Acid-alkali-resisting garment fabric

A technology of acid and alkali resistance and fabrics, applied in the field of fabrics, can solve the problems of easy deformation and wrinkle, etc., and achieve the effect of improving product performance and superior flame retardancy

Inactive Publication Date: 2017-01-04
李红玉
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, natural fabrics such as pure cotton, pure wool, pure silk, and pure hemp have been reduced to general fabrics because of their shortcomings such as easy to wrinkle and deform, and are rarely used as high-end clothing materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acid-alkali-resisting garment fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The acid and alkali-resistant clothing fabric in this embodiment is bonded with a protective coating on the linen fabric, and the coating is composed of the following components in parts by mass: 20 parts of brominated butyl rubber, 18 parts of chlorohydrin rubber, 18 parts of chemical polyethylene, 16 parts of tallow dihydroxyethyl amine oxide, 18 parts of argan oil, 18 parts of terpineol, 16 parts of ethyl propionate, 18 parts of carbo resin, 18 parts of garlic extract, propiconazole 16 parts, 16 parts of sodium monofluorophosphate, 16 parts of dodecyl ethoxy sulfobetaine, 18 parts of sodium dichromate, 16 parts of sodium silicate powder, 14 parts of anhydrous gypsum, 18 parts of calcium acetate, coke 16 parts of sodium phosphate, 14 parts of zinc chromate, 16 parts of menthol, 14 parts of sodium molybdate, 14 parts of sodium antimonate powder, 16 parts of triethylene glycol diisocaprylate, 16 parts of aluminum stearate, hydroxytin Zinc acid 16 parts, dibutyl sebacate...

Embodiment 2

[0022] The acid and alkali-resistant clothing fabric in this embodiment is bonded with a protective coating on the linen fabric, and the coating is composed of the following components in parts by mass: 22 parts of brominated butyl rubber, 20 parts of chlorohydrin rubber, 20 parts of chemical polyethylene, 18 parts of tallow dihydroxyethyl amine oxide, 20 parts of argan oil, 20 parts of terpineol, 18 parts of ethyl propionate, 20 parts of carbo resin, 20 parts of garlic extract, propiconazole 18 parts, 18 parts of sodium monofluorophosphate, 18 parts of dodecyl ethoxy sulfobetaine, 20 parts of sodium dichromate, 18 parts of sodium silicate powder, 16 parts of anhydrous gypsum, 20 parts of calcium acetate, coke 18 parts of sodium phosphate, 16 parts of zinc chromate, 18 parts of menthol, 16 parts of sodium molybdate, 16 parts of sodium antimonate powder, 18 parts of triethylene glycol diisocaprylate, 18 parts of aluminum stearate, hydroxytin Zinc acid 18 parts, dibutyl sebacate...

Embodiment 3

[0028] The acid and alkali-resistant clothing fabric in this embodiment is bonded with a protective coating on the linen fabric, and the coating is composed of the following components in parts by mass: 24 parts of brominated butyl rubber, 22 parts of chlorohydrin rubber, 22 parts of chemical polyethylene, 20 parts of tallow dihydroxyethyl amine oxide, 22 parts of argan oil, 22 parts of terpineol, 20 parts of ethyl propionate, 22 parts of carbo resin, 22 parts of garlic extract, propiconazole 20 parts, 20 parts of sodium monofluorophosphate, 20 parts of dodecyl ethoxy sulfobetaine, 22 parts of sodium dichromate, 20 parts of sodium silicate powder, 18 parts of anhydrous gypsum, 22 parts of calcium acetate, coke 20 parts of sodium phosphate, 18 parts of zinc chromate, 20 parts of menthol, 18 parts of sodium molybdate, 18 parts of sodium antimonate powder, 20 parts of triethylene glycol diisocaprylate, 20 parts of aluminum stearate, hydroxytin Zinc acid 20 parts, dibutyl sebacate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an acid-alkali-resisting garment fabric. A protective coating is stuck on a linen fabric; the coating is prepared from the following components: brominated butyl rubber, chlorohydrine rubber, chlorinated polyethylene, tallow dihydroxyethyl amine oxide, nut oil, terpilenol, ethyl propionate, carbomer resin, garlic extract, propiconazole, sodium monofluorophosphate, dodecyl ethoxyl sulfobetaine, sodium dichromate, sodium silicate powder, anhydrous gypsum, calcium acetate, sodium pyrophosphate, zinc chromate, menthol crystal, sodium molybdate, sodium antimonate powder, tri(ethylene glycol) bis(2-ethylhexanoate), aluminum stearate, zinc hydroxystannate, dibutyl sebacate, diisooctyl ortho-phthalate, wool grease, sodium dodecylbenzene sulfonate, divinylbenzene and sodium carboxymethyl cellulose. The product provided by the invention has relatively excellent flame-retarding, acid-alkali-resisting, mildew-preventing and antibacterial performance, and the performance of the product is improved.

Description

technical field [0001] The invention relates to an acid and alkali resistant clothing fabric, which belongs to the technical field of fabrics. Background technique [0002] Clothing is made of fabric, and fabric is the material used to make clothing. As one of the three elements of clothing, fabrics can not only interpret the style and characteristics of clothing, but also directly affect the color and shape of clothing. Showing its own noble perfection, soft to the touch. In the big world of clothing, the fabrics of clothing are varied and changing with each passing day. But generally speaking, high-quality and high-end fabrics mostly have the characteristics of comfortable wearing, sweat-absorbing and breathable, crisp drape, noble vision, and soft touch. Modern clothing worn on formal social occasions mostly uses high-quality blended fabrics. However, natural fabrics such as pure cotton, pure wool, pure silk, and pure hemp have been reduced to general fabrics due to t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/06C09D5/18C09D5/14C09D5/08C09D7/12D06N3/00D06N3/04
CPCC09D4/06C09D5/08C09D5/14C09D5/18C09D7/61C09D7/63C09D7/65D06N3/0002D06N3/04D06N2201/045
Inventor 不公告发明人
Owner 李红玉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com