Method for continuously preparing boron-doped SiO2 aerogel

An aerogel, boron-doped technology, applied in chemical instruments and methods, inorganic chemistry, non-metallic elements, etc., can solve the problems of affecting the physical properties of silica aerogel, large thermal conductivity, low porosity, etc. Achieve the effect of good light transmittance, high continuity and high porosity

Inactive Publication Date: 2018-02-06
CANEW TECH SHENZHEN CO LTD
View PDF10 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these substances exist between the aerogels in the state of larger particles, which seriously affect the physical properties of the silica airgel itself.
Make it denser and have lower porosity, which has a greater impact on its thermal conductivity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for continuously preparing boron-doped SiO2 aerogel
  • Method for continuously preparing boron-doped SiO2 aerogel
  • Method for continuously preparing boron-doped SiO2 aerogel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] Take the modulus as 3.2, SiO 2 Content is 2842g of water glass of 72.14%, and with water glass, deionized water according to the ratio of molar ratio is 1:15 mixes evenly, carries out ion removal by cation exchange resin device, obtains silicic acid sol, then adds dehydrated alcohol, Methyltriethoxysilane, boric acid and hydrochloric acid solution are mixed, and the overall molar ratio of industrial water glass, deionized water, hydrochloric acid, boric acid, absolute ethanol and methyltriethoxysilane is 1:15:0.001:0.001: 10:0.1. After uniform mixing, measure the pH value of the mixed solution at this time to be 3.4, and let it stand for 1 hour. The amount of ammonia added is 5% of the molar amount of water glass, which is diluted and slowly added to the mixed sol, stirred while adding, and the amount of ammonia added is controlled by a flow rate meter. Carry out post-treatment of the gel according to the process of process 1. After the gel reaction occurs, extrude t...

Embodiment 2

[0059] Take the modulus as 3.2, SiO 2 Content is 2842g of water glass of 72.14%, and water glass, deionized water are mixed evenly according to the ratio of 1:10 according to molar ratio, carries out ion removal by cation exchange resin device, obtains silicic acid sol, then adds dehydrated alcohol, Methyltriethoxysilane, boric acid and hydrochloric acid solution are mixed, and the overall molar ratio of industrial water glass, deionized water, hydrochloric acid, boric acid, absolute ethanol and methyltriethoxysilane is 1:10:0.1:0.1: 10:1. After uniform mixing, measure the pH value of the mixed solution at this time to be 1.8, and let it stand for 1 hour. The amount of ammonia added is 25% of the molar weight of water glass, which is diluted and slowly added to the mixed sol, stirred while adding, and the amount of ammonia added is controlled by a flow rate meter. After the gel reaction occurs, follow-up treatment is carried out according to the process of process 2. Put th...

Embodiment 3

[0061] Take the modulus as 3.2, SiO 2 Content is 2842g of water glass of 72.14%, and with water glass, deionized water according to the ratio that molar ratio is 1:30, mixes evenly, carries out ion removal by cation exchange resin device, obtains silicic acid sol, then adds dehydrated alcohol, Methyltriethoxysilane, boric acid and hydrochloric acid solution are mixed, and the overall molar ratio of industrial water glass, deionized water, hydrochloric acid, boric acid, absolute ethanol and methyltriethoxysilane is 1:30:0.01:0.5: 30:0.5. After uniform mixing, measure the pH value of the mixed solution at this time to be 3.6, and let it stand for 1 hour. The add-on of ammonia water is 16.8% of the molar weight of water glass, it is slowly added in the mixed sol after diluting, stirs while adding, controls the add-on of ammonia water by flow velocity meter. After the gel reaction occurs, process 1 is used to carry out subsequent treatment on the gel. Extrude the gel into the m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for continuously preparing boron-doped SiO2 aerogel, belonging to the preparation field of novel porous materials. According to the method, by setting a preparation system with the functions of raw material feeding, sol preparation, gel preparation, solvent replacement, gel drying and waste material recycling, a large number of boron-doped SiO2 aerogel can be continuously produced. The method has the advantages that the occupied area of equipment is small, the preparation process is continuous and controllable, the production energy consumption is reduced, theequipment cost is lowered, and the labor cost is lowered. The prepared boron-doped SiO2 aerogel has good mechanical property, light transmittance performance and high-temperature stability.

Description

technical field [0001] The invention belongs to the field of preparation of novel inorganic porous materials, in particular to a method for continuously preparing boron-doped SiO with high mechanical strength, low thermal expansion coefficient, high light transmission performance and high thermal stability. 2 Airgel method. Background technique [0002] SiO 2 Airgel is a typical three-dimensional network structure nanomaterial with large specific surface area, high porosity, low density, low thermal conductivity and good dielectric properties. Its unique nanostructure makes it have broad application prospects in the fields of thermal insulation, energy saving, catalytic carrier, oil pollution adsorption and aerospace. [0003] Existing SiO 2 Airgel production mostly uses organosilicon (tetraethyl orthosilicate, methyl orthosilicate) as raw materials, and is dried and produced under supercritical conditions. For example, the production technology of airgel has been disclo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B33/158
CPCC01B33/1585C01P2006/10
Inventor 李蒙蒙陈晓星余永禄刘晓明
Owner CANEW TECH SHENZHEN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap