Multicolor decorative paint for cement tiles and preparation method thereof

A decorative coating and cement tile technology, applied in the field of decorative materials, can solve the problems of poor stain resistance and self-cleaning performance, poor freeze-thaw stability, low temperature resistance, etc., achieve good stain resistance and self-cleaning performance, and long service life , the effect of not easy to crack

Inactive Publication Date: 2015-09-09
SUZHOU DEXIANG DECORATION ENG
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005]Technical problems solved: In view of the shortcomings of the existing cement tile coatings, such as poor stain resistance and self-cleaning performance, low elasticity, low temperature resistance, and poor freeze-thaw stability, The invention provides a colorful decorative coating for cement tiles and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A colorful decorative paint for cement tiles, which contains the following components in parts by mass: 20 parts of water, 30 parts of styrene-acrylic emulsion, 6 parts of quartz powder, 0.8 parts of brown corundum, 10 parts of heavy calcium carbonate, 3 parts of natural rubber, urea-formaldehyde 1 part of resin glue, 0.1 part of soda ash, 0.3 part of calcium hexametaphosphate, 1.5 parts of ethylene glycol, 1.6 parts of tributyl phosphate, 0.01 part of sodium dodecyl sulfonate, 0.02 part of cumene hydroperoxide, organic silicon 0.7 parts of defoamer, 0.1 part of fatty acid methyl ester, 0.3 part of silicone emulsion, and 1.5 parts of dodecyl alcohol ester.

[0020] A preparation method of colorful decorative paint for cement tiles, the preparation steps of the method are as follows:

[0021] Step 1: Add water to the mixer, add styrene-acrylic emulsion, quartz powder, brown corundum, heavy calcium carbonate, natural rubber at a stirring speed of 70r / min, and stir to mix ...

Embodiment 2

[0025] A colorful decorative paint for cement tiles, which contains the following components in parts by mass: 32 parts of water, 46 parts of styrene-acrylic emulsion, 14 parts of quartz powder, 3.4 parts of brown corundum, 26 parts of heavy calcium carbonate, 9 parts of natural rubber, urea-formaldehyde 2.4 parts of resin glue, 0.5 parts of soda ash, 0.8 parts of calcium hexametaphosphate, 3.3 parts of ethylene glycol, 3.5 parts of tributyl phosphate, 0.05 parts of sodium dodecylsulfonate, 0.06 parts of cumene hydroperoxide, organic silicon 1.5 parts of defoamer, 0.4 parts of fatty acid methyl ester, 0.9 parts of silicone emulsion, 4.8 parts of dodecyl alcohol ester.

[0026] A preparation method of colorful decorative paint for cement tiles, the preparation steps of the method are as follows:

[0027] Step 1: Add water to the mixer, add styrene-acrylic emulsion, quartz powder, brown corundum, heavy calcium carbonate, and natural rubber at a stirring speed of 100r / min, and st...

Embodiment 3

[0031] A colorful decorative paint for cement tiles, which contains the following components in parts by mass: 30 parts of water, 42 parts of styrene-acrylic emulsion, 13 parts of quartz powder, 3 parts of brown corundum, 22 parts of heavy calcium carbonate, 8 parts of natural rubber, urea-formaldehyde 2.2 parts of resin glue, 0.4 parts of soda ash, 0.7 parts of calcium hexametaphosphate, 3 parts of ethylene glycol, 3.2 parts of tributyl phosphate, 0.04 parts of sodium dodecylsulfonate, 0.05 parts of cumene hydroperoxide, organic silicon 1.2 parts of defoamer, 0.35 parts of fatty acid methyl ester, 0.8 parts of silicone emulsion, 4 parts of dodecyl alcohol ester.

[0032] A preparation method of colorful decorative paint for cement tiles, the preparation steps of the method are as follows:

[0033] Step 1: Add water to the mixer, add styrene-acrylic emulsion, quartz powder, brown corundum, heavy calcium carbonate, and natural rubber at a stirring speed of 85r / min, and stir to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a multicolor decorative paint for cement tiles and a preparation method thereof. The paint contains the following components in parts by mass: 20-32 parts of water, 30-46 parts of styrene-acrylic emulsion, 6-14 parts of quartz powder, 0.8-3.4 parts of brown fused alumina, 10-26 parts of ground calcium carbonate, 3-9 parts of natural rubber, 1-2.4 parts of urea formaldehyde resin adhesive, 0.1-0.5 part of sodium carbonate, 0.3-0.8 part of calcium hexametaphosphate, 1.5-3.3 parts of ethylene glycol, 1.6-3.5 parts of tributyl phosphate, 0.01-0.05 part of sodium dodecylsulfate, 0.02-0.06 part of isopropyl benzene hydroperoxide, 0.7-1.5 parts of organosilicon defoaming agent, 0.1-0.4 part of fatty acid methyl ester, 0.3-0.9 part of silicone emulsion and 1.5-4.8 parts of alcohol ester-12. The paint provided by the invention has the advantages of favorable pollution-resistant and self-cleaning properties, abundant colors and favorable visual effect.

Description

technical field [0001] The invention relates to the technical field of decorative materials, in particular to a colorful decorative coating for cement tiles and a preparation method thereof. Background technique [0002] Cement tiles are made of cement through roll forming or high-pressure filtration through high-quality molds. Cement tiles have high density, high strength, good rain and frost resistance, smooth surface and accurate size. They are not only suitable for ordinary houses, but also for waterproof and heat insulation of high-end villas and high-rise buildings. Therefore, cement tiles are a common choice for modern construction projects. [0003] The color of the existing cement tile is relatively monotonous, because its aesthetics and practical value can be improved by coating paint. The existing coatings for cement tiles have poor stain resistance and self-cleaning performance, low elasticity, low temperature resistance and poor freeze-thaw stability. [0004...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/29C09D7/12
Inventor 秦勇
Owner SUZHOU DEXIANG DECORATION ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com