Preparation method of anti-static carbon fibre functional composite paper

A carbon fiber and composite paper technology, applied in non-fiber pulp addition, fiber raw material processing, paper and other directions, can solve the problems of poor antibacterial performance and short service life, and achieve the effects of low cost, stable product quality and long antibacterial aging effect.

Active Publication Date: 2018-05-15
安徽鑫光新材料科技股份有限公司 +1
View PDF10 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Antistatic film materials are not suitable for the packaging of large devices, which has limitations. If paper packaging materials can be made into materials with certain antistatic properties, they can be developed into a variety of large, medium and small packaging products. Its application fields Very wide, and the antibacterial properties of existing paper packaging materials are poor, resulting in short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A preparation method of antistatic carbon fiber functional composite paper, comprising the steps of:

[0023] S1. Crush 50kg of wheat straw and 40kg of waste paper, add water until the water content is 90wt%, let it stand for 5 days, drain it, and soak it in a potassium hydroxide solution with a concentration of 1mol / L for 12 days, steam it in water for 20 hours, and dry it. Wet ball milling, concentration, beating, and papermaking to obtain blank paper;

[0024] S2. Mix 20kg of waste paper and 50kg of potassium hydroxide solution with a concentration of 1.2mol / L, let it stand at room temperature for 2 days, then raise the temperature to 80°C and stir for 2 hours, filter with suction, wash the filter cake, dry at 80°C to constant weight, add 30kg of seawater Foam stone powder, 2kg lauryl ammonium chloride, 80kg silver nitrate solution with a concentration of 1.2wt%, adjust the pH value of the system to 6.4-6.8, stir evenly, add 0.2kg silane coupling agent KH-550, stir e...

Embodiment 2

[0027] A preparation method of antistatic carbon fiber functional composite paper, comprising the steps of:

[0028] S1. Pulverize 60kg of wheat straw and 30kg of waste paper, add water until the water content is 80wt%, let stand for 7d, drain and soak in potassium hydroxide solution with a concentration of 2mol / L for 8d, steam for 40h, and dry. Wet ball milling, concentration, beating, and papermaking to obtain blank paper;

[0029] S2. Mix 10kg of waste paper and 100kg of potassium hydroxide solution with a concentration of 0.8mol / L, let it stand at room temperature for 6 days, then raise the temperature to 70°C and stir for 4 hours, filter with suction, wash the filter cake, dry at 70°C to constant weight, add 40kg of seawater Paool stone powder, 1kg lauryl ammonium chloride, 120kg silver nitrate solution with a concentration of 0.5wt%, adjust the pH value of the system to 6.4-6.8, stir evenly, add 0.6kg silane coupling agent KH-550, stir evenly, and irradiate Treat for 5 ...

Embodiment 3

[0032] A preparation method of antistatic carbon fiber functional composite paper, comprising the steps of:

[0033] S1. Crush 52kg of wheat straw, 38kg of waste paper, and 10kg of waste paper, add water to a water content of 88wt%, let it stand for 5.5 days, drain it, soak it in a potassium hydroxide solution with a concentration of 1.4mol / L for 10 days, and steam it over water 25h, drying, wet ball milling, concentration, beating, and papermaking to obtain blank paper;

[0034] S2. Mix 18kg of waste paper and 90kg of potassium hydroxide solution with a concentration of 1.1mol / L, let it stand at room temperature for 3 days, then raise the temperature to 78°C and stir for 2 hours, filter with suction, wash the filter cake, dry at 76°C to constant weight, add 33kg of seawater Paool stone powder, 1.8kg lauryl ammonium chloride, 90kg silver nitrate solution with a concentration of 1wt%, adjust the pH value of the system to 6.4-6.8, stir evenly, add 0.3kg silane coupling agent KH-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of anti-static carbon fibre functional composite paper. The preparation method comprises the following steps: crushing wheat straw and waste paper, addingwater, standing, draining, soaking in a potassium hydroxide solution, steaming in a manner of insulating from water, drying, performing wet ball milling, concentrating, pulping, and performing papermaking to obtain blank paper; mixing waste paper and the potassium hydroxide solution, standing at a room temperature, then heating and stirring, performing suction filtration, washing a filter cake, drying to reach constant weight, adding a sepiolite powder, dodecyl ammonium chloride and silver nitrate solution, regulating the pH value of the system to be 6.4 to 6.8, stirring uniformly, adding a silane coupling agent KH-550, stirring uniformly, performing ultraviolet irradiation treatment, filtering, washing with deionized water, drying, and crushing to obtain a composite antibacterial agent; uniformly mixing graphite, carbon black, a coconut shell carbon powder and the composite antibacterial agent, adding an anti-static agent, a dispersing agent and an adhesive, mixing uniformly, concentrating, coating the surface of the blank paper with the mixture, drying, applying the adhesive to double surfaces, drying a finished product, and rolling paper.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to a preparation method of antistatic carbon fiber functional composite paper. Background technique [0002] As electronic products continue to change people's production and life, electronic semiconductor products are prone to generate and accumulate static electricity during long-term transportation and storage, which has a certain impact on the quality and service life of electronic products. The packaging of products puts forward higher requirements, which can prevent static electricity, and the market demand for packaging materials with higher strength is strong. [0003] The packaging of electronic products usually uses antistatic film as the inner packaging, and then uses cartons as the outer packaging and transportation packaging materials. If the permeability of paper packaging materials can be improved, water molecules in the air can be used to a certain extent, The t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H21/36D21H21/14D21H19/64D21H19/46
CPCD21H19/46D21H19/64D21H21/14D21H21/36
Inventor 赵圣亚
Owner 安徽鑫光新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap