Porous grapheme-based air purifying agent

An air purifier, porous graphene technology, applied in inorganic chemistry, alkali metal compounds, other chemical processes, etc., can solve problems such as human harm and secondary pollution

Inactive Publication Date: 2018-10-02
ANHUI LEJIN ENVIRONMENT TECH CO LTD
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the commonly used method of getting out of the irritating gas in the car room is to open the window and discharge the harmful gas into the air. When the ambient temperature is too high or too low, this discharge method is restricted, or the purchase of an adsorbent The substances adsorb harmful gases, but most of these adsorptive substances can only adsorb indoor pollutants without degrading them, which will cause secondary pollution and still have great harm to the human body.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porous grapheme-based air purifying agent

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0009] The present invention also provides a kind of preparation method of described porous graphene-based air cleaner, comprises the following steps:

[0010] (1) Add foaming agent to polypropylene resin and mix evenly, then obtain polypropylene fiber by electrospinning, and calcinate polypropylene fiber at 300-450°C for 2-4 hours to obtain porous carbon fiber;

[0011] (2) Mix porous carbon fiber, soluble metal salt, silane coupling agent and organic titanate in a solvent to obtain a mixed system, then add inorganic acid to adjust the pH value of the mixed system to be acidic, and then sonicate for 15 to 30 minutes, Then seal and react at 80-120°C for 3-6 hours to obtain modified porous carbon fibers;

[0012] (3) Mix graphene oxide and oxometalate in an aqueous solution evenly, then add melamine, and then seal and react at 80-150°C for 3-8 hours under airtight conditions to obtain a mixed system, and then put the mixed system in the microwave The reaction was carried out f...

Embodiment 1

[0022] A porous graphene-based air cleaner, made of the following parts by weight: 8 parts by weight of tetraethyl titanate, 0.5 parts by weight of nickel acetate, 1.5 parts by weight of silane coupling agent KH7921, 4 parts by weight of graphene oxide , 4 parts by weight of sodium tungstate, 4 parts by weight of melamine, 3 parts by weight of N,N'-dinitrosopentamethylenetetramine, 105 parts by weight of polypropylene resin, 4 parts by weight of hydrochloric acid (2M), 50 parts by weight of ethanol share.

[0023] The preparation method of described porous graphene-based air cleaner comprises the following steps:

[0024] (1) Add N,N'-dinitrosopentamethylenetetramine to polypropylene resin and mix evenly, then obtain polypropylene fiber by electrospinning. The electrospinning process is: power supply voltage 50kV, spinning The temperature is 35°C, the relative humidity is 75%; the needle spacing of the multi-needle spinneret unit is 35cm, and the number of needleheads of the ...

Embodiment 2

[0030] A porous graphene-based air cleaner, made of the following parts by weight: 5 parts by weight of tetraisopropyl titanate, 0.8 parts by weight of magnesium nitrate, 1.8 parts by weight of silane coupling agent KH580, 6 parts by weight of graphene oxide 3 parts by weight of sodium molybdate, 5 parts by weight of melamine, 2 parts by weight of N,N'-dinitrosopentamethylenetetramine, 100 parts by weight of polypropylene resin, 3 parts by weight of hydrochloric acid (3M), 45 parts by weight of water parts by weight.

[0031](1) Add N,N'-dinitrosopentamethylenetetramine to polypropylene resin and mix evenly, then obtain polypropylene fiber by electrospinning. The electrospinning process is: power supply voltage 50kV, spinning The temperature is 35°C, the relative humidity is 75%; the needle spacing of the multi-needle spinneret unit is 35cm, and the number of needleheads of the spinneret unit is 90;

[0032] Calcining polypropylene fibers at 400°C for 2.5 hours to obtain poro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of purifying agents for vehicles, in particular to a porous grapheme-based air purifying agent. The porous grapheme-based air purifying agent is prepared from the following substances in parts by weight: 3-12 parts of organic titanate, 0.1-1 part of soluble metal salt, 1-3 parts of a silane coupling agent, 5-8 parts of graphene oxide, 3-8 parts of oxometallate, 1-12 parts of tripolycyanamide, 1-5 parts of a foaming agent, 80-150 parts of polypropylene resin, 2-10 parts of inorganic acid and 10-50 parts of a solvent. The porous grapheme-based air purifying agent can adsorb harmful gases in air, can catalyze the harmful gases in situ at an adsorption point, and has the advantages of high catalytic efficiency, high removal rate and thorough purification.

Description

technical field [0001] The invention relates to the technical field of air purifiers, in particular to a porous graphene-based air purifier. Background technique [0002] When the concentration of VOCs (volatile organic compounds) in the indoor air is too high, it is easy to cause acute poisoning. In mild cases, headache, dizziness, cough, nausea, vomiting, or drunkenness will occur; in severe cases, liver poisoning and even coma will occur soon , and some may be life-threatening. Living in a room polluted by VOCs for a long time can cause chronic poisoning, damage the liver and nervous system, cause general weakness, drowsiness, and itchy skin. Some may also cause endocrine disorders and affect sexual function; benzene and xylene can also damage the system and even cause leukemia. At present, it has been identified as a carcinogenic and teratogenic substance by the World Health Organization, and the health problems caused by indoor environmental pollution caused by VOCs h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/20B01J20/28B01J20/30B01D53/02B01D53/86D01F9/21D06M11/46D06M101/40
CPCB01J20/20B01D53/02B01D53/86B01D2253/102B01D2255/20707B01D2255/802B01J20/28023D01F9/21D06M11/46D06M2101/40
Inventor 郭常青吴学军
Owner ANHUI LEJIN ENVIRONMENT TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com