Epoxy paint for automobile leaf springs and preparation method thereof

A technology for automotive steel sheets and coatings, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of affecting the quality of automotive leaf spring coatings, poor anti-rust performance, and insufficient protection of automotive steel sheet springs, etc., to achieve improved wet adhesion, Improvement of cross-linking degree and compactness, cost reduction effect

Inactive Publication Date: 2017-03-29
TONGLING SIDE TECH
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the coating is too thin, the general coating has poor antirust performance and is not enough to protect the automobile leaf spring, which requires the new coating to have the highest possible antirust performance under the condition of a thinner coating
At present, the coatings of automobile leaf springs at home and abroad are relatively thick, and there are mo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] A kind of epoxy automobile leaf spring paint, it is made up of the raw material of following weight part:

[0025] Fatty acid polyethylene glycol ester 0.7, triethanolamine 0.4, sodium pyrophosphate 0.8, zinc ricinoleate 1, hydroxyethyl methacrylate 7, phosphorus pentoxide 0.8, p-methoxyphenol 2, tetrabutylammonium bromide 0.6, acrylic acid 17, methyl methacrylate 6, epoxy resin E-51 143, ammonium persulfate 0.07, sodium bicarbonate 2, sodium dodecylbenzenesulfonate 0.6, N, N diethylaniline 0.1, 2 Mercaptobenzimidazole 1, barium stearate 2, methyl nylonate 4, bentonite 6.

[0026] A kind of preparation method of described automobile leaf spring paint, comprises the following steps:

[0027] (1) Add the above-mentioned 2-mercaptobenzimidazole into absolute ethanol which is 7 times its weight, stir evenly, raise the temperature to 80°C, add the above-mentioned barium stearate, keep stirring for 15 minutes, add the above-mentioned methyl Hydroxyethyl acrylate, stirred to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Impact resistanceaaaaaaaaaa
Acid resistanceaaaaaaaaaa
Login to view more

Abstract

The invention discloses epoxy paint for automobile leaf springs. The paint comprises the following raw materials in parts by weight: 0.7-1 part of fatty acid polyethylene glycol ester, 0.4-1 part of triethanolamine, 0.8-1 part of sodium pyrophosphate, 1-2 parts of zinc ricinate, 7-9 parts of 2-hydroxyethyl methacrylate, 0.8-1 part of phosphoric pentoxide, 2-3 parts of 4-methoxyphenol, 0.6-2 parts of tetrabutylammonium bromide, 17-20 parts of acrylic acid, 6-8 parts of methyl methacrylate, 140-150 parts of epoxy resin E-5, 0.07-0.1 part of ammonium persulfate, 2-3 parts of sodium bicarbonate, 0.6-1 part of sodium dodecyl benzene sulfonate, 0.1-0.13 part of N,N-diethylaniline, 1-2 parts of 2-mercapto benzimidazole, 2-3 parts of barium stearate, 4-5 parts of dimethyl nylon acid, and 6-7 parts of bentonite. The paint has low cost, and solves the problems of large 'falling amount' of the automobile leaf springs in the prior art without environmental protection, and bad antirust capability.

Description

technical field [0001] The invention relates to the technical field of anticorrosion coatings, in particular to an epoxy automobile leaf spring coating and a preparation method thereof. Background technique [0002] Acrylic monomers are often used in the polymerization process of water-based acrylic resins. Due to the presence of hydrophilic carboxyl groups on acrylic acid, the stability of polymer emulsions is enhanced. Under dry film conditions, carboxyl groups can closely adhere to the substrate Together, the adhesion between the coatings is greatly improved; but in a humid environment, because the carboxyl group on the acrylic acid is hydrophilic, the association with water is very strong, and the water molecules are easily absorbed into the coating and the metal through the capillary. In the interface, the force between the carboxyl group and the surface of the metal substrate is greatly reduced, the adhesion in the wet state is poor, and the water resistance is reduced...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D151/08C09D5/08C09D7/12C08F290/00C08F230/02
CPCC08F290/00C08L2207/53C09D5/08C09D7/61C09D7/63C09D7/65C09D151/08C08F230/02C08L71/02C08K13/02C08K5/098C08K3/346
Inventor 孔华英
Owner TONGLING SIDE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka