Polypropylene composite material for vehicle door decoration plate

A technology for automobile doors and polypropylene, applied in the field of materials, can solve the problems of large shrinkage rate and easy denting of thick-walled products, and achieve the effects of excellent processing performance, improved bonding strength and simple production process

Inactive Publication Date: 2015-07-15
ANHUI HAINA SICHUAN PLASTICS TECH
View PDF12 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Good formability, but due to large shrinkage, thick-walled products are easy to sag, and it is difficult to meet the requirements for some parts with high dimensional accuracy. The surface of the product has good gloss and is easy to color

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of polypropylene compound material that is used for automobile door trim, it is made up of following raw materials of weight part:

[0021] Hydroxyl-terminated polybutadiene 4, lithium silicate 2-3, sodium mercaptobenzothiazole 0.5, diacetone alcohol 2, calcium ascorbate 0.7, propylene glycol adipate polyester 2, hydroxyethylidene diphosphonic acid 0.3, graphite powder 16 , polyamide wax powder 3, tricresyl phosphate 6, dimethylaminopropylamine 0.4, modification additive 4, polypropylene 105, antioxidant 168 0.7;

[0022] Described modification aid is made up of each raw material of following weight part:

[0023] Bamboo fiber 15, magnesium silicide 2, tea saponin 2, aluminum isopropoxide 0.3, ammonium persulfate 0.6, deionized water 30, butyl acrylate 3, silane coupling agent KH550 0.4;

[0024] Mix magnesium silicide and aluminum isopropoxide, stir evenly, add butyl acrylate, keep stirring at 60°C for 5 minutes, add silane coupling agent KH550, stir and disper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a polypropylene composite material for a vehicle door decoration plate. The polypropylene composite material comprises the following raw materials by weight: 4-7 parts of hydroxyl-terminated polybutadiene, 2-3 parts of lithium silicate, 0.5-1 part of sodium mercaptobenzothiazole, 1-2 parts of diacetone alcohol, 0.7-1 part of calcium ascorbate, 2-4 parts of hexanedioic acid propanediol polyester, 0.1-0.3 part of 1-hydroxyethylidene-1,1-diphosphonic acid, 10-16 parts of graphite powder, 3-5 parts of polyamide wax micro-powder, 4-6 parts of tricresyl phosphate, 0.4-1 part of dimethylaminopropylamine, 4-6 parts of a modification auxiliary agent, 100-105 parts of polypropylene, and 0.7-1 part of an antioxidant 168. The polypropylene composite material of the present invention is mainly used for producing the vehicle door decoration plate, and has characteristics of excellent impact resistance, excellent toughness, excellent rigidity, excellent scratching resistance, excellent processing performance, and simple production process.

Description

technical field [0001] The invention mainly relates to the field of materials, in particular to a polypropylene composite material used for automobile door trim. Background technique [0002] Polypropylene also includes copolymers of propylene and a small amount of ethylene. Usually translucent colorless solid, odorless and non-toxic. Due to the regular structure and high crystallization, the melting point can be as high as 167°C. Containing cobalt and zirconium, corrosion resistance, and the product can be sterilized by steam are its outstanding advantages. Low density, is the lightest general-purpose plastic. The disadvantage is that it has poor low temperature impact resistance and is easy to age, but it can be overcome by modification respectively; [0003] Polypropylene is a non-toxic, odorless, tasteless milky white highly crystalline polymer, and it is one of the lightest varieties of all plastics. It is particularly stable to water, its water absorption rate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L67/02C08L77/00C08L97/02C08L47/00C08K13/06C08K5/523C08K3/04C08K3/34C08K5/05C08K5/1545
CPCC08L23/12C08K2201/014C08L2201/08C08L2205/035C08L2205/16
Inventor 强健娜
Owner ANHUI HAINA SICHUAN PLASTICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap