Zirconium oxide false tooth with gradient mechanical properties, and manufacturing method of zirconium oxide false tooth

A manufacturing method and technology of zirconia, which can be applied to household appliances, ceramic products, and other household appliances, etc., can solve the problems of natural tooth wear, high hardness, low fracture toughness, etc., and achieve improved life expectancy, comprehensive performance improvement, and excellent performance. Effect

Active Publication Date: 2019-01-01
XI AN JIAOTONG UNIV
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the lower fracture toughness and higher hardness of zirconia ceramics lead to severe wear of the contralateral natural tooth and become the main reason for its further development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zirconium oxide false tooth with gradient mechanical properties, and manufacturing method of zirconium oxide false tooth
  • Zirconium oxide false tooth with gradient mechanical properties, and manufacturing method of zirconium oxide false tooth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Use mimics software to carry out three-dimensional reconstruction of CT data, 3-matic software design pore size, porosity and pore arrangement according to mechanical performance requirements and installation requirements, and then use Cura slice software to slice layer thickness, exposure time of each layer and other parameters Set up, adding support structures if necessary. Take 15mL of trimethylolpropane triacrylate and 5mL of ethoxylated pentaerythritol tetraacrylate as photocurable resin monomers; weigh 0.99g of Tego 685 dispersant, 0.11g of polymerization inhibitor MQ, and 0.22g of leveling agent, 0.22g defoamer and 0.22g graphite dye. The resin monomer and various additives were evenly mixed, and ball milled in a ball mill at a speed of 800 rpm / min for 4 hours to obtain a premixed solution. Then weigh 33g of zirconia powder (particle size 100 μm) and 1.1g of photoinitiator diacylphosphine oxide 819, and ball mill at a speed of 800rpm / min for 2h in a ball mill to...

Embodiment 2

[0047] Use mimics software to perform three-dimensional reconstruction of CT data. Magics software designs pore size, porosity and pore arrangement according to mechanical performance requirements and installation requirements, and then uses Cura slice software to set slice layer thickness, exposure time of each layer and other parameters. Add support structures as necessary. Take 15mL of trimethylolpropane triacrylate and 5mL of ethoxylated pentaerythritol tetraacrylate as photocurable resin monomers; weigh 6.2g of Tego 685 dispersant, 0.44g of polymerization inhibitor MQ, and 1.1g of leveling agent, 1.1g defoamer and 1.1g graphite dye. The resin monomer and various additives were evenly mixed, and ball milled in a ball mill at a speed of 1000 rpm / min for 6 hours to obtain a premixed solution. Take again 32g of zirconia powder (100 μm in particle size), and ball mill it for 2 h at a speed of 1000 rpm / min in a ball mill; then weigh 1.1 g of photoinitiator diacylphosphine oxid...

Embodiment 3

[0049] Use mimics software to perform three-dimensional reconstruction of CT data. Magics software designs pore size, porosity and pore arrangement according to mechanical performance requirements and installation requirements, and then uses Cura slice software to set slice layer thickness, exposure time of each layer and other parameters. Add support structures as necessary. Take 15mL of trimethylolpropane triacrylate and 5mL of ethoxylated pentaerythritol tetraacrylate as photocurable resin monomers; respectively weigh 3.4g of Tego 685 dispersant, 0.25g of polymerization inhibitor MQ, and 0.62g of leveling agent, 0.62g defoamer and 0.62g graphite dye. The resin monomer and various additives were evenly mixed, and ball milled in a ball mill at a speed of 1000 rpm / min for 6 hours to obtain a premixed solution. Take again 62g of zirconia powder (100 μm in particle diameter), and ball mill it at a speed of 1000 rpm / min for 2 h in a ball mill; then weigh 2.2g of photoinitiator d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a zirconium oxide false tooth with gradient mechanical properties, and a manufacturing method of the zirconium oxide false tooth. The false tooth comprises an integrally formedbase body and an occlusal surface positioned on the base body, wherein the occlusal surface is provided with a plurality of pores which pass through the interior of the base body; the occlusal surface part and the base body part have different porosities and pore sizes, and the pores are internally filled with dental repairing resin or polyetheretherketone, so that the occlusal surface part has aself-lubricating property, and the excessive wear of the natural surface (4) at the opposite side of the zirconium oxide false tooth is avoided; the manufacturing method comprises the following steps: (1) designing a porous part and preparing a printed document; (2) preparing slurry; (3) forming a green body; (4) carrying out degreasing and sintering treatment; (5) injecting the polyetheretherketone or photosensitive resin for dental restoration. The manufacturing method provided by the invention is used for improving the fracture toughness of a zirconium oxide ceramic material and reducing the hardness so as to enable the zirconium oxide false tooth to be matched with the hardness of natural teeth and human skeleton; the zirconium oxide false tooth can meet demands of clinical applications such as dental prosthesis, false teeth, bone repair and bone filling.

Description

technical field [0001] The invention belongs to the technical field of oral prosthesis manufacture, and in particular relates to a zirconia denture with gradient mechanical properties and a manufacturing method thereof. Background technique [0002] Zirconia ceramic materials have good comprehensive properties such as high melting point, high hardness, high wear resistance, oxidation resistance, etc., and the source of production raw materials is sufficient, the manufacturing cost is low, and it is suitable for large-scale industrial production. It is widely used in the field of biomedicine, especially in the field of oral restorations, due to its excellent mechanical properties and biological properties. However, the lower fracture toughness and higher hardness of zirconia ceramics lead to severe wear of the contralateral natural tooth, which became the main reason for its further development. [0003] Polyetheretherketone (PEEK) is a semi-crystalline thermoplastic polymer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61C13/083A61C13/097C04B35/486C04B35/622C04B38/06
CPCA61C13/083A61C13/097C04B35/486C04B35/622C04B38/067C04B2235/6562C04B2235/6567
Inventor 刘亚雄刘绘龙张玉琪任辉连芩王玲贺健康
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com