Coating combination and metal material

A composition and coating technology, applied in the field of polymers, can solve the problems of poor adhesion and poor adhesion of metal substrates, and achieve the effects of low cost, convenient operation and simple process

Inactive Publication Date: 2015-06-24
CHANGCHUN INST OF APPLIED CHEMISTRY - CHINESE ACAD OF SCI
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The Chinese patent application number 201210071242.0 introduces cyano groups into phenolphthalein polyarylether ketone (PEK-C) to obtain polyarylether nitrile ketone, and mixes polyarylether nitrile ket

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating combination and metal material
  • Coating combination and metal material
  • Coating combination and metal material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0162] Add 0.268g (0.002mol) benzimidazolone, 2.547g (0.008mol) phenolphthalein, 0.671g (0.003075mol) 4,4'- difluorobenzophenone, 1.234g (0.007175 mol) 2,6-dichlorobenzonitrile, 1.589g potassium carbonate, 15g sulfolane and 20mL toluene, heat to 120°C to azeotropically remove water, keep warm for 1.5h, remove toluene, continue to heat to 210°C, react for 2.5h, cool down, Add 20mL DMAc to dilute, precipitate in ethanol / water, filter and pulverize the precipitate, wash it in deionized water 5 times, remove impurities such as inorganic salts and reaction solvents, and obtain a polyaryletherketone quaternary copolymer with the structure of formula III thing;

[0163]

[0164] Take 0.4000 g of the above-prepared polyaryletherketone tetrapolymer having the structure of formula IV after removing the terminal groups, and add 1.6 g of a mixed solvent of N,N-dimethylacetamide and tetrahydrofuran (volume ratio: 3:7) , add 0.008g of TMC-201, 0.006g of BYK-333 and 0.0002g of BYK-088, s...

Embodiment 2

[0170] 1.592g (0.005mol) of phenolphthalein, 0.671g (0.005mol) of benzimidazolone, 1.091g (0.005mol) of difluorobenzophenone, 0.860g (0.005mol) of 2,6 - Dichlorobenzonitrile, the catalyst is a mixed base, the mixed base includes 2.763g potassium carbonate and 1.060g sodium carbonate, 10g sulfolane, 5g diphenyl sulfone and 25mL toluene, heated to 130°C to azeotropically remove water, keep warm for 2h, remove Toluene, continue heating to 200°C, react for 5h, cool down, add 20mL DMAc to dilute, precipitate in ethanol / water, filter and pulverize the precipitate, wash it in deionized water for 7 times, remove impurities such as inorganic salts and reaction solvents, The polyaryletherketone tetrapolymer having the structure of formula VIII after removing the terminal groups was obtained, and the glass transition temperature was 279°C.

[0171]

[0172] Take 0.4000 g of the polyaryletherketone tetrapolymer having the structure of formula VIII after removing the terminal group, add...

Embodiment 3

[0177] 1.752g (0.005mol) bisphenol fluorene, 0.671g (0.005mol), 5,6-dimethyl benzimidazolone, 1.436g (0.005mol) dichlorodiphenyl sulfone, 0.860g (0.005mol) 2,6-dichlorobenzonitrile, the catalyst is a mixed base, the mixed base includes 2.763g potassium carbonate and 1.060g sodium carbonate, 15g sulfolane and 20mL benzene, heated to 90 ° C to azeotropically remove water, Insulate for 3 hours, remove benzene, continue heating to 190°C, react for 12 hours, cool down, add 20mL DMAc to dilute, precipitate in ethanol / water, filter and crush the precipitate, boil and wash 6 times in deionized water, remove inorganic salts and react Impurities such as solvents are removed to obtain a polyaryletherketone tetrapolymer having the structure of formula V after removing the end groups, and the glass transition temperature is 298°C.

[0178]

[0179] Take 0.4000 g of the polyaryletherketone tetrapolymer having the structure of formula V after removing the terminal group, add 1.6 g of a mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Impact strengthaaaaaaaaaa
Heat resistanceaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention provides a coating combination which comprises a coupling agent, a flatting agent, a defoaming agent, a solvent and a poly ether ketone quaternary copolymer. The poly ether ketone quaternary copolymer comprises repetitive units indicated in the formula of 101 and the formula of 102, and the repetitive units indicated in the formula of 101 and the formula of 102 are in the mass ratio of 0.01-100 to 1. The poly ether ketone quaternary copolymer is taken as a base material in the coating combination, and the coating combination is obtained by further adding proper additives; the poly ether ketone quaternary copolymer is characterized in that nitrogen containing groups of a benzene and imidazole structure, a carbazole structure and the like are introduced in the main chain of poly ether nitrile ketone, the chain structure of the poly ether nitrile ketone is changed, and adhesive force of the coating combination to metal is improved through interaction force between lone-pair electrons and a metallic matrix on N.

Description

technical field [0001] The invention belongs to the technical field of macromolecules, and in particular relates to a coating composition and a metal material. Background technique [0002] Phenolphthalein polyaryletherketone (PEK-C) is an amorphous polyaryletherketone resin obtained by polycondensation of phenolphthalein and dihalogenated benzophenone. It has a glass transition temperature of 231 °C and has high heat resistance and fatigue resistance , impact resistance, self-lubricating, high pressure hydrolysis resistance and radiation resistance, acid, alkali and aromatic alkanes chemical reagents and other excellent properties, its comprehensive performance can be compared with polyether ether ketone (PEEK), and its dissolution processing performance is unique It is widely used in high-tech fields such as aviation, aerospace, petrochemical and so on. [0003] Polyarylene ether nitrile is also a kind of thermoplastic high-performance engineering plastics. It was first c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D171/10C08G65/40
CPCC08G65/4025C09D171/10
Inventor 王红华王志鹏周光远苏小龙
Owner CHANGCHUN INST OF APPLIED CHEMISTRY - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap