Water-thinned epoxy wood white primer and preparation method thereof
An epoxy woodware, water-dilutable technology, applied in the field of paint, can solve the problems of poor physical and chemical properties of the coating film, unstable coating film quality, poor yellowing resistance of PU white primer, etc., and achieve improved yellowing resistance , Excellent color fastness, excellent light stability effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0026] Example 1
[0027] Prepare the main paint: weigh 100kg according to the following mass percentages: weigh 52kg of bisphenol A epoxy resin E44, 0.3kg of polyether modified polysiloxane defoamer, and high molecular weight block containing pigment affinity groups Copolymer dispersant 0.6kg, polyether modified polydimethylsiloxane leveling agent 0.4kg, organic bentonite 1kg, rutile titanium dioxide 18kg, zinc stearate and talc mixed filler 12kg, propylene glycol methyl ether 7.7 kg, ethanol 8kg; after weighing the raw materials according to the above mass components, first fully mix the dispersant at room temperature to avoid stratification and turbidity during storage and transportation, which will affect its effect; next, bisphenol A epoxy Resin E44 and half of the mass of propylene glycol methyl ether and ethanol were put into the container and stirred and mixed uniformly, and then respectively added polyether modified polysiloxane defoamer, high molecular weight block copo...
Example Embodiment
[0030] Example 2
[0031] Prepare the main paint; weigh a total of 100 kg according to the following mass components: weigh 46 kg of bisphenol A epoxy resin E44, 0.2 kg of polyether modified polysiloxane defoamer, and high molecular weight embedded pigment with affinity groups. Segment copolymer dispersant 0.5kg, polyether modified polydimethylsiloxane leveling agent 0.3kg, organic bentonite 1.5kg, rutile titanium dioxide 15.5kg, zinc stearate and talc mixed filler 16kg, propylene glycol Methyl ether 11kg, ethanol 9kg; after weighing the raw materials according to the above mass components, first fully mix the dispersant at room temperature to avoid stratification and turbidity during storage and transportation that affect its effect; next, bisphenol A type Epoxy resin E44 and half of the mass of propylene glycol methyl ether and ethanol are put into the container and mixed evenly, then add polyether modified polysiloxane defoamer and high molecular weight block copolymer contain...
Example Embodiment
[0034] Example 3
[0035] Prepare the main paint: weigh 100kg according to the following mass percentages: Prepare the main paint: weigh 100kg according to the following mass percentages: weigh 42kg of bisphenol A epoxy resin E44, and 0.3 of polyether modified polysiloxane defoamer kg, high molecular weight block copolymer dispersant containing pigment affinity group 0.5kg, polyether modified polydimethylsiloxane leveling agent 0.4kg, organic bentonite 2kg, rutile titanium dioxide 15kg, stearic acid Zinc and talc mixed type filler 20kg, propylene glycol methyl ether 9.8kg, ethanol 10kg; after weighing the raw materials according to the above quality components, first fully mix the dispersant at room temperature to avoid stratification and turbidity during storage and transportation Affect its effect; then put the bisphenol A epoxy resin E44 and half of the mass of propylene glycol methyl ether and ethanol into the container and stir and mix evenly, and then add the polyether modi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap