Weather-resistant inorganic exterior wall paint based on graphene and mullite and preparation method thereof

A technology of exterior wall coatings and mullite, which is applied in anti-corrosion coatings, fire-proof coatings, anti-fouling/underwater coatings, etc., can solve the problem of adhesion and other properties that need to be improved, affect the application effect of graphene, and the dispersion effect of graphene is not good Good and other problems, to achieve the effect of light apparent density, good thermal shock stability, and improved anti-corrosion and weather resistance

Active Publication Date: 2021-02-05
GUANGXI XUTENG INDUSTRIAL GROUP CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The Chinese invention patent with application number 201611162668.1 discloses a graphene anti-corrosion coating and its preparation method, which improves the thermal conductivity, adhesion and stability of the coating, but needs to be improved in terms of adhesion and other properties
The Chinese invention patent with application number 201310131419.6 discloses a graphene inorganic coating and its application method, but once the amount of graphene added exceeds 5%, the film quality will be affected
In order to solve the existing deficiencies, the object of the present invention is to provide a graphene-based inorganic coating, because graphene has good thermal stability, excellent impermeability and effective barrier to oxygen, water and corrosive ions, etc. It has obvious advantages in metal anti-corrosion, but the strong van der Waals force and high specific surface area between graphene layers make graphene in coatings easy to gather together, which limits its wide use
Studies have shown that various methods can be used to modify graphene to disperse it, but the application effect of graphene is often affected by the poor dispersion effect of graphene or its short anti-sedimentation time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Weather-resistant inorganic exterior wall paint based on graphene and mullite and preparation method thereof
  • Weather-resistant inorganic exterior wall paint based on graphene and mullite and preparation method thereof
  • Weather-resistant inorganic exterior wall paint based on graphene and mullite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The weather-resistant inorganic exterior wall coating based on graphene and mullite includes the following components according to mass percentage: 5% mullite, 10% perlite, 10% graphene, 5% vitrified microbeads, 7% sepiolite, Albite 14%, light calcium carbonate 5%, bauxite 5%, nano-titanium dioxide 2%, nano-silica sol 10%, additives 23%, pure acrylic emulsion 4%; among them,

[0031]The auxiliary agent includes the following components in terms of mass percentage: 75% sodium silicate, 24% zinc phosphate, and 1% sodium hexametaphosphate;

[0032] The nano-silica sol is first modified by adding γ-methacryloxypropyltrimethoxysilane into the nano-silica sol and stirring at room temperature for 10 hours; the γ-methacryloyl The usage amount of oxypropyltrimethoxysilane is 2.0wt% of the nano-silica sol quality;

[0033] The particle size of the light calcium carbonate is 0.02 μm;

[0034] The preparation method of described inorganic exterior wall paint, comprises the follow...

Embodiment 2

[0040] The weather-resistant inorganic exterior wall coating based on graphene and mullite includes the following components in terms of mass percentage: 10% mullite, 6% perlite, 6% graphene, 3% vitrified microbeads, 5% sepiolite, Albite 12%, light calcium carbonate 8%, bauxite 8%, nano-titanium dioxide 4%, nano-silica sol 15%, additives 20%, pure acrylic emulsion 3%; among them,

[0041] The auxiliary agent includes the following components in terms of mass percentage: 80% sodium silicate, 18% zinc phosphate, and 2% sodium hexametaphosphate;

[0042] The nano-silica sol is first modified by adding γ-methacryloxypropyltrimethoxysilane into the nano-silica sol and stirring at room temperature for 11 hours; the γ-methacryloyl The usage amount of oxypropyltrimethoxysilane is 3.0wt% of the nano-silica sol quality;

[0043] The particle size of the light calcium carbonate is 0.10 μm;

[0044] The preparation method of described inorganic exterior wall paint, comprises the followi...

Embodiment 3

[0050] The weather-resistant inorganic exterior wall coating based on graphene and mullite includes the following components in terms of mass percentages: 12% mullite, 8% perlite, 15% graphene, 3% vitrified microbeads, 9% sepiolite, Albite 6%, light calcium carbonate 5%, bauxite 5%, nano-titanium dioxide 3%, nano-silica sol 10%, additives 20%, pure acrylic emulsion 4%; among them,

[0051] The auxiliary agent includes the following components according to mass percentage: 77% of sodium silicate, 20% of zinc phosphate, and 3% of sodium hexametaphosphate;

[0052] The nano-silica sol is first modified by adding γ-methacryloxypropyltrimethoxysilane into the nano-silica sol and stirring at room temperature for 10.5 hours; the γ-methacrylic acid The usage amount of acyloxypropyltrimethoxysilane is 2.5wt% of the nano-silica sol quality;

[0053] The particle size of the light calcium carbonate is 0.06 μm;

[0054] The preparation method of described inorganic exterior wall paint, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a weather-resistant inorganic exterior wall coating based on graphene and mullite and a preparation method thereof, and belongs to the field of inorganic wall coatings based on graphene. ~15%, graphene 1~20%, vitrified microbeads 2~10%, sepiolite 3~10%, albite 6~15%, light calcium carbonate 5~18%, bauxite 5~ 10%, nano-titanium dioxide 2-8%, nano-silica sol 10-15%, additives 20-30%, pure acrylic emulsion 3-6%. The coating has strong bonding strength, simple construction, and the coating is resistant to washing. At the same time, under high temperature conditions, the coating does not bubble, crack, or fall off, and has the functions of waterproof, fireproof, salt resistance, alkali resistance, heat insulation, anti-corrosion, anti-rust, and anti-aging.

Description

【Technical field】 [0001] The invention relates to the field of graphene-based inorganic wall paint production, in particular to a weather-resistant inorganic exterior wall paint based on graphene and mullite and a preparation method thereof. 【Background technique】 [0002] With the continuous development of my country's modern industry, the types of building materials are also very rich. There are two types of coatings on the market: one is organic coatings. For a long time, organic coatings have been widely used for their good decoration, variety and low price. However, the main raw materials of such materials generally come from natural resources such as coal, oil, and natural gas. A large amount of by-products, volatile solvents and residual monomers will be produced during processing, which are not easy to remove and are also toxic, which not only causes environmental pollution but also wastes a lot of resources and energy, and this type of coating is prone to occurrenc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/00C09D5/18C09D5/08C09D5/16C09D7/61C09D7/62C09D7/65
CPCC09D1/00C09D5/08C09D5/1687C09D5/18
Inventor 黄聿新
Owner GUANGXI XUTENG INDUSTRIAL GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com