Waterproof solar energy back plate glue

A solar backplane and waterproof technology, which is applied in the direction of adhesives, epoxy glue, adhesive types, etc., can solve the problems of water resistance and bond strength that cannot be further improved, so as to reduce self-aggregation and improve waterproofness and the effect of improving bond strength and water resistance

Inactive Publication Date: 2019-02-12
FOSHAN WANHE NEW ENERGY TECH CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The main technical problem to be solved by the present invention is: Aiming at the shortcomings that the traditional solar backplane glue cannot further improve the water resistance and bonding strength, a waterproof solar backplane glue is provided.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof solar energy back plate glue

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0031] Mix graphene oxide and water in a beaker at a mass ratio of 1:200, and ultrasonically disperse for 40 minutes at a frequency of 55 kHz to obtain a graphene oxide dispersion. The graphene oxide dispersion and hydrazine hydrate are mixed at a mass ratio of 100 : 1 mixed in a flask, and adding 0.08 times the weight of the graphene oxide dispersion to the flask with 28% ammonia water, at a temperature of 90°C and a rotating speed of 400r / min, stirring and reacting for 180min, then filtering , to obtain a filter cake, the filter cake was vacuum-dried at a temperature of 65°C for 5 hours to obtain pretreated graphene, and the pretreated graphene and ethanol were mixed in a three-necked flask at a mass ratio of 1:100, and poured into a three-necked Sodium hydroxide with 3 times the mass of pretreated graphene and cationic surfactant with 2 times the mass of pretreated graphene were added to the flask. Under the condition of frequency of 55kHz, after ultrasonic dispersion for 40...

example 2

[0033]Mix graphene oxide and water in a beaker at a mass ratio of 1:200, and ultrasonically disperse for 40 minutes at a frequency of 55 kHz to obtain a graphene oxide dispersion. The graphene oxide dispersion and hydrazine hydrate are mixed at a mass ratio of 100 : 1 mixed in a flask, and adding 0.08 times the weight of the graphene oxide dispersion to the flask with 28% ammonia water, at a temperature of 90°C and a rotating speed of 400r / min, stirring and reacting for 180min, then filtering , to obtain a filter cake, the filter cake was vacuum-dried at a temperature of 65°C for 5 hours to obtain pretreated graphene, and the pretreated graphene and ethanol were mixed in a three-necked flask at a mass ratio of 1:100, and poured into a three-necked Sodium hydroxide with 3 times the mass of pretreated graphene and cationic surfactant with 2 times the mass of pretreated graphene were added to the flask. Under the condition of frequency of 55kHz, after ultrasonic dispersion for 40m...

example 3

[0035] In parts by weight, take in turn: 50 parts of epoxy resin, 20 parts of ethylene-vinyl acetate copolymer, 5 parts of turpentine, 16 parts of phosphorus oxychloride, 22 parts of graphene, 15 parts of polyaspartic acid ester, 8 parts of epoxy soybean oil, 12 parts of isocyanate, 15 parts of carbonate and 80 parts of solvent, mix epoxy resin and solvent in a blender, and add ethylene-vinyl acetate copolymer, turpentine, phosphorus oxychloride to the blender , graphene, polyaspartate, epoxidized soybean oil, isocyanate and carbonate, under the conditions of temperature 30°C and rotation speed 400r / min, after stirring and mixing for 60min, a waterproof solar backsheet adhesive was obtained. Described epoxy resin is epoxy resin E-44. The isocyanate is toluene diisocyanate. The carbonate is zinc carbonate. Described solvent is toluene. Example 4

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses waterproof solar energy back plate glue, and belongs to the technical field of a high polymer material. In parts by weight, 40 to 50 parts of epoxy resin, 15 to 20 parts of ethylene-vinyl acetate copolymers, 2 to 5 parts of turpentine, 8 to 16 parts of phosphorus oxychloride, 15 to 22 parts of modified graphene, 8 to 15 parts of polyaspartic ester, 5 to 8 parts of epoxidized soybean oil, 5 to 12 parts of isocyanates, 8 to 15 parts of carbonate and 60 to 80 parts of solvents are sequentially weighed; the epoxy resin and solvents are mixed in a stirring machine; the ethylene-vinyl acetate copolymers, turpentine, phosphorus oxychloride, modified graphene, polyaspartic ester, epoxidized soybean oil, isocyanates and carbonate are added into the stirring machine; stirringand mixing are performed for 30 to 60 min under the conditions of the temperature being 20 to 30 DEG C and the rotating speed being 300 to 400 r / min to obtain the waterproof solar energy back plate glue. The solar energy back plate glue prepared by the technical scheme has the characteristic of excellent water-resistant performance and bonding intensity.

Description

technical field [0001] The invention discloses a waterproof solar backboard adhesive, which belongs to the technical field of polymer materials. Background technique [0002] Due to the gradual reduction of fossil energy and various pollution problems during its use, countries are strengthening the development and utilization of clean energy such as solar energy. Solar panels are commonly used in solar equipment at present, which is an important device for converting solar energy into electrical energy. The service life of such products is generally designed to be more than 25a. To ensure such a long service life of the product, it is necessary to strictly control the quality of each component, and the role of the solar cell backsheet in these components cannot be underestimated. The solar backsheet is located on the back of the solar cell, which protects and supports the cell. The use environment requires it to have properties such as insulation, weather resistance, and wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/00C09J123/08C09J11/04C09J11/06C09J11/08
CPCC08K2003/267C08L2203/204C08L2205/035C09J11/04C09J11/06C09J11/08C09J163/00C08L23/0853C08L91/00C08K13/06C08K9/04C08K3/042C08K5/29C08K3/26
Inventor 裘友玖刘侠宋宇星
Owner FOSHAN WANHE NEW ENERGY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap