Antifouling dry-powdered emulsion paint and preparation method thereof

A technology of dry powder latex and latex paint, applied in the field of paint, can solve the problems of inconvenient packaging, transportation and storage, waste of resources, poor coating hardness and other problems of liquid latex paint, and achieve increased consistency and water retention performance, convenient storage and transportation, and improved The effect of microporous structure

Active Publication Date: 2016-08-10
许英男
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the latex paints used in architectural decoration on the market are liquid, with a moisture content of more than 30%, which is easy to deteriorate, and must be added with preservatives, which is poor in environmental protection; moreover, liquid latex paints are not easy to pack, transport and store, store and use liquid latex Paint requires a large number of plastic or iron storage tanks, which are expensive, waste resources, and pollute the environment
In addition, the existing latex paint is completely dependent on resin film formation, the coating has poor hardness, is not resistant to collisions, scratches, and stains

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antifouling dry-powdered emulsion paint and preparation method thereof
  • Antifouling dry-powdered emulsion paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] The present embodiment provides a kind of antifouling dry powder latex paint, and raw material component comprises:

[0054] Particle size is 300 mesh white cement, 15 parts by weight;

[0055] Light calcium carbonate with a particle size of 600 meshes, 8 parts by weight;

[0056] Granularity 600 mesh heavy calcium carbonate, 6 parts by weight;

[0057] Granularity is 400 mesh ash calcium, 35 parts by weight;

[0058] Talcum powder, 10 parts by weight;

[0059] Kaolin, 8 parts by weight;

[0060] Titanium dioxide, 8 parts by weight;

[0061] Hydroxyethyl cellulose ether, 0.4 parts by weight;

[0062] VAE redispersible latex powder (Shanxi Sanwei Group, SWF-04 type), 10 parts by weight;

[0063] Polycarboxylate superplasticizer (Swiss Sika Viscocrete 325C), 0.3 parts by weight;

[0064] Sodium gluconate, 0.05 parts by weight;

[0065] Sodium stearate, 0.5 parts by weight;

[0066] Nano silicon dioxide, 1.5 parts by weight;

[0067] PAC, 1.5 parts by weight;

...

Embodiment 2

[0074] The present embodiment provides a kind of antifouling dry powder latex paint, and raw material component comprises:

[0075] Particle size is 1000 mesh white cement, 20 parts by weight;

[0076]Granularity 1200 purpose light calcium carbonate, 10 parts by weight;

[0077] Granularity 1200 purpose heavy calcium carbonate, 8 parts by weight;

[0078] Granularity is 750 mesh ash calcium, 15 parts by weight;

[0079] Talcum powder, 10 parts by weight;

[0080] Kaolin, 8 parts by weight;

[0081] Titanium dioxide, 10 parts by weight;

[0082] Hydroxyethyl cellulose ether, 0.3 parts by weight;

[0083] VAE redispersible latex powder (Shanxi Sanwei Group, SWF-04 type), 12 parts by weight;

[0084] Polycarboxylate superplasticizer (Swiss Sika Viscocrete 325C), 0.5 parts by weight;

[0085] Sodium gluconate, 0.15 parts by weight;

[0086] Sodium stearate, 1 part by weight;

[0087] Nano silica, 2 parts by weight;

[0088] PAC (Zhengzhou Runquan Chemical Products Co., L...

Embodiment 3

[0097] The present embodiment provides a kind of antifouling dry powder latex paint, and raw material component comprises:

[0098] Particle size is 600 mesh white cement, 20 parts by weight;

[0099] Light calcium carbonate with a particle size of 800 meshes, 8 parts by weight;

[0100] 800 meshes of heavy calcium carbonate, 10 parts by weight;

[0101] Granularity is 550 mesh ash calcium, 25 parts by weight;

[0102] Talcum powder, 12 parts by weight;

[0103] Kaolin, 10 parts by weight;

[0104] Titanium dioxide, 14 parts by weight;

[0105] Hydroxyethyl cellulose ether, 0.6 parts by weight;

[0106] VAE redispersible latex powder, 8 parts by weight;

[0107] Polycarboxylate water reducer, 0.4 parts by weight;

[0108] Sodium gluconate, 0.1 parts by weight;

[0109] Sodium stearate, 0.7 parts by weight;

[0110] Nano silica, 2.5 parts by weight;

[0111] PAC, 2.5 parts by weight;

[0112] Organosilicon water repellent, 0.2 parts by weight;

[0113] Thickener, 1 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to an antifouling dry-powdered emulsion paint. Global hardness is provided by the utilization of network-like mineral formed by white cement hydration; an ash-calcium modifying agent is added to improve properties of ash-calcium, and ash-calcium is carbonized to generate netted calcium carbonate which interpenetrates to reinforce middle and late hardness; supported by VAE redispersible latex powder, the system's flexibility and elasticity are improved; by the addition of a composite water reduction material, it is guaranteed that various materials are uniformly dispersed in the system, and micropore structure of the system is improved; by the addition of talcum powder and kaolin, construction performance is improved; by the addition of hydroxyethyl cellulose ether, the system's denseness and water retention capacity are increased; by the introduction of superfine nano-silica, compactness of the system is improved; by the addition of a water repellent, the coating is endowed with overall waterproofing property; and polyaluminum chloride is further added to react with calcium hydroxide in the system so as to generate expansile aluminium hydroxide and hydrated chloroaluminate. Thus, the coating becomes a compact integral body and has strong antifouling performance and good air permeability.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to an antifouling dry powder latex paint and a preparation method thereof. Background technique [0002] Latex paint, also known as latex paint, is a kind of organic paint, which is prepared by adding pigments, fillers and various additives with synthetic resin as the base material. According to different production materials, latex paint mainly includes polyvinyl acetate latex paint, ethylene-propylene latex paint, pure acrylic latex paint, styrene-acrylic latex paint and other varieties; according to different product application environments, it is divided into interior wall latex paint and exterior wall latex paint. There are two types of lacquer; according to the gloss effect of decoration, it can be divided into dull, matte, semi-gloss, mercerized and glossy. [0003] Most of the latex paints used in architectural decoration on the market are liquid, with a moist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2111/00482C04B14/28C04B14/36C04B14/10C04B14/106C04B14/305C04B24/386C04B24/26C04B2103/302C04B14/06C04B22/12C04B24/04C04B24/10C04B24/40
Inventor 许英男
Owner 许英男
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap