A kind of water-soluble alginate antibacterial fiber and preparation method thereof

An alginate and antibacterial fiber technology, applied in the field of fiber manufacturing, can solve problems such as low strength and easy breakage, and achieve the effects of increased strength, easy absorption and good market prospects

Active Publication Date: 2020-11-06
青岛海赛尔新材料科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem mainly solved by the present invention is to provide a water-soluble alginate antibacterial fiber and its preparation method in view of the deficiencies in the prior art. It has the advantages of easy absorption and good antibacterial effect, and also overcomes the disadvantages of low strength and easy breakage of traditional water-soluble fibers, and has a wide range of application prospects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A kind of preparation method of water-soluble alginate antibacterial fiber comprises the following steps:

[0039] (1) Take gelatin and dissolve it in distilled water, then take nano silver-loaded zirconium phosphate and join in the gelatin solution, ultrasonically disperse evenly, the massfraction that the nanometer silver-loaded zirconium phosphate is prepared is 0.05%, and the massfraction of gelatin is 5% % mixed solution;

[0040] (2) Weigh sodium alginate and dissolve it in the mixed solution prepared in step (1) to prepare an aqueous solution of sodium alginate with a mass fraction of sodium alginate of 4%, then stir and heat to 60° C., microwave vibration or high-speed stirring for 2 hours , to obtain a uniform spinning solution;

[0041] (3) The spinning solution prepared by step (2) is degassed, and is sprayed from the spinneret to the first coagulation bath through a metering pump, and the first coagulation bath is that the mass fraction of calcium chloride ...

Embodiment 2

[0049] A kind of preparation method of water-soluble alginate antibacterial fiber comprises the following steps:

[0050] (1) Weigh polyvinyl alcohol and dissolve it in distilled water, then weigh nano-silver-loaded zirconium phosphate and add it to the polyvinyl alcohol solution, and ultrasonically disperse evenly to prepare nano-silver-loaded zirconium phosphate with a mass fraction of 0.2%, polyethylene The mass fraction of alcohol is a mixed solution of 10%;

[0051] (2) Weigh sodium alginate and dissolve it in the mixed solution prepared in step (1) to prepare an aqueous solution of sodium alginate with a mass fraction of sodium alginate of 6%, then stir and heat to 60°C, microwave vibration or high-speed stirring for 2 hours , to obtain a uniform spinning solution;

[0052] (3) The spinning solution prepared by step (2) is degassed, and is sprayed from the spinneret into the first coagulation bath through a metering pump, and the first coagulation bath is that the mass ...

Embodiment 3

[0060] A kind of preparation method of water-soluble alginate antibacterial fiber comprises the following steps:

[0061] (1) Take polyvinyl alcohol and sodium carboxymethyl cellulose and dissolve it in distilled water, then take nanometer silver-loaded zirconium phosphate and join in the polymer solution, ultrasonically disperse evenly, and prepare the mass fraction of nanometer silver-loaded zirconium phosphate as 0.1%, the massfraction of polyvinyl alcohol is 5%, the massfraction of sodium carboxymethylcellulose is a mixed solution of 2%;

[0062] (2) Weigh sodium alginate and dissolve it in the mixed solution prepared in step (1) to prepare an aqueous solution of sodium alginate with a mass fraction of sodium alginate of 5%, then stir and heat to 60° C., microwave vibration or high-speed stirring for 2 hours , to obtain a uniform spinning solution;

[0063] (3) The spinning solution prepared by step (2) is degassed, and is sprayed from the spinneret into the first coagula...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention relates to a water-soluble alginate antibacterial fiber and a preparation method thereof. The preparation method comprises: weighing a water-soluble polymer and dissolving the water-soluble polymer in distilled water, and then adding nano-silver-loaded zirconium phosphate and / or nano-zinc oxide, and carrying out uniform ultrasonic dispersion; weighing sodium alginate and dissolving sodium alginate in the mixed liquor, stirring and heating to obtain a spinning solution; defoaming the spinning solution, metering and ejecting from a spinneret plate into a coagulating bath by a metering pump; preparing a sodium ethylene diamine tetracetate solution; squeezing fiber to remove water, and immersing in the sodium ethylene diamine tetracetate aqueous solution; adding sodium carbonateand sodium bicarbonate and fully mixing, and continuously immersing; preparing a chitosan solution; squeezing fiber to remove water, and immersing in the chitosan solution; squeezing fiber to remove water, drying, and winding. The invention has the advantages as follows: the product is soluble in water; active ingredients are easy to absorb, and the antibacterial effect is good; the disadvantage that traditional water-soluble fiber has low strength and is easy to fracture is dissolved; and the product has a wide application prospect.

Description

technical field [0001] The invention belongs to the technical field of fiber manufacturing, and in particular relates to a water-soluble alginate antibacterial fiber and a preparation method thereof. Background technique [0002] Water-soluble fiber can be dissolved in water or slowly hydrolyzed into water-soluble molecules (or compounds) when encountering water. It is a valuable functional differentiated fiber and can be used in papermaking, medical non-woven fabrics, and female sanitary napkins. However, the existing water-soluble fibers have problems such as low strength and easy breakage during use, which limits the application range of water-soluble fibers. [0003] Seaweed fiber is a new type of high-performance fiber obtained by wet spinning production process with polysaccharide extracted from natural seaweed as raw material and water-soluble metal salt solution as coagulation bath. Because seaweed has accumulated rich minerals in the ocean, and contains ingredients...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/02D01F8/18D01F1/10D01F11/00D06M13/342D06M11/76D06M15/03D06M13/144D06M101/10D06M101/04
CPCD01F1/103D01F8/02D01F8/18D01F11/00D06M11/76D06M13/144D06M13/342D06M15/03D06M16/00D06M2101/04D06M2101/10D06M2200/50
Inventor 郝继海李琪
Owner 青岛海赛尔新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap