A thermal insulation composite board and polyurethane technology, applied in the field of building materials, can solve problems such as hidden safety hazards of external wall and external thermal insulation system, poor weather resistance and deformation of composite boards

Inactive Publication Date: 2016-10-26
ANHUI GUANGYAN NEW MATERIAL TECH
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The weather resistance of the composite board is not good, and after a period of weather resistance, it will fall off or crack, deform, etc., which will bring hidden dangers to the safety of the external wall insulation system
Moreover, the comprehensive performance and production efficiency of ordinary polyurethane are not enough to meet the increasing market demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A modified polyurethane thermal insulation composite board proposed by the present invention includes a gypsum board layer, a thermal insulation board layer and a cement board layer arranged in sequence from the inside to the outside;

[0018] Among them, the raw materials of the insulation board layer include by weight: 100 parts of modified polyurethane, 45 parts of acrylate, 12.5 parts of diisocyanate, 20 parts of alkyd resin, 10 parts of dipropylene glycol butyl ether, 5 parts of silicone resin, 4.5 parts of melamine formaldehyde resin 6.5 parts of chlorinated paraffin, 3 parts of diisocyanate, 3 parts of nitrocellulose, 3 parts of glass fiber, 5 parts of nano calcium carbonate, 5 parts of perlite, 3 parts of fly ash, 6.5 parts of magnesium oxide, 5 parts of n-octanol , 6.5 parts of dodecyl alcohol, 4 parts of cetyl alcohol, 3 parts of polymer diol, 5 parts of fluorine-containing polyether diol, 6.5 parts of compatibilizer, 3 parts of emulsifier, 4.5 parts of foaming...

Embodiment 2

[0021] A modified polyurethane thermal insulation composite board proposed by the present invention includes a gypsum board layer, a thermal insulation board layer and a cement board layer arranged in sequence from the inside to the outside;

[0022] The raw materials of the insulation board layer include by weight: 80 parts of modified polyurethane, 60 parts of acrylate, 9 parts of diisocyanate, 30 parts of alkyd resin, 5 parts of dipropylene glycol butyl ether, 8 parts of silicone resin, and 3 parts of melamine formaldehyde resin. 9 parts of chlorinated paraffin, 1 part of diisocyanate, 4 parts of nitrocellulose, 1 part of glass fiber, 8 parts of nano calcium carbonate, 2 parts of perlite, 5 parts of fly ash, 4 parts of magnesium oxide, 7 parts of n-octanol , 4 parts of lauryl alcohol, 6 parts of cetyl alcohol, 1 part of polymer diol, 7 parts of fluorine-containing polyether diol, 4 parts of compatibilizer, 4 parts of emulsifier, 3 parts of foaming agent, silane diol 8 parts...

Embodiment 3

[0025] A modified polyurethane thermal insulation composite board proposed by the present invention includes a gypsum board layer, a thermal insulation board layer and a cement board layer arranged in sequence from the inside to the outside;

[0026] The raw materials of the insulation board layer include by weight: 120 parts of modified polyurethane, 30 parts of acrylate, 16 parts of diisocyanate, 10 parts of alkyd resin, 15 parts of dipropylene glycol butyl ether, 2 parts of silicone resin, 6 parts of melamine formaldehyde resin 4 parts of chlorinated paraffin, 5 parts of diisocyanate, 2 parts of nitrocellulose, 5 parts of glass fiber, 2 parts of nano calcium carbonate, 8 parts of perlite, 1 part of fly ash, 9 parts of magnesium oxide, 3 parts of n-octanol , 9 parts of dodecyl alcohol, 2 parts of cetyl alcohol, 5 parts of polymer diol, 3 parts of fluorine-containing polyether diol, 9 parts of compatibilizer, 2 parts of emulsifier, 6 parts of foaming agent, silane diol 4 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a modified polyurethane thermal-insulation composite board. The composite board sequentially comprises a gypsum board layer, a thermal-insulation board layer and a cement board layer from inside to outside, wherein the thermal-insulation board layer is prepared from modified polyurethane, acrylate, diisocyanate, an alkyd resin, dipropylene glycol monobutyl ether, an organic silicon resin, a melamine formaldehyde resin, chlorinated paraffin, diisocyanate, nitrocellulose, glass fibers, nano calcium carbonate, perlite, fly ash, magnesium oxide, n-octanol, lauryl alcohol, hexadecanol, polymer dibasic alcohol, fluorine-containing polyether dibasic alcohol, a compatilizer, an emulsifier, a foaming agent, a silane coupling agent, a curing agent and silicone oil. The modified polyurethane thermal-insulation composite board has excellent thermal insulation property and excellent heat resistance.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a modified polyurethane thermal insulation composite board. Background technique [0002] Building energy consumption has always been the focus of our country's attention. Energy conservation and emission reduction has become a basic national policy that our country pays attention to. As a country with large energy consumption, since the late 1980s, my country has gradually implemented energy conservation measures of 30%, 50% and 65%. Three energy-saving work steps, and began to carry out beneficial attempts to implement higher energy-saving indicators in cities with conditions. With the gradual implementation of the goal of 65% energy saving in domestic buildings, polyurethane has great potential. [0003] However, the polyurethane composite panels currently on the market are generally bonded with polyurethane using an interface agent and mortar. The weather resistance of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/08C08L67/08C08L83/04C08K13/04C08K7/14C08K3/26C08K3/22C08K5/05C08G18/48C08G18/54C08G18/32C08G18/66
CPCC08L75/08C08G18/4027C08G18/4833C08G18/542C08G18/6692C08K2201/011C08L2201/08C08L2205/035
Inventor 夏正忠
Owner ANHUI GUANGYAN NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap