Method for preparing high-purity rhenium powder from rhenium-containing high-arsenic copper sulfide

A copper sulfide, high-purity technology, applied in the field of preparation of high-purity rhenium powder, to achieve high yield, simple process, and good industrial application prospects

Active Publication Date: 2016-10-05
KUNMING METALLURGY COLLEGE
View PDF16 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0020] These processes are mainly to separate and recover rhenium from leaching raw ore, waste catalyst, waste liquid and soot, and the method of preparing high-purity rhenium powder by...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high-purity rhenium powder from rhenium-containing high-arsenic copper sulfide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] See attached figure 1 , Conditions: 1000 grams of rhenium-arsenic copper sulfide raw material, the amount of nitric acid added is twice the weight ratio of rhenium-arsenic copper sulfide raw material, slowly heated to 85°C, stirring speed is 250rpm, leaching time is 5h, the flue gas enters the absorption tower , using oxygen enrichment and water spray absorption to form dilute nitric acid. After leaching, filter and wash to obtain leaching solution and leaching residue respectively. Add quicklime to the leaching solution and stir to neutralize residual nitric acid, control the pH to 8.5, filter and wash to obtain Arsenic-copper slag and low-content rhenium-containing filtrate, wherein the arsenic and copper in the slag enter the slag in the form of calcium arsenate and copper hydroxide respectively; the low-content rhenium-containing filtrate uses D296 resin for ion exchange, and after exchange and elution, pure Ammonium rhenate solution is heated and concentrated, and ...

Embodiment 2

[0034] See attached figure 1 , conditions: 1500 grams of rhenium-arsenic-containing copper sulfide raw materials, the amount of nitric acid added is 3.5 times the weight ratio of rhenium-arsenic-containing copper sulfide raw materials, slowly heated to 95°C, stirring speed is 250rpm, leaching time is 4h, and the flue gas enters the absorption tower , using sodium persulfate and water spray absorption to form dilute nitric acid, after leaching, filter and wash to obtain leaching solution and leaching residue respectively, add hydrated lime to the leaching solution and stir to neutralize residual nitric acid, control pH to 9.0, filter and wash, respectively Obtain arsenic-copper slag and low-content rhenium-containing filtrate, wherein the arsenic and copper in the slag enter the slag in the form of calcium arsenate and copper hydroxide respectively; the low-content rhenium-containing filtrate uses Tulsion CR-75 resin for ion exchange, after exchange and washing After desorption...

Embodiment 3

[0036] See attached figure 1 , conditions: 8000 grams of rhenium-arsenic-containing copper sulfide raw materials, the amount of nitric acid added is 4.0 times the weight ratio of rhenium-arsenic copper sulfide-containing raw materials, slowly heated to 85°C, stirring speed is 250rpm, leaching time is 5h, and the flue gas enters the absorption tower , use hydrogen peroxide and water spray to absorb, form dilute nitric acid, after leaching, filter and wash to obtain leaching solution and leaching residue respectively, add hydrated lime to the leaching solution and stir to neutralize residual nitric acid, control pH to 9.5, filter and wash to obtain arsenic Copper slag and low-content rhenium-containing filtrate, wherein the arsenic and copper in the slag enter the slag in the form of calcium arsenate and copper hydroxide respectively; the low-content rhenium-containing filtrate uses Tulsion RCX-5143 resin for ion exchange, after exchange and elution, Obtain pure ammonium rhenate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for high-effectively enriching rhenium from rhenium-containing high-arsenic copper sulfide. The method includes: rhenium-rich slag and a certain amount of alkali are mixed to obtain size, and pressing, heating and alkaline leaching is performed, and after filtering and washing is performed, rhenium enters extract in the form of ammonium rhenate, and a part of arsenic enters the extract in the form of sodium arsenate. Reactive metal power is heated to replace the rhenium in the extract, and after filtering and washing is performed, the rhenium oxide is enriched, and separation between the rhenium and the arsenic can be achieved. The raw material of the method is the rhenium-rich slag which is obtained by sulfide precipitation of acidic wastewater generated during a production process of copper smelting enterprises and is rich in copper and arsenic; the method can fully leach the rhenium, and the metal power is used to replace the extract to obtain a rhenium-enrichment; the process of rhenium extraction can be simplified, and the cost of rhenium extraction is reduced. The method is simple in process, is short in flow, is high in enrichment ratio, is high in material adaptability, is low in cost, is easy to industrialize, has good application value, and can increase output value and profit of the copper smelting enterprises.

Description

technical field [0001] The invention belongs to the field of rare metal metallurgy and material preparation, and relates to a method for preparing high-purity rhenium powder from rhenium-containing high-arsenic copper sulfide. Background technique [0002] The rhenium-containing high-arsenic copper sulfide raw material is a kind of difficult-to-handle rhenium extraction material, which generally comes from the materials produced in the intermediate smelting process of copper smelters. At present, China is the country that produces the most copper in the world, and a large amount of this material Rhenium material has a high value, and now major copper smelting enterprises are paying attention to the extraction and recovery of rhenium. In order to recover rhenium better, a method for preparing high-purity rhenium powder from rhenium-containing high-arsenic copper sulfide was invented. At present, the methods for extracting rhenium from various rhenium-containing materials are...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F9/20
Inventor 范兴祥余宇楠张凤霞
Owner KUNMING METALLURGY COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap