A kind of synthetic method containing ether oxygen bond linear dimethyl dicarbonate

A technology of dimethyl dicarbonate and synthesis method, which is applied in the direction of organic carbonate preparation, chemical instruments and methods, physical/chemical process catalysts, etc., can solve the problems of deactivation, large amount of calcium oxide, etc., and achieve excellent catalytic performance Effect

Active Publication Date: 2021-11-23
ANHUI POLYTECHNIC UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the amount of calcium oxide is large, 10wt%, and it is easy to absorb water and carbon dioxide in the air and deactivate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of synthetic method containing ether oxygen bond linear dimethyl dicarbonate
  • A kind of synthetic method containing ether oxygen bond linear dimethyl dicarbonate
  • A kind of synthetic method containing ether oxygen bond linear dimethyl dicarbonate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] like Figure 1 to Figure 2 Shown, a kind of synthetic method containing ether oxygen bond linear dimethyl dicarbonate comprises:

[0031] Step 1: preparing the catalyst magnesium aluminum hydrotalcite, specifically including:

[0032] 1) Taking magnesium nitrate and aluminum nitrate as raw materials, preparing a salt solution with a total metal concentration of 1.6mol / L, wherein the Mg / Al molar ratio is 3;

[0033] 2) Precipitating agent is prepared with a mixed aqueous solution of sodium hydroxide and sodium carbonate, wherein the concentration of sodium hydroxide is 3.7mol / L, and the concentration of sodium carbonate is 0.3mol / L;

[0034] 3) Under the conditions of 40°C and PH=9.0, magnesium aluminum hydrotalcite was prepared by co-precipitation method, aged at 90°C for 4 hours, filtered, washed, and finally dried at 120°C for 12 hours;

[0035] Step 2: preparing a mixed reaction liquid of diethylene glycol, dimethyl carbonate, and magnesium aluminum hydrotalcite, w...

Embodiment 2

[0040] like Figure 1 to Figure 2 Shown, a kind of synthetic method containing ether oxygen bond linear dimethyl dicarbonate comprises:

[0041] Step 1: preparing the catalyst magnesium aluminum hydrotalcite, specifically including:

[0042] 1) Taking magnesium nitrate and aluminum nitrate as raw materials, preparing a salt solution with a total metal concentration of 1.6mol / L, wherein the Mg / Al molar ratio is 3;

[0043] 2) Precipitating agent is prepared with a mixed aqueous solution of sodium hydroxide and sodium carbonate, wherein the concentration of sodium hydroxide is 3.7mol / L, and the concentration of sodium carbonate is 0.3mol / L;

[0044] 3) Under the conditions of 40°C and PH=9.0, magnesium aluminum hydrotalcite was prepared by co-precipitation method, aged at 90°C for 4 hours, filtered, washed, and finally dried at 120°C for 12 hours;

[0045] Step 2: preparing a mixed reaction liquid of triethylene glycol, dimethyl carbonate, and magnesium aluminum hydrotalcite, ...

Embodiment 3

[0050] like Figure 1 to Figure 2 Shown, a kind of synthetic method containing ether oxygen bond linear dimethyl dicarbonate comprises:

[0051] Step 1: preparing the catalyst magnesium aluminum hydrotalcite, specifically including:

[0052]1) Taking magnesium nitrate and aluminum nitrate as raw materials, preparing a salt solution with a total metal concentration of 1.6mol / L, wherein the Mg / Al molar ratio is 3;

[0053] 2) Precipitating agent is prepared with a mixed aqueous solution of sodium hydroxide and sodium carbonate, wherein the concentration of sodium hydroxide is 3.7mol / L, and the concentration of sodium carbonate is 0.3mol / L;

[0054] 3) Under the conditions of 40°C and PH=9.0, magnesium aluminum hydrotalcite was prepared by co-precipitation method, aged at 90°C for 4 hours, filtered, washed, and finally dried at 120°C for 12 hours;

[0055] Step 2: preparing a mixed reaction liquid of tetraethylene glycol, dimethyl carbonate, and magnesium aluminum hydrotalcite,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a synthesis method of ether oxygen bond-containing linear dimethyl dicarbonate, which comprises one step: preparing a catalyst magnesium aluminum hydrotalcite; second step: preparing a mixed reaction solution of glycol, dimethyl carbonate and magnesium aluminum hydrotalcite 3: Stir the reaction solution, heat up to 90°C, and record the reaction time; 4: Cool to room temperature after the reaction, filter, and purify by rotary evaporation to obtain a linear dimethyl dicarbonate containing ether oxygen bonds. The catalyst prepared by the method of the invention has obvious characteristic peaks of magnesium aluminum hydrotalcite, and the synthesized ether-oxygen bond straight-chain dimethyl dicarbonate has high rotary distillation purity.

Description

technical field [0001] The invention relates to the technical field of synthesizing straight-chain dimethyl dicarbonate containing ether oxygen bonds, in particular to a method for synthesizing straight-chain dimethyl dicarbonate containing ether oxygen bonds. Background technique [0002] Organic carbonate is non-toxic and non-polluting. It is an important chemical intermediate and is widely used in the fields of drugs, cosmetics, fragrances, electrolytes, polymers, and biomedicine. The transesterification method is considered to be the most promising non-optical Carbonate synthesis route. As a green solvent, DMC is chemically stable, non-toxic, non-corrosive, can be miscible with alcohol in any proportion, and has mild reaction conditions with alcohol, so it is often used as a raw material for transesterification. Its relevant transesterification studies mainly focus on the transesterification reaction of DMC and monohydroxy compound to synthesize monocarbonate, especiall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C07C68/06C07C69/96B01J27/232
CPCB01J27/232C07C68/06C07C69/96
Inventor 刘欢陈瑞洋
Owner ANHUI POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka