Wheel rim anticorrosion coating material containing basalt scales, and preparation method thereof

An anti-corrosion coating, basalt technology, applied in anti-corrosion coatings, epoxy resin coatings, coatings and other directions, can solve the problems of poor dispersion and stability, easy settling, coating performance decline, etc., to achieve good resistance to salt spray and reduce infiltration. , Improve the effect of anti-corrosion performance

Inactive Publication Date: 2019-01-25
ANHUI JIANGHUAI WHEEL CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when basalt flakes are used in water-based anti-corrosion coatings, due to their surface inertia, the dispersion and st

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wheel rim anticorrosion coating material containing basalt scales, and preparation method thereof
  • Wheel rim anticorrosion coating material containing basalt scales, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An anti-corrosion coating for wheel rims containing basalt scales is characterized in that it is made of the following raw materials in parts by weight:

[0024] Basalt flake 10, dilute hydrochloric acid 10, cetyltrimethylammonium bromide 1, aniline solution 30, acidic medium 50, ammonium persulfate 5, water-based epoxy resin 50, calcium carbonate 5, talcum powder 5, orthosilicic acid ethyl ester 10;

[0025] The mass concentration of the dilute hydrochloric acid is 2%.

[0026] Further, its preparation method comprises the following steps:

[0027] (1) Put the basalt scales into a tube furnace, feed nitrogen, raise the temperature to 150°C at a rate of 2°C / min, then roast for 2 hours, then cool down to room temperature at a rate of 4°C / min, and ball mill for 20 minutes until The scale diameter is 5 μm;

[0028] (2) Add the basalt scales obtained in step (1) to 20 times its volume of absolute ethanol, heat to 50°C, treat it under ultrasonic conditions of 65Hz and 100...

Embodiment 2

[0038] An anti-corrosion coating for wheel rims containing basalt scales is characterized in that it is made of the following raw materials in parts by weight:

[0039] Basalt flakes 15, dilute hydrochloric acid 30, cetyltrimethylammonium bromide 2, aniline solution 40, acid medium 70, ammonium persulfate 7, water-based epoxy resin 60, calcium carbonate 10, talcum powder 7, orthosilicic acid ethyl ester 15;

[0040] The mass concentration of the dilute hydrochloric acid is 4%.

[0041] Further, its preparation method comprises the following steps:

[0042] (1) Put the basalt scales into a tube furnace, feed nitrogen, heat up to 155°C at a rate of 3°C / min, then roast for 3 hours, then cool down to room temperature at a rate of 5°C / min, and ball mill for 25 minutes until The scale diameter is 30μm;

[0043] (2) Add the basalt flakes obtained in step (1) to 25 times its volume of absolute ethanol, heat to 55°C, treat it under ultrasonic conditions of 68Hz and 1100W for 35min, ...

Embodiment 3

[0053] An anti-corrosion coating for wheel rims containing basalt scales is characterized in that it is made of the following raw materials in parts by weight:

[0054] Basalt flakes 20, dilute hydrochloric acid 50, cetyltrimethylammonium bromide 3, aniline solution 50, acid medium 100, ammonium persulfate 8, water-based epoxy resin 80, calcium carbonate 15, talcum powder 10, orthosilicic acid ethyl ester 20;

[0055] The mass concentration of the dilute hydrochloric acid is 6%.

[0056] Further, its preparation method comprises the following steps:

[0057] (1) Put the basalt scales into a tube furnace, feed nitrogen, raise the temperature to 160°C at a rate of 4°C / min, then roast for 3 hours, then cool down to room temperature at a rate of 5°C / min, and ball mill for 30 minutes until The scale diameter is 50μm;

[0058] (2) Add the basalt scales obtained in step (1) to 30 times its volume of absolute ethanol, heat to 60°C, treat it under ultrasonic conditions of 70Hz and 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wheel rim anticorrosion coating material containing basalt scales, and a preparation method thereof. According to the present invention, the prepared wheel rim anticorrosioncoating material has advantages of high corrosion potential, high linear polarization resistance, high protection efficiency, low corrosion current density, excellent corrosion resistance, good mechanical property, good salt spray resistance, good impact resistance, good adhesion and high hardness of coating film.

Description

technical field [0001] The invention belongs to the technical field of anti-corrosion coatings, and in particular relates to an anti-corrosion coating for wheel rims containing basalt scales and a preparation method thereof. Background technique [0002] Basalt scale is a new type of scale material. It is a new type of material processed by selecting natural basalt ore with excellent performance through special processes such as high-temperature melting, clarification, homogenization, and screening. It presents a transparent or dark green sheet structure. It can not only produce Shielding effect, and also has unique advantages in acid and alkali resistance and corrosion resistance, especially the stable high and low temperature resistance of basalt, as well as excellent dielectric and chemical resistance, making it widely used in coatings, construction, national defense, military, Highway, railway and other fields have great development prospects. [0003] With the continuo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D5/08C09D7/62
CPCC08K2003/265C08K2201/014C09D5/08C09D7/62C09D163/00C08K13/06C08K9/10C08K9/02C08K7/00C08K3/34C08K3/26
Inventor 朱加强
Owner ANHUI JIANGHUAI WHEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap