High-strength waterproof concrete and preparation method thereof

A water-resistant and concrete technology, applied in the field of concrete, can solve the problems of poor durability, unsatisfactory strength and water resistance, and achieve the effect of improving compactness, low early strength and high strength

Inactive Publication Date: 2015-05-06
无为县严桥双龙建材厂
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The strength and water resistance of concrete currently on the market are not ver...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The high-strength water-resistant concrete of the present invention, its raw material comprises the following components by weight: 220 parts of cement, 450 parts of sea sand, 480 parts of stones, 150 parts of water, 95 parts of slag micropowder, 35 parts of nickel slag micropowder, superfine 20 parts of fly ash, 30 parts of diatomaceous earth, 3 parts of desulfurized gypsum, 20 parts of nano-calcium carbonate, 5 parts of granite stone powder, 3 parts of fiber, 0.3 parts of superabsorbent resin, 1.9 parts of dipropyl glycol, stearin 0.3 parts of potassium acid potassium, 12 parts of nano magnesium oxide, 0.6 parts of early strength agent, 0.9 parts of retarder, 0.2 parts of foaming agent, 0.5 parts of foam stabilizer, and 0.2 parts of rust inhibitor.

[0020] The preparation method of the high-strength water-resistant concrete of the present invention comprises the following steps: mixing cement, sea sand and water and stirring, then adding slag micropowder, nickel slag ...

Embodiment 2

[0022] The high-strength water-resistant concrete of the present invention, its raw material comprises the following components by weight: 350 parts of cement, 330 parts of sea sand, 560 parts of stones, 90 parts of water, 150 parts of slag micropowder, 20 parts of nickel slag micropowder, superfine 50 parts of fly ash, 10 parts of diatomaceous earth, 9 parts of desulfurized gypsum, 5 parts of nano-calcium carbonate, 25 parts of granite stone powder, 1 part of glass fiber, 0.9 parts of superabsorbent resin, 1.2 parts of dipropyl glycol, hard 1.3 parts of potassium fatty acid, 3 parts of nano magnesium oxide, 1.2 parts of early strength agent, 0.3 parts of retarder, 0.5 parts of foaming agent, 0.1 part of foam stabilizer, 0.5 parts of rust inhibitor;

[0023] Wherein, the average particle size of the sea sand is 0.3mm; the average particle size of the stone is 8mm; the specific surface area of ​​the slag micropowder is 550m 2 / kg; the specific surface area of ​​the nickel slag ...

Embodiment 3

[0029] The high-strength water-resistant concrete of the present invention, its raw material comprises the following components by weight: 334.6 parts of cement, 427 parts of sea sand, 538 parts of stones, 131 parts of water, 142 parts of slag micropowder, 30 parts of nickel slag micropowder, superfine 33.4 parts of fly ash, 14 parts of diatomaceous earth, 8.2 parts of desulfurized gypsum, 15.3 parts of nano-calcium carbonate, 12.5 parts of granite stone powder, 1.83 parts of polyethylene fiber, 1 part of polyvinyl alcohol fiber, 0.53 parts of superabsorbent resin, dipropylene glycol 1.63 parts of ethylene glycol, 0.94 parts of potassium stearate, 11.4 parts of nano-magnesium oxide, 1.16 parts of early strength agent, 0.74 parts of retarder, 0.46 parts of foaming agent, 0.35 parts of foam stabilizer, and 0.34 parts of rust inhibitor;

[0030] Wherein, the average particle size of the sea sand is 0.6mm; the average particle size of the stone is 15mm; the specific surface area of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses high-strength waterproof concrete. The high-strength waterproof concrete contains the following raw material components: cement, sea sand, pebbles, water, superfine slag powder, superfine nickel slag powder, superfine coal ash, diatomite, flue gas desulfurization gypsum, nano-calcium carbonate, granite powder, fiber, super absorbent resin, dipropyl glycol, potassium stearate, nano-magnesium oxide, an early strength agent, a retarder, a foaming agent, a foam stabilizer and a corrosion inhibitor. The high-strength waterproof concrete is high in strength and good in water tolerance. The invention further discloses a preparation method of the high-strength waterproof concrete. The preparation method has the beneficial effects that the raw materials are easily available, the operation is easy, and the stability of the obtained concrete is good.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to a high-strength water-resistant concrete and a preparation method thereof. Background technique [0002] As a building material with a large amount and a wide range of use in the world, concrete has been widely developed in various countries and regions for its good mechanical properties, economy and adaptability to the environment. put forward higher requirements. As the most commonly used structural form in the field of civil engineering, concrete structures have extremely complex construction and service environments. The durability of concrete in harsh environments is particularly prominent, and has become a research hotspot at home and abroad. Strength and water resistance are important factors affecting the durability of concrete. The strength and water resistance of concrete currently on the market are not very ideal, and the durability is poor, which cannot meet the hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/02C04B28/14C04B14/06C04B18/30
CPCY02W30/91
Inventor 缪碧波
Owner 无为县严桥双龙建材厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap