External wall elastic emulsion with antistatic effect and method for preparing external wall elastic emulsion

An elastic emulsion and antistatic technology, applied in the field of latex paint, can solve the problems of loss of elasticity, achieve the effects of increasing flexibility, rapidly leaking charge, and reducing surface resistivity

Inactive Publication Date: 2018-06-12
上海巴德富实业有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method is to improve the stain resistance performance under the premise of loss of elasticity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] In addition, the present invention also provides a preparation method of the described elastic emulsion for exterior walls with antistatic effect, comprising the following steps:

[0039] a. Preparation of base liquid A: Add 40-50 parts of deionized water and 0.2-3 parts of emulsifier to a polymerization kettle equipped with a stirrer, condenser, and constant-flow pump feeding device, and heat up until the temperature in the kettle reaches 60-90°C;

[0040] b. Preparation of pre-emulsion B: Add all formula amounts of isooctyl acrylate, butyl acrylate, styrene, methyl methacrylate to the pre-emulsification tank with monomer metering tank and agitator at normal temperature and pressure Ester, acrylic acid, methacrylic acid, acrylamide, methacrylamide, hydroxyethyl acrylate, acrylonitrile, acid anhydride functional monomers, 0.8-5 parts of emulsifier, 40-50 parts of deionized water, stir and mix until uniform the pre-emulsion, and stirred for 10-50 minutes for later use; ...

Embodiment 1

[0047] An elastic emulsion for exterior walls with antistatic effect, comprising the following components in parts by weight: 90 parts of deionized water, 10 parts of isooctyl acrylate, 60 parts of butyl acrylate, 20 parts of styrene, methyl methacrylate 5 parts of ester, 0.1 part of acrylic acid, 0.1 part of methacrylic acid, 0.1 part of acrylamide, 3 parts of acrylonitrile, 0.5 part of anhydride functional monomer, 0.5 part of diethanolamine, 0.1 part of modified phosphate polymer, emulsifier 1 part, 0.1 part of initiator, and 0.3 part of ammonia water.

[0048] As an improvement, the acid anhydride functional monomer is mixed with trifluoric anhydride and maleic anhydride in any proportion.

[0049] As an improvement, the modified phosphate ester polymer is a self-made alkyl phosphate amine oxide, which is esterified and copolymerized by heating the alkyl tertiary amine and phosphorus pentoxide in a water bath at 50°C, and then the obtained esterified product The pH is adj...

Embodiment 2

[0069] A kind of exterior wall elastic emulsion with antistatic effect, by weight, comprises the following components: 105 parts of deionized water, 20 parts of isooctyl acrylate, 70 parts of butyl acrylate, 30 parts of styrene, methyl methacrylate 10 parts of ester, 1 part of acrylic acid, 1 part of methacrylic acid, 0.5 parts of acrylamide, 0.2 parts of methacrylamide, 0.2 parts of hydroxyethyl acrylate, 5 parts of acrylonitrile, 1.2 parts of anhydride functional monomer, 2 parts of diethanolamine , 2 parts of modified phosphate ester polymer, 5 parts of emulsifier, 2 parts of initiator, and 2 parts of ammonia water.

[0070] As an improvement, the acid anhydride functional monomer is fumaric anhydride.

[0071] As an improvement, the modified phosphate ester polymer is a self-made alkyl phosphate amine oxide, which is esterified and copolymerized by heating the alkyl tertiary amine and phosphorus pentoxide in a water bath at 65°C, and then the obtained esterified product T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses external wall elastic emulsion with an antistatic effect and a method for preparing the external wall elastic emulsion. The external wall elastic emulsion comprises, by weight,90-120 parts of deionized water, 10-30 parts of iso-octyl acrylate, 60-80 parts of butyl acrylate, 20-35 parts of styrene, 5-15 parts of methyl methacrylate, 0.1-2 parts of acrylic acid, 0.1-1.5 parts of methacrylic acid, 0.1-1 part of acrylamide, 0-0.5 part of methacrylamide, 0-0.5 part of hydroxyethyl acrylate, 3-10 parts of acrylonitrile, 0.5-3 parts of acid anhydride functional monomers, 0.5-4 parts of diethanolamine, 0.1-3 parts of modified organophosphate high polymers, 1-8 parts of emulsifiers, 0.1-5 parts of initiators and 0.3-4.5 parts of ammonia water. The external wall elastic emulsion and the method have the advantages that the antistatic effect can be realized by the external wall elastic emulsion, the external wall elastic emulsion is excellent in stain resistance, and the excellent normal-temperature and low-temperature elasticity of the external wall elastic emulsion can be kept.

Description

technical field [0001] The invention relates to an exterior wall elastic emulsion with antistatic effect and a preparation method thereof, belonging to the technical field of latex paint. Background technique [0002] With the rapid growth of my country's economy, environmental pollution is also getting heavier, and various dusts and oily smog in the atmosphere are increasing. A considerable part of the exterior wall latex paint film loses its aesthetics and decoration due to the dirty surface. The service life of exterior wall latex paint is closely related to its stain resistance, and the quality of stain resistance has become the main obstacle for the application of exterior wall latex paint. At present, the adhesion pollution of exterior wall latex paint can be divided into two types: one is adhesion pollution; the other is inhalation pollution. Adhesive pollution means that pollutants are only physically adsorbed on the surface of the paint film; inhalation pollution m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/08C09D5/24C09D5/16C09D7/65C08F220/18C08F220/14C08F212/08C08F220/06C08F220/56C08F220/20C08F220/44C08F222/06C08F8/32
CPCC08F8/32C08F220/18C08F220/1804C09D5/1656C09D5/1687C09D5/24C09D133/066C08F220/1808C08F220/14C08F212/08C08F220/06C08F220/56C08F220/20C08F220/44C08F222/06
Inventor 梁显平董宇军黄宁陈晓波江彬
Owner 上海巴德富实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com