Production method of titanium implant surface composite coating used for stomatology department

A titanium implant and surface composite technology, which is applied in the field of preparation of composite coatings on the surface of titanium implants used in stomatology, can solve the problems of implant bioactivity, corrosion resistance and wear resistance, and achieve favorable osseointegration , Improve corrosion resistance, improve biocompatibility

Inactive Publication Date: 2017-04-26
WUHU SUNYANG INFORMATION CONSULTATION
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it also uses a single TiO2 film layer to achieve its stated function, and the biological activity, corrosion resistance and wear resistance of the implant are insufficient.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) Take a piece of commercial pure titanium plate, wire-cut it into 8×8×4 size, grind it step by step with sandpaper, put it in acetone, absolute ethanol and ultrapure water beaker for 8 minutes, take it out and put it in Dry in an electric blast drying oven at 56°C for 1.3h;

[0034] (2) Dissolve 0.2CA+0.02β-GP in deionized water to form an electrolyte, adjust the pH value of the electrolyte to 10, use the titanium specimen as the anode, and the stainless steel electrolytic cell as the cathode, and use pulse-direct current voltage to test the titanium The parts are subjected to micro-arc oxidation treatment, and the treatment time is 6 minutes;

[0035] (3) Clean the specimen pretreated by micro-arc oxidation with deionized water and absolute ethanol, and then place it in an electric blast drying oven at 56 ° C for 13 minutes. After drying, use plasma spraying method to coat the surface of the specimen from the inside Spray a small amount of silicon dioxide and silve...

Embodiment 2

[0049] (1) Take a piece of commercial pure titanium plate, cut it into 8×8×4 size by wire cutting, grind it step by step with sandpaper, put it in acetone, absolute ethanol and ultrapure water beaker for 9 minutes and ultrasonically clean it for 9 minutes, take it out and put it in Dry in an electric blast drying oven at 55°C for 1.5h;

[0050] (2) Dissolve 0.2CA+0.02β-GP in deionized water to form an electrolyte, adjust the pH value of the electrolyte to 10, use the titanium specimen as the anode, and the stainless steel electrolytic cell as the cathode, and use pulse-direct current voltage to test the titanium The parts are subjected to micro-arc oxidation treatment, and the treatment time is 8 minutes;

[0051] (3) Clean the specimen pretreated by micro-arc oxidation with deionized water and absolute ethanol, and then place it in an electric blast drying oven at 55°C for 15 minutes. After drying, use plasma spraying method on the surface of the specimen from the inside Spr...

Embodiment 3

[0065] (1) Take a piece of commercial pure titanium plate, cut it into 8×8×4 size by wire cutting, grind it step by step with sandpaper, put it in acetone, absolute ethanol and ultrapure water beaker for 10 minutes and ultrasonically clean it for 10 minutes, take it out and put it in Dry in an electric blast drying oven at 58°C for 1.2h;

[0066] (2) Dissolve 0.2CA+0.02β-GP in deionized water to form an electrolyte, adjust the pH value of the electrolyte to 11, use the titanium specimen as the anode, and the stainless steel electrolytic cell as the cathode, and use pulse-direct current voltage to test the titanium The parts are subjected to micro-arc oxidation treatment, and the treatment time is 8 minutes;

[0067] (3) Clean the specimen pretreated by micro-arc oxidation with deionized water and absolute ethanol, and then dry it in an electric blast drying oven at 60°C for 10 minutes. After drying, use plasma spraying method on the surface of the specimen from inside Spray a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method of a titanium implant surface composite coating used for the stomatology department, and relates to the field of biomedical materials. The method comprises preprocessing of a titanium plate, micro arc oxidation treatment, preparation of a sol solution, and production of the composite coating. A film is produced on the surface of pure titanium by adopting butyl titanate as a precursor and diethanolamine as a complexing agent and adding polyethylene glycol used as a template through a sol-gel technology, so the bioactivity of the titanium material is improved, and the corrosion resistance is enhanced.

Description

technical field [0001] The invention relates to the field of biomedical materials, in particular to a method for preparing a composite coating on the surface of a titanium implant used in stomatology. Background technique [0002] Titanium and titanium alloys have been widely used in the fields of plastic surgery and implantology, and are currently the preferred materials for dental implant restoration. However, pure titanium has low hardness, poor anti-friction performance, and low biological activity on the surface. If it is directly implanted into the human body, there are problems such as long osseointegration time, low bonding strength, and potential impact of free metal ions on human tissues. Therefore, how to obtain specific physical morphology, chemical composition and biochemical modification on the surface of titanium metal through surface modification, so as to form a biological combination with bone tissue, shorten the implantation cycle, obtain early osseointeg...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/06A61L27/30A61L27/32A61L27/34C23C28/04C25D11/02C25D11/26
CPCA61L27/06A61L27/306A61L27/32A61L27/34C23C28/042C25D11/026C25D11/26A61L2430/12A61L2420/08A61L2420/06A61L2420/04A61L2300/104A61L2300/404A61L2400/18C08L71/02
Inventor 许治政赵文娟刘艳
Owner WUHU SUNYANG INFORMATION CONSULTATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com