Nano particles modified by alendronic acid functionalized polyethylene glycol and preparation method of nano particles

A technology of alendronic acid and polyethylene glycol, applied in the field of polyethylene glycol-modified nanoparticles and its preparation, can solve the problems of expensive phospholipid materials, unfavorable clinical application, and many operation steps

Active Publication Date: 2014-11-19
SHENZHEN INST OF ADVANCED TECH
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the preparation method of the LCPII system, there are many operating steps, and there are many factors affecting the transfection efficiency. The cati

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano particles modified by alendronic acid functionalized polyethylene glycol and preparation method of nano particles
  • Nano particles modified by alendronic acid functionalized polyethylene glycol and preparation method of nano particles
  • Nano particles modified by alendronic acid functionalized polyethylene glycol and preparation method of nano particles

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0069] The chemical reaction equation of the preparation process of compound D1 of the present invention is exemplified as follows:

[0070]

[0071] The chemical reaction equation of the preparation process of compound D2 of the present invention is exemplified as follows:

[0072]

[0073]

[0074] The chemical reaction equation of the preparation process of compound D3 of the present invention is exemplified as follows:

[0075]

[0076]

[0077] Preferably, the soluble calcium salt solution is selected from one or more of calcium chloride solution, calcium nitrate solution and calcium bromide solution.

[0078] Preferably, the phosphate solution is selected from one or more of disodium hydrogen phosphate, sodium dihydrogen phosphate, sodium phosphate, potassium dihydrogen phosphate and diammonium hydrogen phosphate, and the carbonate solution is selected from potassium carbonate One or more of sodium carbonate and sodium bicarbonate.

[0079] Preferably, the...

Embodiment 1

[0082] A preparation method of alendronic acid functionalized polyethylene glycol modified nanoparticles, comprising the following steps:

[0083] (1) Preparation of alendronic acid functionalized polyethylene glycol

[0084] Take compound A with a polyethylene glycol molecular weight of 2000 Daltons, and dissolve it in an organic solvent tetrahydrofuran (THF) to prepare a solution containing compound A;

[0085] Compound A:

[0086] Take a glutamic acid solution with a pH value of 7.5, add the glutamic acid to the compound A in a ratio of 1.5:1 to the solution containing compound A, react at room temperature for 10 h, and then use 0.2N hydrochloric acid Adjust the pH value of the mixed solution to 4.5, extract 6 times with chloroform, take the organic phase, dry it with anhydrous sodium sulfate, concentrate under reduced pressure, and then add it dropwise to cold diethyl ether under stirring, let stand, collect the precipitate, and dry to obtain compound B1;

[0087] Comp...

Embodiment 2

[0099] (1) Preparation of four monomethyl ether polyethylene glycols functionalized with alendronic acid

[0100] Compounds B1 and C1 were prepared according to the method in Example 1.

[0101] Take a glutamic acid solution with a pH value of 7.5, add it to the solution containing compound C1 according to the molar ratio of the glutamic acid and the carboxyl group of the compound B1 at a ratio of 3:1, react at room temperature for 8 hours, and then adjust the mixing The pH value of the solution was 2.5, and then extracted 6 times with chloroform, and the organic phase was dried with anhydrous sodium sulfate, concentrated under reduced pressure, added dropwise into cold diethyl ether under stirring, left to stand, the precipitate was collected, and dried to obtain compound B2;

[0102] Compound B2:

[0103] Dissolve the compound B2 in the organic solvent tetrahydrofuran, N,N-dimethylformamide, dioxane, chloroform or dichloromethane, add N-hydroxysuccinimide and 1-ethyl-(3 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides nano-particles modified by alendronic acid functionalized polyethylene glycol. The nano particles are calcium phosphate particles or calcium carbonate particles wrapped with target delivery matters; the target delivery matters are selected from DNA, siRNA and protein acromolecular drugs or micro-molecular chemical drugs; alendronic acid functionalized polyethylene glycol covers the surfaces of the nano particles; and the particle size of the nano particles modified by alendronic acid functionalized polyethylene glycol is 20-50 nm. The nano particles modified by alendronic acid functionalized polyethylene glycol are small in particle size; polyalendronic acid-polyethylene glycol can stably cover the surfaces of phosphate-genetic particles, and therefore, the nano particles can be effectively stabilized for a long time; the body circulation time is prolonged; the nano particles disclosed by the invention are low in cost and toxicity, safe and effective. The invention further provides a preparation method of the nano particles modified by the alendronic acid functionalized polyethylene glycol.

Description

technical field [0001] The invention relates to the field of non-viral gene delivery systems, in particular to an alendronic acid-functionalized polyethylene glycol-modified nanoparticle and a preparation method thereof. Background technique [0002] Gene therapy offers a promising treatment for some major diseases. Since the gene therapy clinical trials began in 1990, only one or two gene therapy drugs have been approved for marketing. The main reason is the lack of stable gene expression and safe and efficient gene delivery vectors. [0003] Calcium phosphate is an excellent non-viral gene carrier with good tissue compatibility and absorption. The particle size obtained by the common calcium phosphate-gene co-precipitation method is larger than 100nm, which is difficult to control, has poor stability, and is difficult to be used for in vivo transfection. [0004] The Chinese patent application with publication number 101829330A discloses a calcium phosphate composite nan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K48/00A61K9/16A61K47/34
Inventor 陈钏王志勇唐征乐何成宜陈志英
Owner SHENZHEN INST OF ADVANCED TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap