Environment-friendly textile auxiliary and preparation method thereof

A kind of textile auxiliaries, environment-friendly technology, applied in the field of environment-friendly textile auxiliaries and its preparation, can solve the problem of dependence on imports of special and high-end textile auxiliaries, and achieve the effect of cheap raw materials, strong toughness, and good application prospects

Inactive Publication Date: 2017-05-10
WUJIANG BEISHE SHENGYUAN TEXTILE PROD AUXILIARIES PLANT
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is still a large gap between domestic textile auxiliaries and the international advanced level in terms of variety and quality, synthesis and application technology, and special and high-grade textile auxiliaries still have to rely on imports

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) Accurately weigh 35 parts of dioctyl sodium sulfosuccinate, 30 parts of disodium edetate, 28 parts of polymethyl silicone resin, 22 parts of styrene maleic anhydride resin, and 12 parts of phthalic anhydride, 10 parts of polyethylene glycol monostearate, 8 parts of fatty alcohol polyoxyethylene ether, 6 parts of coconut oil diethanolamide, 4 parts of nonylphenol polyoxyethylene ether, 4 parts of lignin sulfate 2 parts of activated carbon, 1 part of barium chloride, 3 parts of palmitic acid, 3 parts of methylenebisacrylamide, 100 parts of deionized water;

[0023] (2) Add coconut oil diethanolamide, nonylphenol polyoxyethylene ether, lignin sulfate, activated carbon, and barium chloride into the ball mill, mill for 1 hour, then add deionized water to the milled mixture, and stir at 1000rpm Stir for 2 hours at a high speed to obtain a preliminary mixed solution;

[0024] (3) Send the preliminary mixed solution into the reaction kettle, add polymethyl silicone resin, ...

Embodiment 2

[0028] (1) Accurately weigh 40 parts of dioctyl sodium sulfosuccinate, 33 parts of disodium edetate, 30 parts of polymethyl silicone resin, 24 parts of styrene maleic anhydride resin, and 14 parts of phthalic anhydride, 12 parts of polyethylene glycol monostearate, 9 parts of fatty alcohol polyoxyethylene ether, 7 parts of coconut oil diethanolamide, 5 parts of nonylphenol polyoxyethylene ether, 5 parts of lignin sulfate 3 parts of activated carbon, 2 parts of barium chloride, 4 parts of citric acid, 4 parts of polyethylene glycol dimethacrylate, 100 parts of deionized water;

[0029] (2) Add coconut oil diethanolamide, nonylphenol polyoxyethylene ether, lignin sulfate, activated carbon, and barium chloride into the ball mill, mill for 1.5 hours, and then add deionized water to the milled mixture, at 1500 rpm Stir at a stirring rate for 2.5 hours to obtain a preliminary mixed solution;

[0030] (3) Send the preliminary mixed liquid into the reaction kettle, add polymethyl sil...

Embodiment 3

[0034] (1) Accurately weigh 45 parts of dioctyl sodium sulfosuccinate, 36 parts of disodium edetate, 32 parts of polymethyl silicone resin, 26 parts of styrene maleic anhydride resin, and 16 parts of phthalic anhydride, 14 parts of polyethylene glycol monostearate, 10 parts of fatty alcohol polyoxyethylene ether, 8 parts of coconut oil diethanolamide, 6 parts of nonylphenol polyoxyethylene ether, 6 parts of lignin sulfate 4 parts of activated carbon, 3 parts of barium chloride, 5 parts of linoleic acid, 5 parts of ethylene glycol diglycidyl ether, 100 parts of deionized water;

[0035] (2) Add coconut oil diethanolamide, nonylphenol polyoxyethylene ether, lignin sulfate, activated carbon, and barium chloride into the ball mill, mill for 2 hours, and then add deionized water to the milled mixture, at 2000 rpm Stir for 3 hours at a stirring rate to obtain a preliminary mixed solution;

[0036] (3) Send the preliminary mixed liquid into the reaction kettle, add polymethyl silico...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly textile auxiliary and a preparation method thereof. The environment-friendly textile auxiliary is prepared with sodium diethylhexyl sulfosuccinate, ethylene diamine tetraacetic acid, methyl silicone resin and styrene maleic anhydride resin as main components, phthalic anhydride, polyethylene glycol monostearate, fatty alcohol-polyoxyethylene ether, cocomut oil diethanolamide, nonylphenol polyoxyethylene ether, lignin sulfate, activated carbon, barium chloride, organic acid, a cross-linking agent and deionzied water are added, and the technologies of ball milling, stirring, emulsifying, pH adjusting, heating, heat preservation, ultrasonic oscillation, high-speed shearing and the like are also used. Therefore, after the prepared textile auxiliary is used, textile fabrics are high in toughness and good in viscosity stability, and the textile auxiliary is environmentally friendly, free of toxins, capable of meeting industrial requirements and good in application prospect.

Description

technical field [0001] The invention relates to the technical field of textile auxiliaries, in particular to an environment-friendly textile auxiliaries and a preparation method thereof. Background technique [0002] Textile auxiliaries are necessary chemicals in the process of textile production and processing. Textile auxiliaries play an indispensable role in improving the product quality and added value of textiles. It can not only endow textiles with various special functions and styles, such as softness, wrinkle resistance, shrink resistance, waterproof, antibacterial, antistatic, flame retardant Etc., can also improve the dyeing and finishing process, play a role in saving energy and reducing processing costs. Textile auxiliaries are crucial to improving the overall level of the textile industry and their role in the textile industry chain. There are nearly 100 categories of textile auxiliaries in the world, producing nearly 16,000 varieties, with an annual output of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M13/256D06M13/342D06M15/643D06M15/233D06M15/53D06M15/01D06M11/74D06M13/419D06M11/155D06M13/188D06M13/207D06M13/203
CPCD06M13/256D06M11/155D06M11/74D06M13/188D06M13/203D06M13/207D06M13/342D06M13/419D06M15/01D06M15/233D06M15/53D06M15/643
Inventor 钱华
Owner WUJIANG BEISHE SHENGYUAN TEXTILE PROD AUXILIARIES PLANT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com