A Molybdenum Oxide Nanoribbon/Graphene Composite Material and Its Application in the Preparation of Hydrogen Sensitive Elements

A technology of composite materials and sensitive components, applied in the direction of nanotechnology, nanotechnology, material resistance, etc., can solve the problems of repeatability and poor reliability, and achieve the effects of high controllability, small size, and increased comparative area

Inactive Publication Date: 2017-06-16
HUBEI UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the repeatability and reliability of the current composite method for preparing one-dimensional molybdenum oxide and graphene are poor, and both need to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Molybdenum Oxide Nanoribbon/Graphene Composite Material and Its Application in the Preparation of Hydrogen Sensitive Elements
  • A Molybdenum Oxide Nanoribbon/Graphene Composite Material and Its Application in the Preparation of Hydrogen Sensitive Elements
  • A Molybdenum Oxide Nanoribbon/Graphene Composite Material and Its Application in the Preparation of Hydrogen Sensitive Elements

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A preparation method of molybdenum oxide nanobelt / graphene composite material, comprising the steps of:

[0048] Step A: Preparation of Graphene Oxide

[0049] a1) Weigh 3.0g of graphite powder and 18.0g of potassium permanganate into a 1000ml beaker, stir for 10min with a glass rod, and mix well to obtain a solid mixed powder;

[0050] a2) Measure 360ml of concentrated sulfuric acid with a mass fraction of 98% and 40ml of concentrated phosphoric acid with a mass fraction of 65%, respectively, and add them to the beaker containing the solid mixed powder as described in step a1), stir magnetically for 30 minutes, and mix well to obtain a mixed liquid;

[0051] a3) Put the beaker containing the mixed liquid described in step a2) into a 50°C water bath, continue to stir, and keep warm for 12 hours to obtain a viscous liquid mixed product;

[0052] a4) Mix 10ml of hydrogen peroxide with a mass fraction of 30% and 500ml of distilled water respectively, then magnetically st...

Embodiment 2

[0076] A preparation method of molybdenum oxide nanobelt / graphene composite material, comprising the steps of:

[0077] Step A: Preparation of Graphene Oxide

[0078] Graphene oxide adopts the graphene oxide prepared by embodiment 1;

[0079] Step B: Preparation of molybdenum oxide nanoribbons / graphene composites

[0080] b1) In a 50ml reaction container, measure 0.75ml of the graphene oxide dispersion prepared in step A, measure 33ml of deionized water, stir and disperse evenly, and obtain a diluted dispersion;

[0081] b2) Slowly add 6.25ml of concentrated nitric acid with a mass fraction of 65% to the diluted dispersion obtained in step b1), continue to stir and mix evenly to obtain a mixed acid solution, the concentration of nitric acid in the mixed acid solution is 2.5mol / L ;

[0082] b3) Add 2.4195g of sodium molybdate (Na 2 MoO 4 2H 2 O), stirring slowly makes sodium molybdate fully dissolved, mixes evenly, obtains mixed reaction liquid, and the concentration of m...

Embodiment 3

[0097] A preparation method of molybdenum oxide nanobelt / graphene composite material, comprising the steps of:

[0098] Step A: Preparation of Graphene Oxide

[0099] Graphene oxide adopts the graphene oxide prepared in embodiment 1.

[0100] Step B: Preparation of molybdenum oxide nanoribbons / graphene composites

[0101] b1) In a 50ml reaction vessel, measure 0.5ml of the graphene oxide dispersion prepared in step A, measure 33.25ml of deionized water, stir and disperse evenly to obtain a diluted dispersion;

[0102] b2) Slowly add 6.25ml of concentrated nitric acid with a mass fraction of 65% to the diluted dispersion obtained in step b1), continue to stir and mix evenly to obtain a mixed acid solution, the concentration of nitric acid in the mixed acid solution is 2.5mol / L ;

[0103] b3) Add 2.4195g of sodium molybdate (Na 2 MoO 4 2H 2 O), stirring slowly makes sodium molybdate fully dissolved, mixes evenly, obtains mixed reaction liquid, and the concentration of moly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a one-dimensional nanometer metal molybdenum oxide nanobelt / graphene composite semiconductor material, which uses graphene oxide and Na 2 MoO 4 2H 2 O as the raw material, the molybdenum oxide nanobelt / graphene composite material was prepared by a one-step hydrothermal method. The preparation of graphene composites has the disadvantages of poor repeatability and unstable performance. In addition, the present invention also uses a simple method to coat the molybdenum oxide nanobelt / graphene composite material after ultrasonic dispersion on the interdigitated electrode, and prepares a hydrogen sensitive element with excellent performance. The response time of low-concentration hydrogen to 1000ppm (0.1%, volume fraction) hydrogen is only 10.6s, and the sensitivity is about 95%, showing the advantages of high sensitivity, fast response and short recovery time.

Description

technical field [0001] The invention belongs to the technical field of preparation of nano-composite semiconductor materials and gas-sensing components. Specifically, the invention relates to a one-dimensional nanometer metal molybdenum oxide nanoribbon / graphene composite semiconductor material and its preparation method and the use of the material in the preparation of hydrogen Applications in sensitive components. Background technique [0002] With the rapid development of economy and society, the consumption of fossil fuels is getting faster and faster, and the resulting energy crisis and environmental pollution are becoming more and more serious. Hydrogen has attracted more and more attention and research because of its advantages of wide sources, non-polluting products and automatic regeneration. At present, hydrogen, as a protective gas and reducing gas, has been widely used in many fields such as industrial production, medical and health care, national defense and mi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N27/12B82Y30/00B82Y40/00
Inventor 顾豪爽杨树林胡永明王钊罗显涛
Owner HUBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com