Foamed light cement board

A technology of cement foaming and cement foaming agent, which is applied in the field of cement foamed lightweight board, can solve problems such as poor foaming ability, and achieve the effects of ensuring quality, improving speed and producing large foam volume.

Inactive Publication Date: 2018-01-12
南丹县住房和城乡建设局
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a cement foam lightweight board to solve the problem of poor foaming ability of the existing cement foam board

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A cement foam light board is formed by adding cement foaming agent to the cement slurry and then pouring it into a mold to solidify. The cement slurry includes the following components in parts by mass: 25 parts of acid cement, 10 parts of sodium polyacrylate , 10 parts of calcium chloride, 5 parts of sodium bicarbonate, 5 parts of magnesium oxide, 5 parts of sodium dodecylbenzenesulfonate, 3 parts of disodium edetate, 10 parts of quartz sand, 5 parts of sodium pyrophosphate; The acid cement of the present embodiment is a mixture of Portland cement and sulphoaluminate cement;

[0013] The cement foaming agent comprises the following components by mass: 25 parts of cement composite foaming agent paste, 10 parts of hydrogen peroxide, 1 part of polyether modified silicone oil, and 10 parts of water; The paste, hydrogen peroxide, polyether modified silicone oil and water are added into a high-speed mixer and stirred to obtain a cement foaming agent.

Embodiment 2

[0015] A cement foam light board is formed by adding cement foaming agent to cement slurry, stirring it, pouring it into a mold and solidifying it. The cement slurry includes the following components by mass: 35 parts of acid cement, 15 parts of sodium polyacrylate , 25 parts of calcium chloride, 10 parts of sodium bicarbonate, 15 parts of magnesium oxide, 8 parts of sodium dodecylbenzenesulfonate, 5 parts of disodium edetate, 15 parts of quartz sand, and 9 parts of sodium pyrophosphate; The acid cement of the present embodiment is sulphoaluminate cement;

[0016] The cement foaming agent comprises the following components by mass: 80 parts of cement composite foaming agent paste, 35 parts of hydrogen peroxide, 5 parts of polyether modified silicone oil, and 45 parts of water; The paste, hydrogen peroxide, polyether modified silicone oil and water are added into a high-speed mixer and stirred to obtain a cement foaming agent.

Embodiment 3

[0018] A cement foam light board is formed by adding cement foaming agent to the cement slurry and then pouring it into a mold to solidify. The cement slurry includes the following components by mass: 25 parts of acid cement, 10 parts of sodium polyacrylate , 10 parts of calcium chloride, 5 parts of sodium bicarbonate, 5 parts of magnesium oxide, 5 parts of sodium dodecylbenzenesulfonate, 3 parts of disodium edetate, 10 parts of quartz sand, 5 parts of sodium pyrophosphate; The acid cement of the present embodiment is Portland cement;

[0019] The cement foaming agent comprises the following components by mass: 25 parts of cement composite foaming agent paste, 10 parts of hydrogen peroxide, 1 part of polyether modified silicone oil, and 20 parts of water; The paste, hydrogen peroxide, polyether modified silicone oil and water are added into a high-speed mixer and stirred to obtain a cement foaming agent.

[0020] Since the cement slurry is made of acid cement, sodium polyacry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a foamed light cement board, and belongs to the technical field of production of foamed cement boards. The foamed light cement board is formed by adding a cement foaming agentinto a cement slurry, stirring, pouring into a mould and curing, wherein the cement slurry comprises the following components in parts by mass: 25-35 parts of acid cement, 10-15 parts of sodium polyacrylate, 10-25 parts of calcium chloride, 5-10 parts of sodium hydrogen carbonate, 5-15 parts of magnesium oxide, 5-8 parts of sodium dodecyl benzenesulfonate, 3-5 parts of disodium ethylenediaminetetraacetate, 10-15 parts of quartz sand and 5-9 parts of sodium pyrophosphate; the cement foaming agent comprises the following components in parts by mass: 25-80 parts of a composite cement foaming agent paste, 10-35 parts of hydrogen peroxide, 1-5 parts of polyether-modified silicone oil and 10-45 parts of water. Compared with the prior art, the foamed light cement board has the advantage as follows: the problem that the conventional foamed cement board has a poor foaming capability can be solved.

Description

technical field [0001] The invention relates to the technical field of cement foam board manufacture, in particular to a cement foam lightweight board used for building exterior walls. Background technique [0002] Cement foam board is launched in response to the national "Interim Regulations on Fire Protection of Civil Building External Thermal Insulation System and External Wall Decoration". After the cement foaming agent is mixed with the cement slurry and poured into shape, it is the best product currently used in the fire barrier. At present, the foaming agents used in the manufacture of cement foam boards can be divided into three categories: chemical foaming agents, physical foaming agents and surfactants; Correspondingly, the foaming ability is poor, which directly increases the bearing capacity of the main project, and cannot meet the needs of customers pursuing lightweight and environmentally friendly products. Contents of the invention [0003] The technical p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B38/02C04B111/40C04B111/52
Inventor 韦建宇
Owner 南丹县住房和城乡建设局
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap