Polyolefin-kind high-molecular obstruction explosion-proof material and preparation method thereof

A technology for barrier explosion-proof materials and polyolefins, which is applied in the field of preparation of polyolefin polymer barrier explosion-proof materials, can solve the problems of complex molding process, oil quality pollution, and difficult recycling of non-metallic thermosetting polyurethane foam explosion-proof materials, etc. Achieve the effect of overcoming easy corrosion, low production cost and low price

Active Publication Date: 2015-11-25
JIANGSU AMPUTE EXPLOSION PREVENTION TECH
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is, for the traditional metal (aluminum alloy) explosion-proof materials and products, when methanol gasoline storage tanks and transport explosion-proof, it is easily corroded by additives in methanol gasoline and fragmented to cause pollution to the quality of oil products, and non- Metal thermosetting polyurethane foam explosion-proof materials have defects such as complicated molding process and difficult recycling. Design a polyolefin polymer barrier with low price, light weight, corrosion resistance, flame retardancy, antistatic, high fluidity, easy molding and recyclability. Explosion-proof material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyolefin-kind high-molecular obstruction explosion-proof material and preparation method thereof
  • Polyolefin-kind high-molecular obstruction explosion-proof material and preparation method thereof
  • Polyolefin-kind high-molecular obstruction explosion-proof material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The mass parts array of raw materials is: 80 parts of polyethylene, 20 parts of flame retardant (decabromodiphenyl ether and antimony trioxide mixture, mass ratio 2:1), 15 parts of conductive carbon black, 3.5 parts of foaming agent, nucleating 1.2 parts of nano-calcium carbonate, 5 parts of toughening agent, 2.5 parts of flame-retardant plasticizer phosphate, antioxidant tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate ] 2.5 parts of pentaerythritol esters.

[0031] The raw materials of the above formula are fully dried and mixed evenly in a high-speed mixer according to the proportion. Use Zhoushan Tongfa Machinery Manufacturing Co., Ltd. SJSZ-25 co-rotating conical twin-screw extruder (screw diameter 25mm, compression ratio 1:10), set the temperature at 180-220°C, screw speed 200 rpm, and extrude Granulate. After the obtained pellets were fully dried, they were molded into standard splines with an injection molding machine, and tested for mechanical prope...

Embodiment 2

[0035] The mass parts array of raw materials is: 80 parts of polypropylene, 25 parts of flame retardant (a mixture of decabromodiphenyl ether and antimony trioxide, mass ratio 2:1), 10 parts of conductive carbon black, 3.8 parts of foaming agent, nucleating 1.5 parts of nano-attapulgite, 10 parts of toughening agent, 2.5 parts of flame-retardant plasticizer phosphate, antioxidant tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid Esters] 2.5 parts of pentaerythritol esters.

[0036] The raw materials of the above formula are fully dried and mixed evenly in a high-speed mixer according to the proportion. Use Zhoushan Tongfa Machinery Manufacturing Co., Ltd. SJSZ-25 co-rotating conical twin-screw extruder (screw diameter 25mm, compression ratio 1:10), set the temperature at 220-260°C, screw speed 200 rpm, and extrude Granulate. After the obtained pellets were fully dried, they were injection molded into standard splines with an injection molding machine, and tested...

Embodiment 3

[0040] The mass parts array of raw materials is: 80 parts of polystyrene, 20 parts of flame retardant (decabromodiphenyl ether and antimony trioxide mixture, mass ratio 2:1), 15 parts of conductive carbon black, 3.8 parts of foaming agent, the composition 1.6 parts of nuclear agent nano-montmorillonite, 5 parts of toughening agent, 1 part of flame-retardant plasticizer phosphate, antioxidant tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propane Ester] 1 part of pentaerythritol ester.

[0041] The raw materials of the above formula are fully dried and mixed evenly in a high-speed mixer according to the proportion. Use Zhoushan Tongfa Machinery Manufacturing Co., Ltd. SJSZ-25 co-rotating conical twin-screw extruder (screw diameter 25mm, compression ratio 1:10), set the temperature at 150-220°C, screw speed 200 rpm, and extrude Granulate. After the obtained pellets were fully dried, they were molded into standard splines with an injection molding machine, and tested for mecha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of high-molecular materials, and especially relates to a preparation method for a polyolefin-kind high-molecular obstruction explosion-proof material. The method comprises fully drying polyolefin, a fire retardant, an antistatic agent, a flexibilizer and various auxiliary agents, uniformly mixing in a high-speed mixer, then adding into a screw-combined co-rotating conical twin-screw extruder with an appropriate length-diameter ratio, setting the extruder temperature to be 160-280 DEG C, performing cooling and heating processing, then sending into a slitting system, and cutting into an obstruction explosion-proof polyethylene material pellet with a fixed length, so as to prepare the obstruction explosion-proof material which is cheap in price, easy to process and excellent in performances.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a preparation method of a polyolefin polymer barrier explosion-proof material. Background technique [0002] Inflammable, explosive and dangerous chemicals such as fuel are extremely vulnerable to combustion and explosion caused by external energy such as static electricity, gunshots, and collisions during storage, transportation and use, resulting in chemical plants, oil refineries, gas stations, automobiles, oil trucks, oil depots, Oil storage tanks and other accidents caused explosions, which caused irreparable huge losses to the property of the country and the people. For this reason, various countries in the world have successively developed various explosion-suppressing materials. In recent years, in the storage and transportation of flammable and explosive dangerous chemicals, a safety technology for preventing explosions is vigorously promoted, whic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06C08L25/06C08L23/12C08L51/06C08K13/02C08K5/521C08K5/06C08K3/26C08K3/22C08K3/04C08J9/10
CPCC08J9/103C08L23/06C08L23/12C08L25/06C08L2201/02C08L2201/04C08L2205/24C08L51/06C08K13/02C08K3/04C08K2003/265C08K5/521C08K3/2279C08K5/06C08K3/34C08K3/346
Inventor 马国良
Owner JIANGSU AMPUTE EXPLOSION PREVENTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com