cannot meet the requirements of modern society.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The composition of the high-hardness wear-resistant ball of the present invention includes by mass fraction: C: 0.02%, Mn: 0.44%, W: 0.03%, Si: 0.64%, Ni: 0.45%, Cr: 8.3%, Mo: 0.11 %, V: 0.9%, Nb: 0.2%, Ca: 0.018%, Zr: 0.015%, Cu: 0.01%, Zn: 0.035%, S: 0.028%, P: 0.033%, the balance is Fe and unavoidable Impurities.

[0024] The preparation method of the high hardness wear-resistant ball of the present invention comprises the following steps:

[0025] S1. Smelting: Add steel scrap to an intermediate frequency induction melting furnace and heat to 1502°C. After holding for 40 minutes, add ferrochrome, ferromolybdenum, ferrovanadium, ferroniobium, and ferrotungsten. After complete melting, add ferrosilicon and ferromanganese. Raise the temperature to 1570°C and heat until it is completely melted, then add nickel alloy, silicon-calcium alloy, iron-zirconium, and metal zinc. After the raw materials are completely melted and slag removed, molten steel is obtained. After pou...

Embodiment 2

[0030]The high hardness wear-resistant ball of the present invention, its composition includes by mass fraction: C: 0.06%, Mn: 0.38%, W: 0.022%, Si: 0.81%, Ni: 0.38%, Cr: 5%, Mo: 0.13 %, V: 1.0%, Nb: 0.45%, Ca: 0.01%, Zr: 0.014%, Cu: 0.03%, Zn: 0.01%, S: 0.02%, P: 0.03%, the balance is Fe and unavoidable Impurities.

[0031] The preparation method of the high hardness wear-resistant ball of the present invention comprises the following steps:

[0032] S1. Melting: Add steel scrap to an intermediate frequency induction melting furnace and heat it to 1520°C. After holding for 20 minutes, add ferrochrome, ferromolybdenum, ferrovanadium, ferroniobium, and ferrotungsten. After complete melting, add ferrosilicon and ferromanganese. Raise the temperature to 1540°C and heat until it is completely melted, then add nickel alloy, silicon-calcium alloy, iron-zirconium, and metal zinc. After the raw materials are completely melted and slag removed, molten steel is obtained. After pouring,...

Embodiment 3

[0037] The high-hardness wear-resistant ball of the present invention, its composition includes by mass fraction: C: 0.05%, Mn: 0.86%, W: 0.01%, Si: 0.53%, Ni: 0.21%, Cr: 9.8%, Mo: 0.15 %, V: 0.7%, Nb: 0.5%, Ca: 0.038%, Zr: 0.015%, Cu: 0.018%, Zn: 0.019%, S: 0.021%, P: 0.029%, the balance is Fe and unavoidable Impurities.

[0038] The preparation method of the high hardness wear-resistant ball of the present invention comprises the following steps:

[0039] S1. Smelting: Add steel scrap to an intermediate frequency induction melting furnace and heat it to 1500°C. After holding for 45 minutes, add ferrochrome, ferromolybdenum, ferrovanadium, ferroniobium, and ferrotungsten. After complete melting, add ferrosilicon and ferromanganese. Raise the temperature to 1530°C and heat until it is completely melted, then add nickel alloy, silicon-calcium alloy, iron-zirconium, and metal zinc. After the raw materials are completely melted and slag removed, molten steel is obtained. After p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-hardness wear-resistant ball, which comprises C, Mn, W, Si, Ni, Cr, Mo, V, Nb, Ca, Zr, Cu, Zn, S and P. The invention also discloses a preparation method of a high-hardness wear-resistant ball. The heat treatment process is as follows: heating up to 980-1030°C, keeping warm for 50-80min and water-cooling to room temperature; heating up to 800-820°C, keeping warm for 30-75min and water-cooling to room temperature ; Heating up to 500-530°C, keeping warm for 130-150min and water-cooling to room temperature; the surface of the wear-resistant ball is modified by reactive nitrogen arc cladding, and the cladding powder is a combination of titanium powder and graphite powder; the composition of titanium powder includes: C, Mo, Si, Fe, Cl, N, O, H, the balance is Ti; cladding current 150‑180A, nitrogen flow rate 12‑18L / min. The high-hardness wear-resistant ball of the present invention has high hardness and excellent impact strength, heat resistance, wear resistance and corrosion resistance.

Description

technical field [0001] The invention relates to the technical field of wear-resistant materials, in particular to a high-hardness wear-resistant ball and a preparation method thereof. Background technique [0002] Frictional behavior is ubiquitous, causing huge national economic losses. The survey found that abrasive wear alone causes industrial countries to lose 1%-4% of their gross national product every year. With the rapid economic development and social progress, the social loss caused by wear will be even greater. [0003] Abrasive materials are generally used under corresponding working conditions, and their performance requirements are also different due to different use environments. Under dry grinding conditions, the failure modes of wear-resistant materials are mainly material wear, macroscopic fracture and wear surface deformation caused by abrasive wear. Therefore, the basic performance requirements for wear-resistant materials are proposed: (1) High hardness, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More