A kind of hydrophobic porous ceramic product and its preparation process

A technology of porous ceramics and preparation technology, applied in the field of ceramic products, can solve the problems of porous ceramics, such as the brittleness of porous ceramics has not been effectively solved, lack of continuity, large-scale system production, etc., to make up for the shortcomings of brittleness, shorten drying time, and low density. Effect

Active Publication Date: 2021-04-13
福建省泉州市契合工贸有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are various processes for preparing such porous ceramics, such as organic foam impregnation process, sol-gel process, etc., but there is still a lack of continuous, large-scale system production processes, and the brittleness of porous ceramics has not been effectively resolved. , to be further studied

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hydrophobic porous ceramic product and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A hydrophobic porous ceramic product, comprising a body and a glaze, the body comprising the following raw materials in parts by weight: 24 parts of silicon nitride, 15 parts of zirconium dioxide, 11 parts of clay, 23 parts of aluminum silicate, cordierite 14 parts, 18 parts of silicon carbide, 10 parts of diatomaceous earth, 9 parts of albite, 14 parts of aluminum oxide, 12 parts of fluxing material, described fluxing material is by weight ratio of talc, wollastonite and sodium silicate Mixed in a ratio of 2:3:3; the glaze includes the following raw materials in parts by weight: 18 parts of dolomite, 22 parts of silicon carbide, 14 parts of calcium oxide, 13 parts of potassium feldspar, 4 parts of clay, hexametaphosphoric acid Sodium 1 part.

[0027] This embodiment also provides a process for preparing the hydrophobic porous ceramic product, comprising the following steps:

[0028] Step 1. Weigh and pulverize the green body raw material according to the weight part, ...

Embodiment 2

[0036] A hydrophobic porous ceramic product, comprising a body and a glaze, the body comprising the following raw materials in parts by weight: 29 parts of silicon nitride, 16 parts of zirconium dioxide, 15 parts of clay, 25 parts of aluminum silicate, cordierite 16 parts, 19 parts of silicon carbide, 12 parts of diatomaceous earth, 11 parts of albite, 17 parts of aluminum oxide, 15 parts of fluxing material, described fluxing material is by weight ratio of talc, wollastonite and sodium silicate Mixed in a ratio of 2:3:3; the glaze includes the following raw materials in parts by weight: 22 parts of dolomite, 24 parts of silicon carbide, 15 parts of calcium oxide, 14 parts of potassium feldspar, 5 parts of clay, hexametaphosphoric acid Sodium 2 parts.

[0037] This embodiment also provides a process for preparing the hydrophobic porous ceramic product, comprising the following steps:

[0038] Step 1. Weigh and pulverize the green body raw material according to the weight, put...

Embodiment 3

[0046] A hydrophobic porous ceramic product, comprising a green body and a glaze. The green body includes the following raw materials in parts by weight: 32 parts of silicon nitride, 17 parts of zirconium dioxide, 16 parts of clay, 28 parts of aluminum silicate, cordierite 18 parts, 22 parts of silicon carbide, 15 parts of diatomite, 12 parts of albite feldspar, 21 parts of aluminum oxide, 16 parts of fluxing material, described fluxing material is by weight ratio of talc, wollastonite and sodium silicate Mixed in a ratio of 2:3:3; the glaze includes the following raw materials in parts by weight: 24 parts of dolomite, 26 parts of silicon carbide, 16 parts of calcium oxide, 18 parts of potassium feldspar, 6 parts of clay, hexametaphosphoric acid Sodium 3 parts.

[0047] This embodiment also provides a process for preparing the hydrophobic porous ceramic product, comprising the following steps:

[0048] Step 1. Weigh the green body raw material according to the weight and pulv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of ceramic products, in particular to a hydrophobic porous ceramic product and a preparation process thereof, including a green body and a glaze, and the green body is composed of the following raw materials in parts by weight: 27 parts by weight of silicon nitride, zirconia 16 parts, 12 parts of clay, 24 parts of aluminum silicate, 16 parts of cordierite, 19 parts of silicon carbide, 14 parts of diatomaceous earth, 11 parts of albite, 18 parts of alumina, and 13 parts of flux; the glaze It consists of the following raw materials in parts by weight: 21 parts of dolomite, 23 parts of silicon carbide, 14 parts of calcium oxide, 17 parts of potassium feldspar, 5 parts of clay, and 2 parts of sodium hexametaphosphate. The preparation process includes the following steps: raw material modification of green body; hot press casting; dewaxing and biscuit firing; glazing; firing. The invention has a simple process and is suitable for large-scale production, and the produced ceramic product has the advantages of high mechanical strength, porous water repellency and high temperature resistance.

Description

technical field [0001] The invention relates to the technical field of ceramic products, in particular to a hydrophobic porous ceramic product and a preparation process thereof. Background technique [0002] The ceramic industry is one of the oldest industries in my country, and its ornamental value has always been greater than its use value. Nowadays, with the continuous advancement of science and technology, people have higher and higher requirements for the performance of ceramics, which makes the development of various performance Ceramics have become a new research hotspot. Among them, the hydrophobic modification of ceramics is one of the current hot spots. The wettability of solid materials means that when a liquid contacts a solid surface, the liquid can gradually penetrate or adhere to the solid surface, which is one of the important characteristics of the solid surface. This feature is determined by the chemical composition and microstructure of the solid surface. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/584C04B38/02C03C8/00C04B41/86
CPCC03C8/00C04B35/584C04B38/02C04B41/009C04B41/5022C04B41/86C04B2235/3217C04B2235/3244C04B2235/3418C04B2235/3454C04B2235/3463C04B2235/3472C04B2235/3481C04B2235/349C04B2235/3826C04B2235/96C04B38/0074C04B41/4539
Inventor 陈绿宗陈敦添陈巧谊
Owner 福建省泉州市契合工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com