Anti-oxidization and high-intensity 3D printing material for building engineering and preparation method of printing material

A technology for 3D printing and construction engineering, applied in the field of 3D printing materials, can solve the problems of oxidation resistance and strength that cannot meet the needs of existing technologies, and that the performance of polyphenylene sulfide cannot be satisfied.

Inactive Publication Date: 2017-09-08
HEFEI SKE INTELLIGENT TECH
View PDF1 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polyphenylene sulfide is a special engineering plastic with excellent heat resistance, chemical corrosion resistance, electrical properties, flame retardancy and adhesive properties, etc. It is widely used in textiles, automobiles, household appliances, electronic appliances, mechanical instruments, petroleum In the fields of chemical industry, national defense and military industry, aerosp

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-oxidization and high-intensity 3D printing material for building engineering and preparation method of printing material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An oxidation-resistant high-strength 3D printing material for construction projects proposed by the present invention, its raw materials include: 100 parts of modified polyphenylene sulfide, 30 parts of polyphenylene sulfone, 10 parts of polycarbonate, 6.5 parts of polyvinyl chloride resin 4.5 parts of diisocyanate, 10 parts of trimethyl phosphate, 30 parts of chlorinated polyethylene, 6 parts of polytetrafluoroethylene micropowder, 8 parts of hydroxypropyl methylcellulose, 4 parts of nano-titanium dioxide, 3.5 parts of zinc borate, three 3.5 parts of antimony oxide, 6 parts of organic montmorillonite, 3 parts of glass fiber, 6 parts of nano zinc oxide, 20 parts of basalt plain weave fiber cloth, 6.5 parts of nano silicon dioxide, 3.5 parts of ethyl orthosilicate, silane coupling agent 4.5 parts of KH-570, 7.5 parts of glycerin, 2 parts of defoamer, 7.5 parts of anti-oxidation modifier, and 12 parts of modified filler.

Embodiment 2

[0019]The invention proposes an oxidation-resistant high-strength 3D printing material for construction engineering. The raw materials include: 80 parts of modified polyphenylene sulfide, 40 parts of polyphenylene sulfone, 5 parts of polycarbonate, and 9 parts of polyvinyl chloride resin. Parts, 3 parts of diisocyanate, 15 parts of trimethyl phosphate, 20 parts of chlorinated polyethylene, 9 parts of polytetrafluoroethylene micropowder, 4 parts of hydroxypropyl methylcellulose, 6 parts of nano-titanium dioxide, 2 parts of zinc borate, three 5 parts of antimony oxide, 3 parts of organic montmorillonite, 5 parts of glass fiber, 3 parts of nano zinc oxide, 30 parts of basalt plain weave fiber cloth, 4 parts of nano silicon dioxide, 5 parts of ethyl orthosilicate, silane coupling agent 3 parts of KH-570, 10 parts of glycerin, 1 part of defoamer, 9 parts of anti-oxidation modifier, and 8 parts of modified filler.

[0020] The modified polyphenylene sulfide is prepared according to ...

Embodiment 3

[0024] An oxidation-resistant high-strength 3D printing material for construction projects proposed by the present invention, its raw materials include: 120 parts of modified polyphenylene sulfide, 20 parts of polyphenylsulfone, 15 parts of polycarbonate, 4 parts of polyvinyl chloride resin 6 parts, 6 parts of diisocyanate, 5 parts of trimethyl phosphate, 40 parts of chlorinated polyethylene, 3 parts of polytetrafluoroethylene micropowder, 12 parts of hydroxypropyl methylcellulose, 2 parts of nano-titanium dioxide, 5 parts of zinc borate, three 2 parts of antimony oxide, 9 parts of organic montmorillonite, 1 part of glass fiber, 9 parts of nano zinc oxide, 10 parts of basalt plain weave fiber cloth, 9 parts of nano silicon dioxide, 2 parts of ethyl orthosilicate, silane coupling agent 6 parts of KH-570, 5 parts of glycerin, 3 parts of defoamer, 6 parts of anti-oxidation modifier, and 16 parts of modified filler.

[0025] A method for preparing an oxidation-resistant high-stren...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-oxidization and high-intensity 3D printing material for building engineering. The anti-oxidization and high-intensity 3D printing material is prepared from the following raw materials: modified polyphenylene sulfide, polyethylene sulfone, polycarbonate, polyvinyl chloride resin, diisocyanate, trimethyl phosphate, chlorinated polyethylene, polytetrafluoroethylene fine powder, hydroxypropyl methyl cellulose, nano titanium dioxide, zinc borate, antimonous oxide, organic bentonite, glass fiber, nano-zinc oxide, basalt plain fiber cloth, nanosilicon dioxide, tetraethoxysilane, a silane coupling agent KH-570, glycerinum, a defoaming agent, an anti-oxidization modifier and a modifier filler. The invention further provides a preparation method of the anti-oxidization and high-intensity 3D printing material for building engineering. The prepared 3D printing material is excellent in oxidization resistance and intensity.

Description

technical field [0001] The invention relates to the technical field of 3D printing materials, in particular to an oxidation-resistant high-strength 3D printing material for construction engineering and a preparation method thereof. Background technique [0002] Polyphenylene sulfide is a special engineering plastic with excellent heat resistance, chemical corrosion resistance, electrical properties, flame retardancy and adhesive properties, etc. It is widely used in textiles, automobiles, household appliances, electronic appliances, mechanical instruments, petroleum In the fields of chemical industry, national defense and military industry, aerospace and other fields, as a kind of 3D printing material, the performance of pure polyphenylene sulfide cannot meet the needs of actual use, and its oxidation resistance and strength cannot meet the needs of existing technologies, so there is an urgent need Design an oxidation-resistant high-strength 3D printing material for architec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L81/02C08L81/06C08L69/00C08L27/06C08L23/28C08L27/18C08L1/28C08K13/06C08K9/08C08K7/14C08K3/34C08K3/22C08K3/38C08K5/5425B33Y70/00
CPCB33Y70/00C08K2003/2241C08K2003/387C08K2201/011C08K2201/014C08L81/02C08L2201/08C08L2205/02C08L2205/035C08L81/06C08L69/00C08L27/06C08L23/286C08L27/18C08L1/284C08K13/06C08K9/08C08K7/14C08K3/346C08K3/22C08K3/38C08K3/2279C08K5/5425
Inventor 吕月林
Owner HEFEI SKE INTELLIGENT TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap