Montmorillonite-modified ethylene propylene diene monomer tubing

A technology of EPDM rubber and montmorillonite, applied in the field of EPDM rubber, can solve the problems of unsatisfactory heat resistance and aging resistance, slow vulcanization speed, insufficient oil resistance, etc., and achieve improvement of slow vulcanization speed , Improve wear resistance, increase the effect of crosslinking density

Inactive Publication Date: 2016-04-27
安徽都邦电器有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] EPDM rubber not only has excellent heat resistance, oxygen resistance, ozone resistance, weather resistance and aging resistance, but also has good chemical resistance, electrical insulation performance and low temperature performance. In addition, it also has low density and high filling property. and hot water resistance, etc., have been widely used in wire and cable, auto parts, heat-resistant hoses, home appliances an

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of montmorillonite modified EPDM pipe material proposed by the present invention, its raw material comprises the following components by weight: 50 parts of EPDM rubber, 35 parts of butadiene rubber, 10 parts of silicone rubber, 15 parts of styrene-butadiene rubber 5 parts of epoxy resin, 5 parts of liquid nitrile rubber, 2 parts of 1,2-polybutadiene, 1.5 parts of stearic acid, 2 parts of zinc oxide, 1,4-bis-tert-butylperoxyisopropyl 2 parts of benzene, 0.2 parts of bis(diisopropyl)phosphoryl disulfide, 1.5 parts of sulfur, 10 parts of modified montmorillonite, 15 parts of magnesium hydroxide, 5 parts of magnesium methacrylate, and 10 parts of carbon nanotubes , 5 parts of attapulgite, 10 parts of polyacrylonitrile fiber, 3 parts of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, 12 parts of ammonium polyphosphate, 3 parts of tricresyl phosphate 1 part, 5 parts of castor oil, 3 parts of silane coupling agent, 1 part of 2-mercaptobenzothiazole, 0.1 part of sod...

Embodiment 2

[0017] A kind of montmorillonite modified EPDM pipe material proposed by the present invention, its raw material comprises the following components by weight: 65 parts of EPDM rubber, 20 parts of butadiene rubber, 20 parts of silicone rubber, 5 parts of styrene-butadiene rubber 10 parts of epoxy resin, 2 parts of liquid nitrile rubber, 5 parts of 1,2-polybutadiene, 0.5 parts of stearic acid, 1 part of zinc oxide, 1,4-bis-tert-butylperoxyisopropyl 1 part of benzene, 1.2 parts of bis(diisopropyl)phosphoryl disulfide, 0.8 parts of sulfur, 25 parts of modified montmorillonite, 5 parts of magnesium hydroxide, 15 parts of magnesium methacrylate, and 5 parts of carbon nanotubes , 10 parts of attapulgite, 3 parts of polyacrylonitrile fiber, 12 parts of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, 5 parts of ammonium polyphosphate, 8 parts of tricresyl phosphate 3 parts of castor oil, 10 parts of silane coupling agent, 0.3 parts of 2-mercaptobenzothiazole, 1 part of sodium dimet...

Embodiment 3

[0019]A kind of montmorillonite modified EPDM pipe material proposed by the present invention, its raw material comprises the following components by weight: 62 parts of EPDM rubber, 28 parts of butadiene rubber, 17 parts of silicone rubber, 9 parts of styrene-butadiene rubber 8.5 parts of epoxy resin, 3.5 parts of liquid nitrile rubber, 4 parts of 1,2-polybutadiene, 0.8 parts of stearic acid, 1.8 parts of zinc oxide, 1,4-bis-tert-butylperoxyisopropyl 1.5 parts of benzene, 1.1 parts of bis(diisopropyl)phosphoryl disulfide, 1 part of sulfur, 21 parts of modified montmorillonite, 8 parts of magnesium hydroxide, 12 parts of magnesium methacrylate, and 7 parts of carbon nanotubes , 8 parts of attapulgite, 5.8 parts of polyacrylonitrile fiber, 10 parts of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, 8 parts of ammonium polyphosphate, 6.5 parts of tricresyl phosphate 3.8 parts of castor oil, 7 parts of silane coupling agent, 0.58 part of 2-mercaptobenzothiazole, 0.9 part of s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a montmorillonite-modified ethylene propylene diene monomer (EPDM) tubing, raw materials of which comprise EPDM, cis-polybutadiene, silicone rubber, styrene butadiene rubber, epoxy resin, liquid nitrile-butadiene rubber, 1,2-polybutadiene, stearic acid, zinc oxide, 1,4-bis(1-(tert-butylperoxy)-1-methylethyl)-benzene, bis(diisopropyl)DIPDIS, sulphur, modified montmorillonite, magnesium hydroxide, magnesium methacrylate, carbon nanotube, attapulgite, polyacrylonitrile fibre, 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, ammonium polyphosphate, tritolyl phosphate, castor oil, a silane coupling agent, 2-mercaptobenzothiazole, sodium dimethyldithiocarbamate and an anti-aging agent. The montmorillonite-modified EPDM tubing of the invention has advantages of high strength, good oil resistance, good heat resistance, good ageing resistance, excellent flame resistance and long service life.

Description

technical field [0001] The invention relates to the technical field of EPDM rubber, in particular to a montmorillonite-modified EPDM rubber pipe. Background technique [0002] EPDM rubber not only has excellent heat resistance, oxygen resistance, ozone resistance, weather resistance and aging resistance, but also has good chemical resistance, electrical insulation performance and low temperature performance. In addition, it also has low density and high filling property. and hot water resistance, etc., have been widely used in wire and cable, auto parts, heat-resistant hoses, home appliances and other fields, but EPDM rubber also has the disadvantages of poor oil resistance and slow vulcanization speed. In addition, as an organic polymer The material has the defect of being flammable. With the rapid development of world industry, the quantity and quality requirements of EPDM rubber are getting higher and higher. Simple EPDM materials can no longer fully meet the requiremen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08L9/00C08L83/04C08L9/06C08L63/00C08L9/02C08K13/06C08K9/04C08K9/02C08K9/06C08K3/34C08K7/24
CPCC08L23/16C08K2201/011C08K2201/014C08L2201/02C08L2201/08C08L2203/18C08L2205/02C08L2205/035C08L2205/08C08L2205/16C08L2312/00C08L9/00C08L83/04C08L9/06C08L63/00C08L9/02C08K13/06C08K9/08C08K9/04C08K9/02C08K9/06C08K3/346C08K7/24
Inventor 聂锐
Owner 安徽都邦电器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap