Elastic cushioning rubber material and preparation method thereof

A rubber material and anti-buffering technology, applied in the field of rubber, can solve the problems of low tear strength and tensile strength, poor wet skid resistance, poor processing performance, etc., and achieve high resilience, improved weather resistance, and improved mechanical properties. Effect

Inactive Publication Date: 2016-06-22
宁波远欣石化有限公司
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the main disadvantages of finished materials made of single butadiene rubber are poor wet skid resistance, low tear strength and tensile strength, high cold flow, and poor processability. Traditional methods to improve these shortcomings are to us...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] A kind of elastic anti-buffer rubber material, it is made up of the following raw materials of weight part:

[0022] Magnesium oxide 0.1, zinc oxide 1, accelerator TMTD0.8, sulfur 1, antioxidant AW1, tributyl citrate 7, buffer additive 5, medical stone powder 2, ethylene glycol monobutyl ether 4, propylene glycol alginate 1. Polybenzimidazole fiber 3, oxidized polyethylene wax 2, 8-hydroxyquinoline copper 0.7, silane coupling agent KH5600.1, butadiene rubber 100, wollastonite powder 10, dodecyltrimethylammonium chloride 0.7;

[0023] Described buffer aid is made up of the raw material of following weight part:

[0024] Polyurethane thermoplastic elastomer 20, polydimethylsiloxane 0.1, polyamide wax 2, lauryl mercaptan 0.2, toluene diisocyanate 2, N, N diethylaniline 0.1, calcium stearate 7, sp800. 3. Anhydrous ethanol 40;

[0025] The preparation method of described buffer aid comprises the following steps:

[0026] (1) Add the above-mentioned polyamide wax to absol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Breaking strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an elastic anti-buffer rubber material, which is composed of the following raw materials in parts by weight: magnesium oxide 0.1-0.3, zinc oxide 1-2, accelerator TMTD 0.8-1, sulfur 1-2, anti-aging Agent AW1-2, tributyl citrate 7-9, buffer additive 5-7, medical stone powder 2-4, ethylene glycol monobutyl ether 4-6, propylene glycol alginate 1-2, polybenzimidazole Fiber 3-4, oxidized polyethylene wax 2-4, 8-hydroxyquinoline copper 0.7-1, silane coupling agent KH5600.1-0.2, butadiene rubber 100-140, wollastonite powder 10-12, dodecane Base trimethyl ammonium chloride 0.7-1; The present invention adopts polyurethane thermoplastic elastomer as the main body of the anti-buffer material, which not only has good impact strength, but also can improve various mechanical properties of finished rubber and improve weather resistance. The anti-buffer rubber material invented has good flexibility and high resilience, and can be used as a variety of safety protection buffer materials. It has no volatilization of toxic and harmful components, and is safe and reliable.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to an elastic anti-buffer rubber material and a preparation method thereof. Background technique [0002] Butadiene rubber is the abbreviation of cis-1,4-polybutadiene rubber, and its molecular formula is (C4H6)n. Butadiene rubber is a synthetic rubber with regular structure formed by the polymerization of butadiene, and its cis structure content is more than 95%. According to different catalysts, it can be divided into nickel-based, cobalt-based, titanium-based and rare earth-based (Nd-based) butadiene rubber. Butadiene rubber is the second largest synthetic rubber after styrene-butadiene rubber. Compared with natural rubber and styrene-butadiene rubber, it has excellent cold resistance, wear resistance and elasticity after vulcanization, less heat generation under dynamic load, and good aging resistance. It is easy to use with natural rubber, neoprene or nitrile rubber. Butadien...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/00C08L75/04C08L79/04C08K13/02C08K3/34C08K3/22C08K3/06C08K5/11
CPCC08L9/00C08L2205/035C08L2205/16
Inventor 施利群
Owner 宁波远欣石化有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products