A kind of hot-melt marking paint and preparation method thereof

A marking paint, hot-melt type technology, applied in the field of marking paint, can solve the problems of reducing the reflective effect and service life of marking lines, and the falling off of reflective materials, so as to improve visibility, reduce cracks and even fall off of marking lines, Effect of increasing light intensity

Active Publication Date: 2018-10-23
WELL ROAD MACHINERY CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For another example, the current improvement methods for improving the nighttime visibility and rainy day visibility of marking paint are usually achieved through the traditional method of adding reflective materials such as ordinary glass beads, but conventional reflective materials such as glass beads are usually All of them exist in the marking paint in granular form. During use, the reflective material will fall off due to the abrasion of vehicle tires and road cleaning operations, which will significantly reduce the reflective effect and service life of the marking. Frequent refurbishment of marking lines

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hot-melt marking paint and preparation method thereof
  • A kind of hot-melt marking paint and preparation method thereof
  • A kind of hot-melt marking paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A hot-melt marking paint, comprising a primer coating, an intermediate coating and a surface coating; wherein the primer coating is prepared from the following raw materials in parts by weight: 25 parts of EVA resin, 30 parts of acrylic resin, terephthalate 2.5 parts of dioctyl formate, 4 parts of mineral fusion oil, 13 parts of asphaltene from petroleum rectification, 2.5 parts of polyisobutylene, 3 parts of microcrystalline wax, 6 parts of butyl acetate, 8 parts of hexamethyldisiloxane;

[0035] The intermediate layer coating is prepared from the following raw materials in parts by weight: 12 parts of EVA resin, 30 parts of C5 petroleum resin, 5 parts of castor oil resin, 5 parts of elastic acrylic resin, 18 parts of heavy calcium carbonate, 23 parts of quartz sand, modified 5 parts of soybean oil, 7 parts of ethoxy ethyl propionate, 2.5 parts of microcrystalline wax, 1.5 parts of polyethylene wax, 5 parts of glass fiber, 2.5 parts of polymer fiber, 12 parts of pigment...

Embodiment 2

[0043] A hot-melt marking paint, comprising a primer coating, an intermediate coating and a surface coating; wherein the primer coating is prepared from the following raw materials in parts by weight: 20 parts of EVA resin, 20 parts of acrylic resin, terephthalate 2 parts of dioctyl formate, 3 parts of mineral fusion oil, 15 parts of asphaltene from petroleum rectification, 3 parts of polyisobutylene, 2 parts of microcrystalline wax, 5 parts of butyl acetate, 9 parts of hexamethyldisiloxane;

[0044] The intermediate layer coating is prepared from the following raw materials in parts by weight: 10 parts of EVA resin, 20 parts of C5 petroleum resin, 6 parts of castor oil resin, 4 parts of elastic acrylic resin, 15 parts of heavy calcium carbonate, 20 parts of quartz sand, modified 6 parts of soybean oil, 6 parts of ethoxy ethyl propionate, 2 parts of microcrystalline wax, 2 parts of polyethylene wax, 4 parts of glass fiber, 2 parts of polymer fiber, 10 parts of pigment, 5 parts ...

Embodiment 3

[0049] A hot-melt marking paint, comprising a primer coating, an intermediate coating and a surface coating; wherein the primer coating is prepared from the following raw materials in parts by weight: 30 parts of EVA resin, 40 parts of acrylic resin, terephthalate Dioctyl formate 3 parts, mineral fusion oil 5 parts, petroleum distillation asphaltenes 10 parts, polyisobutylene 2 parts, microcrystalline wax 4 parts, butyl acetate 7 parts, hexamethyldisiloxane 7 parts;

[0050] The intermediate layer coating is prepared from the following raw materials in parts by weight: 15 parts of EVA resin, 35 parts of C5 petroleum resin, 4 parts of castor oil resin, 6 parts of elastic acrylic resin, 20 parts of heavy calcium carbonate, 25 parts of quartz sand, modified 4 parts of soybean oil, 8 parts of ethyl ethoxy propionate, 3 parts of microcrystalline wax, 1 part of polyethylene wax, 6 parts of glass fiber, 3 parts of polymer fiber, 10 parts of nano strontium aluminate phosphor, rare eart...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of traffic paint and in particular relates to hot-melt traffic paint and a preparation method thereof. According to the paint, multiple functional aids areselected to be combined to be used, the wear resistance, cracking resistance, corrosion resistance and antifouling property of the paint are improved. The primer paint can be well combined with the ground, so that pavement micro-pores are closed, the variation of the pavement and traffic line deformation under high-temperature or high-pressure conditions can be balanced, cracking even drop of thetraffic line caused by the variation of the deformation is reduced, and the mind-set of improving the cracking resistance, drop and other inner performances of the traffic line by adjusting the components and doses of various aids in the paint only in the traditional paint is broken; coloring pigments and auxiliary luminous materials are added into intermediate paint layer to serve as a traffic sign luminous layer and are combined with the surface paint to be used; glass beads are added into the surface paint, so that the reflective refraction of the coating is improved. Due to rare-earth high polymer photoluminescence materials and nano fluorescent particles in the intermediate layer and the surface layer, the visibility of the traffic line is obviously improved.

Description

technical field [0001] The invention relates to the technical field of marking paint, in particular to a hot-melt marking paint and a preparation method thereof. Background technique [0002] Road marking paint is a kind of safety mark and a "special voice". The traffic safety management department uses road marking paint to delineate vehicle driving lanes and channelize traffic, so as to strengthen traffic safety management, reduce vehicle and personal accidents and beautify purpose of urban roads. Therefore, the performance requirements for road marking paint are relatively high, and usually require quick drying, visibility, anti-rutting, low-temperature and high-temperature resistance, wear resistance, rain reflective properties, etc., and with the continuous increase in the number of vehicles In order to prolong the service life of the marking paint and prolong the replacement cycle, it is usually required that the marking paint has good antifouling performance, and eve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D123/08C09D7/61C09D7/63C09D157/02C09D5/22C09D5/08C09D5/32C09D5/16C09D5/33
Inventor 王树文杨传光向永
Owner WELL ROAD MACHINERY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com