Functional magnetic oxidized graphene catalyst material of hydramine-containing compound and its preparation method and application

A graphene catalytic material and compound technology, applied in metal/metal oxide/metal hydroxide catalysts, chemical instruments and methods, physical/chemical process catalysts, etc. The problems of low degree of material bonding, complex preparation process and easy falling off can achieve the effect of reducing loss consumption, high catalytic activity and avoiding falling off.

Active Publication Date: 2017-10-17
杭州蓝锋尚能源科技有限公司
View PDF9 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the preparation process of the existing graphene oxide ferroferric oxide composite materials is mostly complicated, and the degree of bonding between the prepared ferric oxide particles and the graphene oxide composite material is not high, and the ferric oxide particles in the loading structure are large. The part is still in a bare state, on the one hand, it is easy to fall off, and on the other hand, it is easy to be consumed by the Fenton reaction process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Functional magnetic oxidized graphene catalyst material of hydramine-containing compound and its preparation method and application
  • Functional magnetic oxidized graphene catalyst material of hydramine-containing compound and its preparation method and application
  • Functional magnetic oxidized graphene catalyst material of hydramine-containing compound and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The preparation method of graphene oxide is as follows:

[0040] (1) Measure 23mL of concentrated sulfuric acid (98%), pour it into a three-necked flask and then ice-bath it to lower its temperature below 4°C. Subsequently, 1 g of graphite powder and 0.5 g of sodium nitrate were weighed. After it is dispersed in concentrated sulfuric acid, slowly add 3g of potassium permanganate into the mixed solution within 1h, and control the reaction temperature during the addition process not to exceed 10°C; after the addition of potassium permanganate is completed, react below 10°C for 1h.

[0041] (2) The temperature of the mixed solution obtained from the above reaction was raised to 38° C., and allowed to react with stirring at 38° C. for 0.5 h. Subsequently, 80 mL of distilled water was slowly added to the mixed solution. And slowly raise the temperature to 95°C, and keep stirring for 30min. Afterwards, 60 mL of deionized water was added to the mixed solution to stop the re...

Embodiment 2

[0044] The preparation method of the magnetic graphene oxide catalytic material of triethanolamine functionalization is as follows:

[0045] (1) Add 10 g of 98% triethanolamine into 20 mL of distilled water, and stir at room temperature for 30 min.

[0046] (2) 0.3g FeCl 3 ·6H 2 O was added to the above solution and stirred at 25 °C for 30 min.

[0047] (3) Add 15 mL (concentration of about 6 mg / mL) graphene oxide suspension into the solution prepared in step (2), and stir at 25° C. for 30 min.

[0048] (4) Add the stirred reaction precursor into a polytetrafluoroethylene-lined reactor, set the heating rate of the reactor so that the temperature of the solution in the reactor rises to 200°C within 200 minutes, and Insulation reaction 6h.

[0049] (5) After the reaction is completed, after the temperature of the reactor is cooled to room temperature, it is washed to neutrality with an aqueous solution, and the magnetic graphene oxide catalytic material (A) modified by triet...

Embodiment 3

[0054] Catalytic degradation performance of ferroferric oxide nanoparticles and triethanolamine functionalized magnetic graphene oxide catalytic material for methylene blue:

[0055] Preparation 50mL concentration is 100mg / L, and pH is the solution of the methylene blue of 4.0, wherein the concentration of hydrogen peroxide is 10mmol / L, adds the magnetic graphene oxide catalytic material of ferric oxide nano-particle and triethanolamine functionalization of 10mg respectively, React at 80°C for 35 minutes. The experimental results are as Figure 4 shown by Figure 4 It can be seen that the triethanolamine functionalized magnetic graphene oxide material (A) has a degradation rate of more than 98% for methylene blue in 5 minutes, and its degradation rate is much higher than that of ferric oxide nanoparticles. This shows that the triethanolamine-functionalized magnetic graphene oxide can effectively solve the problem of agglomeration of iron ferric oxide nanoparticles, and the l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a functional magnetic oxidized graphene catalyst material of hydramine-containing compound and its preparation method and application. The catalyst takes hydramine-containing compound, oxidized graphene trivalent ferric salt; through hydrothermal reaction, the one-step synthesis is realized; ferriferrous oxide nanoparticles in the prepared catalyst material are firmly anchored on the surface of the oxidized graphene by the hydramine-containing compound, thereby effectively solving problems of uneven dispersion and poor stability of ferriferrous oxide and avoiding the agglomeration and loss of the ferriferrous oxide in the application process; besides, ferriferrous oxide is tightly combined with the oxidized graphene and the hydramine-containing compound so that the pollutant and electronic transfers are more convenient, the Fenton catalytic degradation performance of the composite material is greatly promoted; the catalyst method of the catalyst material is simple in technique, mild in condition, free from waste discharge, safe and environmental-friendly; therefore, the material is more applicable to the scaled industrial production and application.

Description

technical field [0001] The invention relates to a Fenton catalyst, in particular to a functionalized magnetic graphene oxide catalytic material containing hydroxylamine compounds, a preparation method thereof and a functionalized magnetic graphene oxide catalytic material containing hydroxylamine compounds as a Fenton catalyst in The application in treating organic matter in water belongs to the technical field of organic wastewater treatment. Background technique [0002] With the rapid development of cities and industries, global water pollution is increasing day by day. There are many kinds of organic pollutants in water bodies and they are very harmful. Simple physical treatment methods cannot completely degrade or transform pollutants, so Fenton oxidation technology has gradually become a hot spot of concern. The combination of ferrous salt and hydrogen peroxide becomes Fenton's reagent, Fe 2+ and H 2 o 2 The reaction generates hydroxyl radicals with high oxidation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/745B01J21/18C02F1/72C02F101/30
CPCC02F1/725B01J21/18B01J23/745C02F2101/308B01J35/33
Inventor 曹占芳温欣钟宏王帅刘广义
Owner 杭州蓝锋尚能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com