Ceramic material
A technology for ceramic materials and raw materials, applied in the field of ceramic material preparation, can solve the problems of high price and lack of ceramic raw materials, and achieve the effects of good impact resistance, energy saving and other good performances.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0037] The preparation method of described ceramic material comprises the following steps:
[0038] S1: Put dry sludge, crop straw, limestone, dolomite, diatomaceous earth, iron oxide, silicon dioxide, zirconia, aluminum fragments, and glass fiber into the pulverizer at a speed of 400-800r / min Grinding for 2-3 hours to obtain a composite powder;
[0039] S2: put the composite powder prepared in step S1 into a ball mill, perform ball milling treatment at a speed of 500-600r / min for 1-2h, and pass through a 200-300 mesh sieve to obtain a powder;
[0040] S3: Stir the powder prepared in step S2, water reducer, foaming agent, foam regulator, catalyst, crosslinking agent, foam stabilizer, hydrogen peroxide, and water at a temperature of 100-120r / min for 4 -5h, make the slurry;
[0041] S4: vacuumize the slurry prepared in step S3 for 15-20 min at a vacuum degree of 0.85-0.95 to obtain a blank;
[0042] S5: Microwave treatment the blank obtained in step S4 at 60-70° C. for 10-20 ...
Embodiment 1
[0045] A ceramic material, in parts by weight, comprising the following raw materials: 64 parts of dry sludge, 40 parts of crop straw, 17 parts of limestone, 16 parts of dolomite, 14 parts of diatomite, 10 parts of iron oxide, 8 parts of silicon dioxide 8 parts, 8 parts of zirconium dioxide, 5 parts of aluminum fragments, 3 parts of glass fiber, 3 parts of water reducer, 0.9 parts of foaming agent, 0.8 parts of foam regulator, 0.5 parts of catalyst, 0.5 parts of crosslinking agent, foam stabilizer 0.3 parts of agent, 35 parts of hydrogen peroxide, and 420 parts of water.
[0046] The water content of the dried sludge is 10%.
[0047] The grain size of the crop straw powder is ≤300 μm, the moisture content is ≤14%, and the crop is corn.
[0048] The water reducer is a polycarboxylate water reducer.
[0049] The blowing agent is azodicarbonamide.
[0050] The foam regulator is an acrylate foam regulator.
[0051] The catalyst is stannous octoate.
[0052] The crosslinking a...
Embodiment 2
[0061] A ceramic material, in parts by weight, comprising the following raw materials: 42 parts of dry sludge, 32 parts of crop straw, 10 parts of limestone, 10 parts of dolomite, 10 parts of diatomite, 8 parts of iron oxide, 6 parts of silicon dioxide 6 parts, 6 parts of zirconium dioxide, 4 parts of aluminum fragments, 2 parts of glass fiber, 2 parts of water reducer, 0.6 parts of foaming agent, 0.4 parts of foam regulator, 0.4 parts of catalyst, 0.4 parts of crosslinking agent, foam stabilizer 0.2 parts of agent, 30 parts of hydrogen peroxide, and 350 parts of water.
[0062] The water content of the dried sludge was 7%.
[0063] The particle size of the crop straw powder is ≤300 μm, the moisture content is ≤14%, and the crop is rice.
[0064] The water reducer is a polycarboxylate water reducer.
[0065] The blowing agent is azodicarbonamide.
[0066] The foam regulator is an acrylate foam regulator.
[0067] The catalyst is triethylenediamine·hexahydrate.
[0068] Th...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
breakdown field strength | aaaaa | aaaaa |
water content | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com