Activated carbon diatomite particles capable of rapid purification of flue gas and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of diatomite particles and activated carbon, applied in chemical instruments and methods, separation methods, other chemical processes, etc., can solve the problems of high operation and maintenance costs, slow reaction speed, low desulfurization efficiency, etc., and achieves high porosity and surface area. The effect of many holes and high desulfurization accuracy
Inactive Publication Date: 2015-04-01
ANHUI PHOENIX INT CO LTD
View PDF5 Cites 11 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] Wet FGD technology uses a solution or slurry containing absorbent to desulfurize and treat desulfurized products in a wet state. This method has the advantages of fast desulfurization reaction speed, simple equipment, and high desulfurization efficiency. However, severe corrosion, high operation and maintenance costs and Easy to cause secondary pollution and other problems
The desulfurization absorption and product treatment of the dry FGD technology are carried out in a dry state. This method has the advantages of no sewage waste acid discharge, less corrosion of equipment, no obvious cooling of the flue gas during the purification process, and high flue temperature after purification, which is beneficial to the chimney. Exhaust diffusion, less secondary pollution, etc., but there are problems such as low desulfurization efficiency, slow reaction speed, and large equipment
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0012] specific implementation plan
[0013] The present invention will be described in detail below through specific examples.
[0014] An activated carbon diatomite particle capable of rapidly purifying flue gas, prepared from the following raw materials in parts by weight (kg): woody activated carbon 105, diatomite 35, tripotassium citrate 1, expanded perlite 4, ammonium chloride 3. Zirconium silicate 2, nano-kaolin 6, nano-silicon dioxide 4, copper sulfate 3, polyoxyethylene rosin acid ester 1, methyldiethanolamine 3, adsorption aid 4, appropriate amount of water;
[0015] The adsorption aid is made of the following raw materials in parts by weight (kg): zircon powder 8, deer marsh soil 2, magnesium chloride 2, sodium bicarbonate 1.5, natural coke powder 2, polyacrylamide 2, cerium dioxide 2, cork 12. Bamboo fiber 10; the preparation method is to dry cork and bamboo fiber at 100°C-120°C for 1-1.5 hours, crush them into 40-60 mesh powder, and then add appropriate amount of...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses activated carbon diatomite particles capable of rapid purification of flue gas, and is characterized in that the activated carbon diatomite particles are prepared from the following raw materials in parts by weight: 105-110 parts of wooden activated carbon, 35-40 parts of diatomite, 1-2 parts of tripotassium citrate, 4-6 parts of expanded perlite, 3-5 parts of ammonium chloride, 2-3 parts of zirconium silicate, 6-9 parts of nano kaolin, 4-6 parts of nano silica, 3-5 parts of copper sulfate, 1-2 parts of rosin-polythylene oxide ester, 3-5 parts of methyldiethanolamine, 4-6 parts of an adsorption auxiliary agent, and a proper amount of water. The formula is reasonable; with addition of nano kaolin and expanded perlite, much surface pores exist, and the porosity is high; with addition of methyldiethanolamine, the activated carbon diatomite particles have a flue gas rapid purifying effect; with addition of the adsorption auxiliary agent, the activated carbon diatomite particles have special porousness, and prolong the contact time with gas; and activated carbon can quickly adsorb various solutes and free gases, and is high in activity, high in desulfurization precision, and suitable for industrial dry desulfurization, automobile tail gas desulfurization, daily air purification and the like.
Description
technical field [0001] The invention relates to a desulfurization activated carbon and a preparation method thereof, in particular to an activated carbon diatomite particle capable of rapidly purifying flue gas and a preparation method thereof. Background technique [0002] Wet FGD technology uses a solution or slurry containing absorbent to desulfurize and treat desulfurized products in a wet state. This method has the advantages of fast desulfurization reaction speed, simple equipment, and high desulfurization efficiency. However, severe corrosion, high operation and maintenance costs and It is easy to cause secondary pollution and other problems. The desulfurization absorption and product treatment of the dry FGD technology are carried out in a dry state. This method has the advantages of no sewage waste acid discharge, less corrosion of equipment, no obvious cooling of the flue gas during the purification process, and high flue temperature after purification, which is be...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.