Production method of high-purity lithium hydroxide
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A lithium hydroxide, high-purity technology, applied in the field of salt chemical industry, can solve the problems of long and complex process routes, high cost of raw and auxiliary materials, and low yield of lithium ions, and achieve simple process routes, high comprehensive utilization of resources, lithium The effect of high ion yield
Active Publication Date: 2016-10-12
启迪清源(上海)新材料科技有限公司
View PDF4 Cites 38 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0009] It can be seen that when extracting lithium from salt lakes, lithium chloride is used to produce lithium carbonate, and then lithium carbonate is used as raw material to produce lithium hydroxide by causticization, the process route is long and complicated, the yield of lithium ions is low, the cost of raw and auxiliary materials is high, and resources are seriously wasted. , poor product quality
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0039] The best implementation mode of the present invention is described below through the preferred embodiment. The specific implementation mode here is to illustrate the present invention in detail, and should not be construed as a limitation of the present invention, without departing from the spirit and essential scope of the present invention , various variations and modifications can be made, all of which should be included within the protection scope of the present invention.
[0040] The preferred embodiment of the present invention provides a method for producing high-purity lithium hydroxide. The production method of this high-purity lithium hydroxide comprises the following steps:
[0041]a. Obtain the first concentrated solution concentrated by reverse osmosis, wherein the content of magnesium ions is ≤30ppm, the content of lithium ions is about 4-6g / L, the content of sodium ions is 3-5g / L, the content of calcium ions is ≤5ppm, potassium Ion ≤ 300ppm, sulfate ion...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The present invention relates to a production method of high-purity lithium hydroxide. A crystallization mother liquor waste water is obtained after production of potassium chloride by using a salt lake bittern as the raw material, a magnesium-lithium ratio of the crystallization mother liquor waste water is 200-500:1, an eligible eluant is obtained through ion sieve adsorption and elution of the crystallization mother liquor waste water, and after treatment of the eluant through the ultrafiltration membrane technology, the sectional type nanofiltration technology, the external regeneration continuous hybridization technology and the reverse osmosis technology, a reverse osmosis concentrated solution is obtained. In the reverse osmosis concentrated solution, the content of magnesium ions is <=300 ppm, the content of lithium ions is 4-6 g / L, the content of sodium ions is 3-5 g / L, the content of calcium ions is <=5 ppm, the content of sulfate ions is 1-30 ppm and the content of boron is <=400 ppm. According to the production method provided by the present invention, the reverse osmosis concentrated solution is used as the raw material, the process comprises ultrahigh pressure reverse osmosis continuous hybridization for boron-removing, continuous hybridization for sulfate radical removing, ion-exchange membrane electrolysis, and crystallizing evaporation, and by using the hybridization boron-removing technology, the ion-exchange membrane electrolysis technology and the crystallizing evaporation technology, the high-purity lithium hydroxide is obtained, with the byproducts being the boric acid and sodium hydroxide. The process is continuous, controllable, high in extraction rate, low in production cost and easy to industrialize.
Description
technical field [0001] The invention belongs to the field of salt chemical industry, in particular to a production method of high-purity lithium hydroxide. Background technique [0002] The bittern after extracting potassium is used as raw material. The ratio of magnesium to lithium in the raw material reaches 200-500:1, and the ratio of magnesium to lithium in the qualified eluent after ion sieve adsorption and elution drops to 3-4:1. After ultrafiltration technology, segmented nanofiltration technology, and in vitro regeneration The reverse osmosis concentrate is obtained after separation and purification by continuous separation technology and reverse osmosis technology. Among them, the magnesium ion content is ≤30ppm, the lithium ion content is about 4-6g / L, the sodium ion content is 3-5g / L, the calcium ion content is ≤5ppm, the potassium ion content is ≤300ppm, and the sulfate ion content is 1-30ppm. The content of boron element is ≤400ppm. In the traditional process...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.