Active molecule clad double-layer porous biodegradable material as well as preparation method and application thereof

A technology of active molecules and degradable materials, which is applied to double-layer porous biodegradable materials coated with active molecules and the fields of preparation and application thereof, which can solve the problem of degradation speed, single release speed of active molecules, unfavorable nutrients or air circulation, and stability. problems such as poor performance, to achieve the effect of improving the effective duration, low cost, and low pollution

Active Publication Date: 2019-02-12
BLOOMAGE BIOTECHNOLOGY CORP LTD +1
View PDF13 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] In order to solve the problems of poor stability, single degradation rate and release rate of active molecules in the existing materials, the non-porous structure is not conducive to the circulation of nutrients or air, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Active molecule clad double-layer porous biodegradable material as well as preparation method and application thereof
  • Active molecule clad double-layer porous biodegradable material as well as preparation method and application thereof
  • Active molecule clad double-layer porous biodegradable material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Preparation of porous degradable materials coated with antibiotics

[0038] (1) Dissolve hyaluronic acid with a molecular weight of 500 kD and hydroxyethyl cellulose of 1300 kD in purified water and fully dissolve it to prepare a mixed casting solution with a mass concentration of hyaluronic acid and hydroxyethyl cellulose of 1.0%, Use sodium hydroxide solution to adjust the pH value to 12 to obtain an alkaline solution;

[0039] (2) Add epoxy compound crosslinking agent 1,4-butanediol diglycidyl ether 0.2 μl / ml to the alkaline solution, stir evenly, carry out crosslinking at 40°C, and the reaction time is 6h;

[0040] (3) Add a 0.08 µm diameter nano-calcium carbonate solution to the cross-linked polysaccharide solution, disperse evenly, and pour the porogen into a dry mold at a constant temperature of 25°C to form the mass concentration of the porogen at 0.1% to 0.9% (w / v);

[0041] (4) Purify the dried film in ethanol for 48 hours, replace the ethanol every 12 hours,...

Embodiment 2

[0052] Preparation of porous cross-linked films coated with vascular endothelial growth factor and recombinant human epidermal growth factor

[0053] (1) In the four groups of samples A1, A2, B1, and B2, hyaluronic acid with a molecular weight of 1500 kD and carboxymethyl cellulose with a molecular weight of 90 kD were dissolved in 20 mM pH 5.0 phosphate buffer, hyaluronic acid, carboxymethyl cellulose The mass concentration of base cellulose is 2%, 1%;

[0054] (2) Add 0.1mol cross-linking agent carbodiimide to the solution, stir well, and carry out cross-linking reaction at 45°C for 4 hours;

[0055] (3) Add uniformly dispersed 0.1 μm nano-calcium carbonate particles to A1 and A2 samples, and add uniformly dispersed 150 μm paraffin microspheres to B1 and B2 samples, both with a mass concentration of 1%, and dry at a constant temperature of 25°C;

[0056] (4) Purify the film in ethanol for 48 hours, replace the ethanol every 12 hours, then place the film in deionized water f...

Embodiment 3

[0064] Preparation of porous cross-linked hyaluronic acid material coated with non-steroidal anti-inflammatory drugs

[0065] (1) Dissolve hyaluronic acid and carboxymethyl cellulose with a molecular weight of 3000 kD in 20mM phosphate buffer at pH 5.0, and the mass concentrations of hyaluronic acid and carboxymethyl cellulose are 5% and 1.25% respectively;

[0066] (2) Add 1M cross-linking agent carbodiimide to the solution, stir evenly, and carry out cross-linking reaction at 30°C for 8 hours;

[0067] (3) Add 50 µm nano-calcium carbonate particles with a mass concentration of 2% to the solution, disperse evenly, and dry at a constant temperature of 25°C;

[0068] (4) After drying, the cross-linked material was purified in ethanol for 48 hours, and the ethanol was replaced every 12 hours, and then the film was purified in deionized water for 8 hours, and put into a 40-mesh sieve until no liquid flowed down;

[0069] (5) Put the cross-linked porous material after washing awa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an active molecule clad double-layer porous biodegradable material. The material is prepared through the following steps of (1), cross-linking hyaluronic acid with a natural polysaccharide; (2); adding a pore-forming agent into a cross-linking solution, and drying at a constant temperature; (3), purifying for multiple times to wash off the pore-forming agent; (4), immersingin a hyaluronic acid solution containing an active molecule with a specific function; and (5), carrying out vacuum freeze drying. The material is of a double-layer structure; an inner layer is compact in structure and good in mechanical property and stability; an outer layer generates adhesiveness in case of water; the inner and outer layers both carry specific active factors and the material hasa sustained-release effect. Further, the cost is low, the process is short in period, the pollution and the energy consumption is low. The material can be widely applied to multiple fields of medicines, cosmetics and the like.

Description

technical field [0001] The invention relates to the technical field of biodegradable new materials, in particular to a porous biodegradable material coated with active molecules and a preparation method thereof, and to the application of the material in medical materials and cell scaffolds. Background technique [0002] Porous materials have interconnected porous structures, which can be prepared into various forms such as thin films, gels, and microspheres. They provide controllable passages for the outside and inside of the material at the same time, and create an environment where nutrients can be exchanged and circulated. It is considered to be the most effective Promising Scaffold Materials for Tissue Engineering. [0003] Hyaluronic acid (Hyaluronic Acid, referred to as HA, also known as hyaluronic acid) is a natural substance widely present in humans and animals. It is a polymer composed of disaccharide units composed of glucuronic acid and acetylhexosamine. Mucopoly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/28A61L15/42A61L15/62A61L15/44A61K8/02A61K8/73C08J9/26C08J9/28C08J3/24C08L5/08C08L1/28
CPCA61K8/0212A61K8/731A61K8/735A61L15/28A61L15/425A61L15/44A61L15/62A61L2300/216A61L2300/252A61L2300/406A61L2300/41A61L2300/414C08J3/246C08J9/0061C08J9/26C08J9/28C08J2301/28C08J2305/08
Inventor 冯晓毅宋永民宫衍革耿凤郭文逸郭学平
Owner BLOOMAGE BIOTECHNOLOGY CORP LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com