Environment-friendly PVA solid glue and preparation method thereof

A solid glue, environmental protection technology, applied in the direction of glue sticks, adhesives, adhesive types, etc., can solve the problems of non-fine texture, affecting coating performance, formaldehyde removal, etc., and achieve the effect of cheap production cost and improved performance

Inactive Publication Date: 2017-11-28
NINGBO PASCO UNITED IND
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the texture of this glue stick is not delicate, which affects the spreadability during use
[0003] Glue sticks made from polyvinyl acetal contain residual aldehydes, and aldehydes, especially formaldehyde and acetaldehyde, are harmful to human health if exposed to them for a long time, such as Chen Yonghong (China Adhesives. 2001, 10 (3): 21-23) have studied with polyvinyl alcohol, formaldehyde, urea, sodium stearate etc. as main raw material and prepare the formula and the technological condition of solid glue stick, although the solid glue stick of production, reduce glue stick with urea The content of formaldehyde in the medium, but can not really remove the formaldehyde

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0055] A preparation method of environment-friendly PVA solid glue, comprising the following steps:

[0056] Step 1, prepare raw materials;

[0057] Step 2. Add deionized water into the reaction kettle, stir slowly and add polyvinyl alcohol powder, wait for 20-30 minutes, so that the polyvinyl alcohol powder is fully infiltrated;

[0058] Step 3. Next, let the steam flow while stirring to raise the temperature of the mixture to 60°C to swell the PVA. After adding a humectant and half of the defoamer, raise the temperature to 95°C, keep the temperature constant for 30-60 minutes, and stir until the solution is uniform;

[0059] Step 4. After cooling to room temperature, slowly add an acid regulator to adjust the pH value to 4.5-5.5, then add a silicone modifier, and stir until the solution is transparent and clear;

[0060] Step 5: Add tackifier, and then pass steam while stirring to raise the temperature of the above mixed solution to 80-85°C, add sodium hydroxide to the solu...

Embodiment 1

[0064] Step 1, prepare raw materials according to the following weight percentages:

[0065] Deionized water 62.05%, glycerin 7.0%, propylene glycol 5.0%, polyvinyl alcohol (PVA) 15.0%, hydrochloric acid 0.3%, polyacrylic acid emulsion 3.0%, silane coupling agent 0.55%, defoamer 0.3%, sodium hydroxide 0.3 %, sodium stearate 6.0%, sodium sulfite 0.3%, BIT0.20%;

[0066] Step 2. Add deionized water into the reaction kettle, stir slowly and add polyvinyl alcohol powder, wait for 20 minutes, so that the polyvinyl alcohol powder is fully infiltrated;

[0067] Step 3. Next, let the steam flow while stirring to raise the temperature of the mixed solution to 60°C to swell the PVA. After adding a humectant (7.0% glycerin, 5.0% propylene glycol) and half of the defoamer, raise the temperature to 95°C and keep the temperature at 30°C. Minutes, stir until the solution is uniform;

[0068]Step 4. After cooling to room temperature, slowly add an acid regulator to adjust the pH value to 4....

Embodiment 2

[0072] Step 1, prepare raw materials according to the following weight percentages:

[0073] Deionized water 67.05%, glycerin 6.0%, propylene glycol 4.0%, polyvinyl alcohol (PVA) 13.0%, sulfuric acid 0.3%, water-based polyurethane 3.0%, silane coupling agent 0.55%, defoamer 0.3%, sodium hydroxide 0.3% , sodium stearate 5.0%, sodium sulfite 0.3%, OIT 0.20%;

[0074] Step 2. Add deionized water into the reaction kettle, stir slowly and add polyvinyl alcohol powder, wait for 20 minutes, so that the polyvinyl alcohol powder is fully infiltrated;

[0075] Step 3. Next, let the steam flow while stirring to raise the temperature of the mixed solution to 60°C to swell the PVA. After adding a humectant (6.0% glycerin, 4.0% propylene glycol) and half of the defoamer, raise the temperature to 95°C and keep the temperature at 60°C. Minutes, stir until the solution is uniform;

[0076] Step 4. After cooling to room temperature, slowly add an acid regulator to adjust the pH value to 5.5, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A kind of environment-friendly PVA solid glue of the present invention comprises deionized water 40.0%-70.0%, humectant 2.0%-15.0%, polyvinyl alcohol 10%-25.0%, acid regulator 0%-1.0%, tackifier 1.0%‑5.0%, silicone modifier 0.05%‑5.0%, defoamer 0%‑0.5%, sodium hydroxide 0.1%‑0.5%, sodium stearate 1.0%‑10.0%, antioxidant 0 %‑0.5%, preservative 0.20%‑0.30%; the preparation method is: add deionized water and polyvinyl alcohol powder in the reaction kettle, add humectant and half of the defoamer after heating by steaming, add acidic acid after cooling to room temperature Regulator to adjust the PH value, then add silicone modifier, then add tackifier, sodium hydroxide, sodium stearate, the remaining half of defoamer, antioxidant and preservative, and let it stand for discharging and filling. Cooling molding obtains PVA solid glue.

Description

technical field [0001] The invention relates to an environment-friendly solid glue, in particular to an environment-friendly PVA solid glue and a preparation method thereof. Background technique [0002] Solid glue stick is also called solid glue. Compared with liquid glue, solid glue stick is not only easy to carry, but also does not flow or stick to hands, so it is very popular. The main adhesives used for solid glue sticks are polyvinyl alcohol (PVA), hydroxymethylcellulose, polyvinylpyrrolidone (PVP), polyvinyl acetal, polymer resin mixture, starch, etc., which are currently on the market. The solid glue mainly uses polyvinylpyrrolidone, polyvinyl alcohol, and polyvinyl formal as adhesives, adding some substances that are easy to solidify and form as gelling agents, and then adding humectants, preservatives, and fragrances. prepared by the drug. The adhesive paper effect of polyvinylpyrrolidone is very good, but its cost is higher; With polyvinyl alcohol as the glue st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J9/00C09J129/04C09J11/06C09J11/08
CPCC09J9/005C08K2201/014C09J11/06C09J11/08C09J129/04C08L33/02C08K13/02C08K5/053C08K5/54C08L75/04C08L3/02
Inventor 钱小华
Owner NINGBO PASCO UNITED IND
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com