Novel degradable polyurethane biological material as well as preparation method and application thereof

A biomaterial, polyurethane technology, applied in the field of biomedical polymer materials, can solve the problems of lack of selective arrangement and combination of blocks, difficult to control material properties, etc., and achieve the effects of high surface energy, high crystallinity, and enhanced mechanical strength

Inactive Publication Date: 2018-02-13
许开天
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, almost all conventional segmented polyurethanes are synthesized by coupling the terminal hydroxyl groups of diols or / and polyols with isocyanates using diisocyanates as coupling agents, even though this method provides materials with improved properties, But in fact, it lacks block selectivity and regular arrangement and combination, and can only be assembled and connected in a random way to form a block copolymer (that is, a traditional random block polyurethane polymer, abbreviated: RanPU, such as figure 1 shown), and this kind of random structure will make the material properties difficult to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel degradable polyurethane biological material as well as preparation method and application thereof
  • Novel degradable polyurethane biological material as well as preparation method and application thereof
  • Novel degradable polyurethane biological material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Synthesis of Alternating Block Polyurethanes (Alt-PU) and Random Block Polyurethanes (Ran-PU) Based on Aliphatic Polyesters and Hydrophilic Polyethers:

[0050] Dissolve the aliphatic polyester diol in the organic solvent (chloroform) in the three-necked flask first, and then use the hydrophilic polyether-diisocyanate prepared by the end-capping reaction, according to the ratio of 1:1 with the diol The molar equivalent is slowly dropped into the flask, and after reacting at 30-100° C. for 8-72 hours, the alternating block polyurethane Alt-PU is obtained. Above-mentioned reaction also can directly be carried out in reaction raw material body, also can use the organotin catalyst of 1 / 100000 to 1 / 100,000 (weight ratio), as 2-ethylhexanoate tin, butyltin dilaurate etc., reflect The hydroxyl and isocyanate groups in the system should have an equal molar ratio.

[0051] Use aliphatic polyester diol and hydrophilic polyether as the reaction body, add tin-containing catalyst, ...

Embodiment 2

[0054] Application of Alternating Block Polyurethane (Alt-PU) and Random Block Polyurethane (Ran-PU) Biomaterials Prepared in Example 1 in the Preparation of Nerve Restoration Sockets: Preparation of Porous Nerve Restoration by Using Dip Coating and Salt Immersion Socket pipe, using a stainless steel wire with an outer diameter of 1.5mm as a mold, then air-drying the polymer coating on the resulting mold for 2 days, vacuum drying for 2 days, then leaching the salt in deionized water, freeze-drying and demoulding to obtain Neuroprosthetic socket.

[0055] Nerve repair sleeve, also known as nerve repair catheter or nerve repair sheath; it can also be called nerve repair covering sheet and nerve protection open tube. The nerve repair sleeve prepared by the alternating block polyurethane (Alt-PU) has a microporous pipeline structure, a microporous sheet structure and a microporous opening with a porosity of 10-99% and a pore size of 100 nm to 500 μm (micrometer). pipeline structu...

Embodiment 3

[0073] The alternating block polyurethane (Alt-PU) biomaterial prepared in Example 1 was applied to the preparation of eyelid brackets, and the manufacturing method was liquid-solid phase separation and freeze-drying method: put a certain amount of Alt-PU material into a beaker, Organic solvent was added until Alt-PU was completely dissolved into a transparent solution. Pour the solution into a stainless steel mold, control the thickness of the poured liquid surface, place the mold containing the solution in an ice-water mixing incubator at -20-0°C for 1-10 hours, take it out and place it in a -10-4°C for 1- After 24 hours, move to a freeze dryer for freeze-drying, then freeze-dry for 1-24 hours, take out the stainless steel mold and put it in a normal temperature vacuum dryer to dry for 1-48 hours, take out the molded bracket, and then cut the bracket into 1cm 2 Bracket, get 0.7mm×1cm 2 Eyelid implants. The eyelid implant bracket has a porous film structure with a porosity ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a novel biodegradable polyurethane biomaterial, its preparation method and its application in degradable implant and non-implant medical devices. The new material is an alternating block polyurethane polymer material based on biodegradable polyester diol and hydrophilic polyether diol. It is obtained by the selective coupling reaction between intermediate or aliphatic polyester diols and diisocyanate-terminated aliphatic polyester blocks. The product of the present invention has a controllable and predictable chemical structure and regular polymer chain arrangement, and has a surface microphase patterned structure, and can be widely used in many medical and non-medical device fields, among which peripheral nerve repair catheters, half-moon Excellent performance has been shown in applications such as plate repair, anti-adhesion films, meninges, eyelid reconstruction scaffolds, trauma dressings, bone composite porous repair scaffolds, and other tissue regeneration of soft and hard tissues.

Description

technical field [0001] The invention relates to the field of biomedical polymer materials, in particular to a novel biodegradable polyurethane biomaterial and its preparation method and application. Background technique [0002] Biodegradable block polyurethane is a class of widely used biomaterials. At present, several corresponding implanted medical devices have been approved by European CE and US FDA for human use. Due to its excellent hemocompatibility, excellent mechanical and processing properties, it is widely used in tissue engineering, regenerative medicine, controlled drug delivery, wound healing and other applications. However, almost all conventional segmented polyurethanes are synthesized by coupling the terminal hydroxyl groups of diols or / and polyols with isocyanates using diisocyanates as coupling agents, even though this method provides materials with improved properties, But in fact, it lacks block selectivity and regular arrangement and combination, and c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/48C08G18/42C08G18/32A61L27/18A61L27/58A61L27/50A61L27/60
CPCC08G18/4825A61L27/18A61L27/50A61L27/58A61L27/60A61L2430/02A61L2430/32A61L2430/34C08G18/3206C08G18/42C08G18/4277C08G18/428C08G18/4833C08G18/4854C08G2230/00C08L75/06C08L75/08
Inventor 许开天
Owner 许开天
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com