Comprehensive anti-corrosion coating with alloy co-doping, Dacromet and sealing layer
A technology of anti-corrosion coating and sealing layer, which is applied in the direction of anti-corrosion coating, metal material coating technology, coating, etc., can solve the problems of insufficient surface hardness, chromium pollution, etc., and achieve the effect of high surface hardness and good anti-corrosion performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
specific Embodiment 1
[0022] An alloy co-infiltration, dacromet and sealing layer comprehensive anti-corrosion coating provided in this embodiment includes alloy co-infiltration agent, dacromet coating liquid and sealing liquid:
[0023] The alloy co-infiltration agent includes the following components in parts by mass: 100 parts of zinc powder, 15 parts of aluminum powder, 85 parts of alumina powder, 20 parts of nickel powder, 3 parts of cerium oxide powder, 0.6 part of ammonium chloride, the above raw materials The particle size is 300 mesh; the zinc powder, aluminum powder, alumina powder, nickel powder and cerium oxide powder in the above raw materials are mixed evenly, heated to 150-200°C, kept for 30-50 minutes and then cooled to After mixing with ammonium chloride at room temperature, the alloy co-penetration agent is prepared;
[0024] Dacromet anti-corrosion coating solution, including A component and B component; A component includes the following components in parts by mass: 10 parts of ...
specific Embodiment 2
[0027] A kind of alloy co-infiltration, dacromet and sealing layer comprehensive anti-corrosion coating provided by this embodiment, the main formula composition is the same as that of specific embodiment 1, and the difference with specific embodiment 1 is:
[0028] The alloy co-infiltration agent includes the following components in parts by mass: 100 parts of zinc powder, 10 parts of aluminum powder, 100 parts of alumina powder, 30 parts of nickel powder, 5 parts of cerium oxide powder, and 0.8 part of ammonium chloride;
[0029] Dacromet anti-corrosion coating solution, component A includes the following components in parts by mass: 10 parts of zinc flakes and aluminum flakes, wherein the ratio of zinc flakes and aluminum flakes is 2:1; 55 parts of deionized water, fatty alcohol polyoxygen 2.0 parts of vinyl ether; B component includes the following components in parts by mass: 10 parts of amorphous compound molybdate compound, 15 parts of barium salt, 0.6 part of hydrogen p...
specific Embodiment 3
[0032] A kind of alloy co-infiltration, dacromet and sealing layer comprehensive anti-corrosion coating provided by this embodiment, the main formula composition is the same as that of specific embodiment 1, and the difference with specific embodiment 1 is:
[0033] The alloy co-infiltration agent includes the following components in parts by mass: 100 parts of zinc powder, 20 parts of aluminum powder, 80 parts of alumina powder, 10 parts of nickel powder, 2 parts of cerium oxide powder, and 0.5 part of ammonium chloride;
[0034] Dacromet anti-corrosion coating solution, component A includes the following components in parts by mass: 10 parts of zinc flakes and aluminum flakes, wherein the ratio of zinc flakes and aluminum flakes is 2:3; 60 parts of deionized water, fatty alcohol polyoxygen 0.5 parts of vinyl ether; B component includes the following components in parts by mass: 10 parts of amorphous compound molybdate compound, 5 parts of barium salt, 0.8 part of hydrogen per...
PUM
Property | Measurement | Unit |
---|---|---|
Vickers hardness value | aaaaa | aaaaa |
Vickers hardness value | aaaaa | aaaaa |
Epoxy value | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com