Preparation method of two-dimensional transverse polymer heterojunction visible-light response catalytic hydrogen production material and application thereof

A technology of polymers and heterojunctions, applied in the direction of organic compound/hydride/coordination complex catalysts, chemical instruments and methods, physical/chemical process catalysts, etc. Problems such as high exciton binding energy and slow transfer rate of photogenerated carriers achieve the effect of improving photocatalytic effect and low cost

Active Publication Date: 2018-10-09
TONGJI UNIV
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the polymer properties of graphitic carbon nitride, the binding energy of photogenerated excitons is high, and it is difficult to dissociate into photogenerated carriers (hot electrons and hot holes). At the s...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of two-dimensional transverse polymer heterojunction visible-light response catalytic hydrogen production material and application thereof
  • Preparation method of two-dimensional transverse polymer heterojunction visible-light response catalytic hydrogen production material and application thereof
  • Preparation method of two-dimensional transverse polymer heterojunction visible-light response catalytic hydrogen production material and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Add 10 g of melamine to 50 mL of phenanthrene in methanol, stir for 2 h at room temperature, and then ultrasonically disperse for 50 min. The power of ultrasonic dispersion is controlled at 100 W, and the temperature of ultrasonic dispersion is controlled at 40 °C. Afterwards, it was transferred to a drying oven at 60 °C for 10 h. After complete drying, it was calcined in a muffle furnace at a heating rate of 15 °C / min. During the heating process, the temperature was maintained at 300 °C for 1 h and at 400 °C for 1 h. h, keep the temperature at 550 °C for 4 h, wash with deionized water 5 times after cooling, and dry at 60 °C for 12 h. heterojunction materials. The hydrogen production of the two-dimensional heterojunction material prepared by the present invention is as high as 2156 μmol / g after being irradiated for 6 hours under a xenon lamp light source, which is about 4 times the hydrogen production of pure graphite phase carbon nitride.

[0019] The test of the phot...

Embodiment 2

[0022] 10 g of melamine was added to 25 mL of phenanthrene in methanol solution, stirred at room temperature for 2 h, and then ultrasonically dispersed for 50 min. The power of ultrasonic dispersion was controlled at 100 W, and the temperature of ultrasonic dispersion was controlled at 40 °C. Then transfer to a 60°C oven for drying for 10 hours. After complete drying, place it in a muffle furnace for calcination. The heating rate is 15°C / min. During the heating process, keep the temperature at 300°C for 1h, and keep the temperature at 400°C for 1h. Keep the temperature at 550°C for 4 h, and other operations are the same as in Example 1. The resulting photocatalytic hydrogen production was 1314 μmol / g.

Embodiment 3

[0024] 10 g of melamine was added to 75 mL of phenanthrene in methanol solution, stirred at room temperature for 2 h, and then ultrasonically dispersed for 50 min. The power of ultrasonic dispersion was controlled at 100 W, and the temperature of ultrasonic dispersion was controlled at 40 °C. Then transfer to a 60°C oven to dry for 10h. After complete drying, place it in a muffle furnace for calcination. The heating rate is 15°C / min. During the heating process, keep the temperature at 300°C for 1h, and keep the temperature at 400°C for 1h. Keep the temperature at 550°C for 4 h, and other operations are the same as in Example 1. The resulting photocatalytic hydrogen production was 1739 μmol / g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of a two-dimensional transverse polymer heterojunction visible-light response catalytic hydrogen production material and application thereof. A phenanthrene polymer semiconductor plane is grafted to a graphite phase carbon nitride plane through a high-temperature thermo-polymerization method; as a phenanthrene polymer semiconductor is matched with a graphite phase carbon nitride semiconductor energy band to form a heterojunction structure, and a built-in field is formed at a boundary of heterojunctions to promote dissociation of light excitons, thephotocatalytic performance of a graphite phase carbon nitride material is improved; meanwhile, both the phenanthrene polymer semiconductor and graphite phase carbon nitride are visible-light responsecatalysts and are polymer conjugate materials; a pi-pi conjugate exists along a heterojunction plane, so that photon-generated carriers can be transmitted faster in a pi-pi conjugate system, and thetwo-dimensional polymer heterojunction material achieves higher light exciton dissociation efficiency and carrier transmission rate. The method has the advantages of a simple process, low cost, shortperiod, visible-light response and the like, and the finally formed two-dimensional transverse polymer heterojunction photocatalytic material is excellent in photocatalytic hydrogen production performance.

Description

technical field [0001] The invention belongs to the technical field of new energy and new materials, and in particular relates to a preparation method and application of a two-dimensional transverse polymer heterojunction visible light response catalytic hydrogen production material. Background technique [0002] With the rapid development of modern industrialization, people's demand for energy is gradually increasing. The currently widely used fossil fuels have problems such as serious pollution and depleted reserves, which have brought serious troubles to the sustainable development of the earth. Since 1972, Japanese scientists Fujishima and Honda (Nature, 1972, 238, 37–38. doi:10.1038 / 238037a0) reported TiO 2 Since the photocatalytic decomposition of water to produce hydrogen under ultraviolet excitation, scientists are keen to use semiconductor photocatalysis to convert low-density solar energy into high-density hydrogen energy under solar radiation. In 2009, polymer se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J31/28B01J31/06C01B3/04
CPCB01J31/06B01J31/28B01J35/004C01B3/042C01B2203/1041C01B2203/107Y02E60/36
Inventor 陈银广董山山
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap