Low-temperature-resistant PVC composite cable material and preparation method thereof

A composite cable material, low temperature resistance technology, applied in the field of wire and cable, to achieve the effect of increased tensile strength and elongation at break, improved long-term heat resistance and oil resistance, good mechanical properties and oil resistance

Inactive Publication Date: 2019-01-01
XINYA ELECTRONICS
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention provides a low temperature resistant PVC composite cable material and a preparation method thereof, which solves the above technical problems existing in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] 100 parts of EPDM compound, 18 parts of ethylene-vinyl acetate copolymer, 16 parts of nano-silica, 4 parts of composite compatibilizer, 15 parts of chlorinated polyethylene, 5 parts of dicumyl peroxide, 0.2 part of sulfur, TMTD 0.4 parts of accelerator, 3.2 parts of composite vulcanization aids, 80 parts of fillers, 15 parts of high degree of polymerization polyvinyl chloride, 0.8 parts of anti-aging agent and 20 parts of plasticizer, the degree of polymerization of the high degree of polymerization polyvinyl chloride is 2500,

[0034] Described EPDM compound is made up of the material of following mass parts:

[0035] ①92 parts of EPDM rubber;

[0036] ②8 parts of modified chlorosulfonated polyethylene;

[0037] The mass ratio of dicumyl peroxide, glycidyl methacrylate and styrene in the composite compatibilizer is 0.4:3.2:5, triallyl isocyanurate and trihydroxy The mass ratio of methylpropane trimethacrylate is 1:1.5, 60 parts of calcined pottery clay, 5 parts of ca...

Embodiment 2

[0044] 100 parts of EPDM compound, 20 parts of ethylene-vinyl acetate copolymer, 18 parts of nano-silica, 6 parts of composite compatibilizer, 15 parts of chlorinated polyethylene, 8.5 parts of dicumyl peroxide, 0.3 parts of sulfur, TMTD 0.4 parts of accelerator, 3.2 parts of composite vulcanization aids, 60 parts of fillers, 20 parts of high degree of polymerization polyvinyl chloride, 0.8 parts of anti-aging agent and 25 parts of plasticizer, the degree of polymerization of the high degree of polymerization polyvinyl chloride is 2500,

[0045] Described EPDM compound is made up of the material of following mass parts:

[0046] ①90 parts of EPDM rubber;

[0047] ②10 parts of modified chlorosulfonated polyethylene;

[0048] The mass ratio of dicumyl peroxide, glycidyl methacrylate and styrene in the composite compatibilizer is 0.4:3.2:5, triallyl isocyanurate and trihydroxy The mass ratio of methylpropane trimethacrylate is 1:2.5, 40 parts of calcined pottery clay, 5 parts o...

Embodiment 3

[0055] 100 parts of EPDM compound, 19 parts of ethylene-vinyl acetate copolymer, 17 parts of nano-silica, 5 parts of composite compatibilizer, 15 parts of chlorinated polyethylene, 7.5 parts of dicumyl peroxide, 4.6 parts of composite vulcanization aid part, 0.3 part of sulfur, 0.4 part of TMTD accelerator, 0.2 part of tellurium dithiocarbamate, 75 parts of filler, 17 parts of high degree of polymerization polyvinyl chloride, 0.8 part of anti-aging agent and 23 parts of plasticizer. The degree of polymerization of polyvinyl chloride is 2500,

[0056] Described EPDM compound is made up of the material of following mass parts:

[0057] ① 94 parts of EPDM rubber;

[0058] ②6 parts of modified chlorosulfonated polyethylene;

[0059] The mass ratio of dicumyl peroxide, glycidyl methacrylate and styrene in the composite compatibilizer is 0.4:3.2:5, triallyl isocyanurate and trihydroxy The mass ratio of methyl propane trimethacrylate is 1:2, 50 parts of calcined pottery clay, 10 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a low-temperature-resistant PVC composite cable material which is prepared from 100 parts of EPDM composite, 18 to 20 parts of ethylene-vinyl acetate copolymer, 16 to 18 parts of nano silicon dioxide, 4 to 6 parts of a composite compatilizer, 15 parts of chlorinated polyethylene, 5 to 8.5 parts of dicumyl peroxide, 0.2 to 0.3 part of sulfur, 0.4 part of a TMTD accelerant, 3.2 to 5.5 parts of a composite vulcanizing agent, 60 to 80 parts of a filling agent, 15 to 20 parts of high polymerization degree polyvinyl chloride, 0.8 part of an anti-aging agent and 20 to 25 partsof a plasticizer, wherein the EPDM composite is prepared from 90 to 94 parts of ethylene-propylene-diene monomer and 6 to 10 parts of modified chlorosulfonated polyethylene; the composite compatilizeris prepared from a mixture of dicumyl peroxide, glycidyl methacrylate and styrene; the composite vulcanizing agent is a mixture of triallyl isocyanurate and trimethylolpropane trimethyl acrylate. According to the composite cable material disclosed by the invention, the ingredients are optimized and designed; thus, the prepared composite cable material has the advantages of better low temperatureresistance and oil resistance and more excellent mechanical property.

Description

technical field [0001] The invention relates to the field of wires and cables, in particular to a low-temperature-resistant PVC composite cable material and a preparation method thereof. Background technique [0002] Wire and cable is a wire product used to transmit electric (magnetic) energy, information and realize electromagnetic energy conversion. As the main carrier of power transmission, wires and cables are widely used in electrical equipment, lighting circuits, household appliances, etc., and their quality directly affects the quality of projects and the safety of consumers' lives and property. The current wire and cable materials include PVC, PE, PP, EPDM, etc. PVC materials have excellent mechanical and physical properties, flexibility, chemical resistance, cheap price, and excellent processing performance, but they are not resistant to oil and organic solvents. And the insulation is hard. EPDM has excellent oxidation resistance, ozone resistance and corrosion re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L51/04C08L23/08C08L23/28C08L27/06C08L23/34C08L71/00C08K13/02C08K5/14C08K3/36C08K5/3492C08K5/40H01B3/28
CPCC08K2201/003C08K2201/011C08L51/04C08L2201/08C08L2203/202C08L2205/035C08L2312/00H01B3/28C08L23/0853C08L23/286C08L27/06C08L23/34C08L71/00C08K13/02C08K5/14C08K3/36C08K5/34924C08K5/40
Inventor 石刘建贺云峰
Owner XINYA ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More