Powder metallurgy abrasion-resistant corrosion-resistant bearing material and preparing method thereof

A bearing material and powder metallurgy technology, applied in the field of powder metallurgy, can solve problems such as low hardness, poor heat resistance, and shortened life, and achieve the effects of high hardness, excellent tensile strength performance, and strong wear resistance

Inactive Publication Date: 2018-05-15
余姚市奥祥轴承有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional bearings are mostly made of steel, but the hardness of steel is lower than that of ceramics. Bearings made of steel are not wear-resistant and have poor heat resistance. When the bearing is in a high temperature environment for a long time, the bearing made of steel is prone to expansion Deformation, leading to bearing corrosion and shortening of service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The present invention will be described in detail below through specific examples.

[0017] A powder metallurgy wear-resistant and corrosion-resistant bearing material, made of the following raw materials in parts by weight (kg): vanadium carbide 0.4, chromium carbide 0.2, graphite 0.5, molybdenum powder 2.0, nickel powder 9.4, silicon carbide 0.15, tantalum carbide 0.2, Polyethylene wax powder 2, iron powder 93, additive 1;

[0018] The auxiliary agent is made of the following raw materials in parts by weight (kg): iron powder 3, kaolin 2, nano-carbon 2, zirconium fluoride 1, alum 2, sodium alginate 3, sodium tripolyphosphate 1, corundum powder 3, Copper sulfate 1, calcium stearate 1, vinyl triethoxysilane 3; the preparation method is to mix iron powder, kaolin, zirconium fluoride, alum, sodium alginate, sodium tripolyphosphate, corundum powder, copper sulfate, Grind it into 200-300 mesh powder, then add vinyltriethoxysilane and mix evenly, press it into a billet at 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a powder metallurgy abrasion-resistant corrosion-resistant bearing material. The powder metallurgy abrasion-resistant corrosion-resistant bearing material is characterized in that the powder metallurgy abrasion-resistant corrosion-resistant bearing material is made of the following raw materials of, by weight, 0.4-0.6 part of vanadium carbide, 0.2-0.3 part of chromium carbide, 0.5-0.8 part of graphite, 2.0-3.2 parts of molybdenum powder, 9.4-9.6 parts of nickel powder, 0.15-0.25 part of silicon carbide, 0.2-0.3 part of tantalum carbide, 2-3 parts of polyethylene wax powder, 93-94 parts of iron powder and 1-2 parts of additives. The corrosion-resistant high-temperature-resistant bearing material is made by adding titanium carbide, vanadium carbide, chromium carbide,nickel, molybdenum and graphite, and has the characteristics of being high in hardness, not prone to deforming, high in corrosion resistance, resistant to high temperature, resistant to corrosion andthe like, the structural stiffness, hardness, fatigue resistance and tensile strength performance are excellent, and the powder metallurgy abrasion-resistant corrosion-resistant bearing material is suitable for the high-temperature abrasion environment.

Description

technical field [0001] The invention relates to the field of powder metallurgy, in particular to a powder metallurgy wear-resistant and corrosion-resistant bearing material and a preparation method thereof. Background technique [0002] The bearing is a component that fixes and reduces the friction coefficient of the load during the mechanical transmission process. Its main function is to support the mechanical rotating body to reduce the mechanical load friction coefficient of the equipment during the transmission process. According to the different friction properties of moving elements, bearings can be divided into two types: rolling bearings and sliding bearings. Traditional bearings are mostly made of steel, but the hardness of steel is lower than that of ceramics. Bearings made of steel are not wear-resistant and have poor heat resistance. When the bearing is in a high temperature environment for a long time, the bearing made of steel is prone to expansion Deformation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22F1/00B22F5/10C22C38/12C22C38/08C22C33/02
CPCC22C33/0285C22C38/08C22C38/12B22F5/106B22F2998/10B22F1/10B22F3/1017B22F3/02B22F9/04B22F3/1007B22F2009/043
Inventor 周栋
Owner 余姚市奥祥轴承有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap