Medical hydroxybutyl chitosan sponge and preparation method thereof
A technology of hydroxybutyl chitosan and chitosan, applied in the fields of medicine and health, can solve the problems of easy to cause immunogenic reaction, weak tissue adhesion, easy to detach from the wound surface, etc., achieve good hemostasis, avoid toxic and side effects, The effect of promoting tissue healing
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0029] Example 1
[0030] Step 1: Purification of Chitosan Products
[0031] Weigh a certain amount of chitosan crude product, dissolve it in 1% hydrochloric acid at a ratio of 1g:50mL, filter to remove insoluble matter, dropwise add 1mol / L sodium hydroxide solution to a slightly alkaline solution to obtain a precipitate, wash with purified water to neutrality, desalted and dehydrated with ethanol solution, and dried to obtain purified chitosan.
[0032] Step 2: Preparation of hydroxybutyl chitosan
[0033] The purified chitosan powder was dispersed in a 50% aqueous solution of sodium hydroxide or potassium hydroxide at a ratio of 1 g:10 mL for alkalization treatment, and heated for 24 hours under nitrogen protection at a temperature of 50°C. The excess lye solution was filtered off, the remaining solid was dispersed in isopropanol aqueous solution at the ratio of 1g:20mL, then a certain volume of 1,2-butylene oxide was added, reacted for 1 hour, and heated at 70°C for 18 ho...
Example Embodiment
[0043] Example 2
[0044] Step 1: Purification of Chitosan Products
[0045] Same as step 1 in Example 1.
[0046] Step 2: Preparation of hydroxybutyl chitosan
[0047] The purified chitosan powder was dispersed in a 50% sodium hydroxide or potassium hydroxide aqueous solution at a ratio of 1 g:10 mL for alkalization treatment, and heated for 24 hours under nitrogen protection at a temperature of 40°C. The excess lye solution was filtered off, the remaining solid was dispersed in isopropanol aqueous solution at the ratio of 1 g:20 mL, and then a certain volume of 1,2-butylene oxide was added, reacted for 1 hour, and heated at 60°C for 24 hours. After cooling, adjust the pH value to neutral, filter out insoluble matter, add ethanol, centrifuge, and dry to obtain a hydroxybutyl chitosan product.
[0048] Step 3: Preparation of hydroxybutyl chitosan solution
[0049] Under clean environment conditions, prepare hydroxybutyl chitosan solution, weigh the above items according to...
Example Embodiment
[0057] Example 3
[0058] Step 1: Purification of Chitosan Products
[0059] Same as step 1 in Example 1.
[0060] Step 2: Preparation of hydroxybutyl chitosan
[0061] The purified chitosan powder was dispersed in a 50% aqueous solution of sodium hydroxide or potassium hydroxide at a ratio of 1 g:10 mL for alkalization treatment, and heated for 24 hours under nitrogen protection at a temperature of 50°C. The excess lye solution was filtered off, the remaining solid was dispersed in isopropanol aqueous solution at the ratio of 1 g:20 mL, and then a certain volume of 1,2-butylene oxide was added, reacted for 1 hour, and heated at 55°C for 24 hours. After cooling, adjust the pH value to neutral, filter out insoluble matter, add ethanol, centrifuge, and dry to obtain a hydroxybutyl chitosan product.
[0062] Step 3: Preparation of hydroxybutyl chitosan solution
[0063] Under clean environment conditions, prepare hydroxybutyl chitosan solution, weigh the above items according...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap